Thermosetting resin compositions prepared from isocyanates and epoxyphenols
Assignee: Hitachi Ltd
•
Filing: 1974-06-25
•
Granted: 1976-10-05
•
Expires: 1994-06-25
Abstract
Abstract Thermosetting resin compositions are obtained by mixing a resinous addition product produced by reacting an isocyanate compound having a molecular weight of 100 to 2000 and containing at least two isocyanate groups in its molecule with an epoxyphenol compound represented by the formula, ##EQU1## wherein R is a bi- or more valent group containing phenyl, R 1 is hydrogen, methyl or ethyl, m and n each are an integer of 1-8, and optionally an ordinary thermosetting epoxy resin, and 0.01 to 10 % by weight of a basic heterocycle forming catalyst based on the weight of said resinous addition product, said isocyanate compound and said epoxyphenol compound being blended so that said OH group may be present in an amount of 1/3 to 1 equivalent per equivalent of said isocyanate group and said epoxy group may be present in an amount of one-fifth to two-thirds equivalent per equivalent of said isocyanate group. The said addition product can be converted into a stable B-stage and is particularly useful as a varnish for prepreg.
Inventors
- 👤 Hitoshi Yokono
- 👤 Shunichi Numata
- 👤 Kazuo Goto
- 👤 Masahiko Sakai
- 👤 Toshikazu Narahara
- 👤 Junji Mukai
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 16:24
CPC Classifications
C; C08; C08G; C08G18/00; C08G18/06; C08G18/28; C08G18/2805; C08G18/2815; C08G18/08; C08G18/16; C08G18/18; C08G18/2845; C08G18/40; C08G18/58
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
171 words
A thermosetting resin composition comprising a reaction product of an isocyanate compound having a molecular weight of 100 to 2000 and containing at least two isocyanate groups in its molecule with an epoxyphenol compound which is represented by the formula, ##EQU2## wherein R is a bi- or more valent group containing phenyl, R 1 is hydrogen, methyl or ethyl, m and n each are an integer of 1-8, and 0.01 to 10% by weight of a catalyst which forms an isocyanurate bond and an oxazolidone bond on curing, based on the weight of said reaction product, said isocyanate compound and said epoxyphenol compound being blended so that said OH group may be present in an amount of 1/3 to 1 equivalent per equivalent of said isocyanate group and said epoxy group may be present in an amount of one-fifth to two-thirds equivalent per equivalent of said isocyanate group and the resulting blend being heated to effect masking of at least part of the NCO groups and thereby form said reaction product.
Claim 2
Dependent Claim
171 words
A thermosetting resin composition comprising a reaction product of an isocyanate compound having a molecular weight of 100 to 2000 and containing at least two isocyanate groups in its molecule with an epoxyphenol compound which is represented by the formula, ##EQU2## wherein R is a bi- or more valent group containing phenyl, R 1 is hydrogen, methyl or ethyl, m and n each are an integer of 1-8, and 0.01 to 10% by weight of a catalyst which forms an isocyanurate bond and an oxazolidone bond on curing, based on the weight of said reaction product, said isocyanate compound and said epoxyphenol compound being blended so that said OH group may be present in an amount of 1/3 to 1 equivalent per equivalent of said isocyanate group and said epoxy group may be present in an amount of one-fifth to two-thirds equivalent per equivalent of said isocyanate group and the resulting blend being heated to effect masking of at least part of the NCO groups and thereby form said reaction product.
Claim 3
Dependent Claim
29 words
A composition according to claim 1, wherein said catalyst is at least one selected from the group consisting of a tertiary amine a quaternary ammonium salt and an imidazole.
Claim 4
Dependent Claim
29 words
A composition according to claim 1, wherein the composition comprises further an epoxy compound containing at least two vicinal epoxy groups in its molecule and containing no OH group.
Claim 5
Dependent Claim
31 words
A composition according to claim 3, wherein said epoxy compound containing at least two vicinal epoxy groups in its molecule and containing no OH group is polyglycidylether of a phenol novolac.
Claim 6
Dependent Claim
191 words
A B-stage resin composition obtained by partially curing a thermosetting resin composition to form a resin composition having no three-dimensional structure, said thermosetting resin composition comprising a reaction product of an isocyanate compound having a molecular weight of 100 to 2000 and containing at least two isocyanate groups in its molecule with an epoxyphenol compound which is represented by the formula, ##STR3## wherein R is a bi- or more valent group containing phenyl, R 1 is hydrogen, methyl or ethyl, m and n each are an integer of 1-8, and 0.01 to 10% by weight of catalyst which forms an isocyanurate bond and an oxazolidone bond on curing, based on the weight of said reaction product, said isocyanate compound and said epoxyphenol compound being blended so that said OH group may be present in an amount of 1/3 to 1 equivalent per equivalent of said isocyanate group and said epoxy group may be present in an amount of one-half to two-thirds equivalent per equivalent of said isocyanate group and the resulting blend being heated to effect masking of at least part of the NCO groups and thereby form said reaction product.
