Aluminum cartridge case
Assignee: Alcoa Corp
•
Filing: 1975-08-22
•
Granted: 1976-10-05
•
Expires: 1995-08-22
Abstract
Abstract An improved cartridge case is fabricated from rod or bar stock formed from a billet of an alloy containing, by weight, 5.2 to 6.2% Zn, 1.9 to 2.5% Mg, 1.2 to 1.9% Cu, 0.18 to 0.25% Cr, the remainder essentially aluminum. The method of fabrication of the cartridge case from a billet of the alloy comprises a controlled sequence of steps in forming rod or bar