Claim 7
Dependent Claim
191 words
A B-stage resin composition obtained by partially curing a thermosetting resin composition to form a resin composition having no three-dimensional structure, said thermosetting resin composition comprising a reaction product of an isocyanate compound having a molecular weight of 100 to 2000 and containing at least two isocyanate groups in its molecule with an epoxyphenol compound which is represented by the formula, ##STR3## wherein R is a bi- or more valent group containing phenyl, R 1 is hydrogen, methyl or ethyl, m and n each are an integer of 1-8, and 0.01 to 10% by weight of catalyst which forms an isocyanurate bond and an oxazolidone bond on curing, based on the weight of said reaction product, said isocyanate compound and said epoxyphenol compound being blended so that said OH group may be present in an amount of 1/3 to 1 equivalent per equivalent of said isocyanate group and said epoxy group may be present in an amount of one-half to two-thirds equivalent per equivalent of said isocyanate group and the resulting blend being heated to effect masking of at least part of the NCO groups and thereby form said reaction product.
Claim 8
Dependent Claim
29 words
A composition according to claim 5, wherein said catalyst is at least one selected from the group consisting of a tertiary amine a quaternary ammonium salt and an imidazole.
Claim 9
Dependent Claim
29 words
A composition according to claim 5, wherein the composition comprises further an epoxy compound containing at least two vicinal epoxy groups in its molecule and containing no OH group.
Claim 10
Dependent Claim
31 words
A composition according to claim 7, wherein said epoxy compound containing at least two vicinal epoxy groups in its molecule and containing no OH group is polyglycidylether of a phenol novolac.
Claim 11
Dependent Claim
21 words
A composition according to claim 1, wherein masking of a NCO group is effected by the formation of a urethane bond.
Claim 12
Dependent Claim
18 words
A composition according to claim 1, wherein the blend is heated to a temperature from 100° to 120°C.
Claim 13
Dependent Claim
17 words
A composition according to claim 1, wherein said blend is heated to a temperature up to 100°C.
Claim 14
Dependent Claim
24 words
A resin composition obtained from the composition of claim 5, wherein the B-stage resin composition is cured at a temperature of at least 130°C.
Claim 15
Dependent Claim
21 words
A composition according to claim 5, wherein masking of a NCO group is effected by the formation of a urethane bond.
Claim 16
Dependent Claim
18 words
A composition according to claim 5, wherein the blend is heated to a temperature from 100° to 120°C.
Claim 17
Dependent Claim
17 words
A composition according to claim 5, wherein said blend is heated to a temperature up to 100°C.
Claim 18
Dependent Claim
62 words
A composition according to claim 2, wherein said quaternary ammonium salt is selected from the group consisting of cetyltrimethylammonium bromide, cetyltrimethylammonium chloride, dodecyltrimethylammonium iodide, trimethyldodecylammonium chloride, benzyldimethyltetradecylammonium chloride, benzyldimethylpalmitylammonium chloride, allylcoconuttrimethylammonium bromide, benzylmethylstearylammonium bromide, stearyltrimethylammonium chloride and benzyldimethyltetradecylammonium acetylate and said imidazole is selected from the group consisting of 2-methylimidazole, 2-ethylimidazole, 2-undecylimidazole, 2-heptadecylimidazole, 2-methyl-4-ethylimidazole, 1-butylimidazole, 1-propyl-2-methylimidazole, 1-benzyl-2-methylimidazole, 1-cyanoethyl-2-undecylimidazole, 1-cyanoethyl-2-phenylimidazole, 1-azine-2-methylimidazole, and 1-azine-2-undecylimidazole.
Claim 19
Dependent Claim
62 words
A composition according to claim 6, wherein said quaternary ammonium salt is selected from the group consisting of cetyltrimethylammonium bromide, cetyltrimethylammonium chloride, dodecyltrimethylammonium iodide, trimethyldodecylammonium chloride, benzyldimethyltetradecylammonium chloride, benzyldimethylpalmitylammonium chloride, allylcoconuttrimethylammonium bromide, benzylmethylstearylammonium bromide, stearyltrimethylammonium chloride and benzyldimethyltetradecylammonium acetylate and said imidazole is selected from the group consisting of 2-methylimidazole, 2-ethylimidazole, 2-undecylimidazole, 2-heptadecylimidazole, 2-methyl-4-ethylimidazole, 1-butylimidazole, 1-propyl-2-methylimidazole, 1-benzyl-2-methylimidazole, 1-cyanoethyl-2-undecylimidazole, 1-cyanoethyl-2-phenylimidazole, 1-azine-2-methylimidazole, and 1-azine-2-undecylimidazole.
Claim 20
Dependent Claim
20 words
A composition according to claim 1, wherein said epoxy phenol compound has a molecular weight of from 100 to 2000.
Claim 21
Dependent Claim
20 words
A composition according to claim 5, wherein said epoxy phenol compound has a molecular weight of from 100 to 2000.
Claim 22
Dependent Claim
37 words
A resin composition obtained from the composition of claim 13, wherein the B-stage resin is cured at a temperature that causes cleavage of said urethane bond and the formation of an oxazolidone ring and an isocyanurate ring.
Claim 23
Dependent Claim
23 words
A composition according to claim 2, wherein said tertiary amine is selected from the group consisting of trimethylamine, triethylamine, tetramethylbutanediamine, tetramethylpentanediamine and tetramethylhexanediamine.
Claim 24
Dependent Claim
18 words
A composition according to claim 1, wherein the epoxyphenol compound is selected from the group consisting of: ##SPC10##
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-10-05 | 1980-04-05 | 1980-10-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-10-05 | 1984-04-05 | 1984-10-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-10-05 | 1988-04-05 | 1988-10-05 | $7700.00 | Window Closed / Lapsed |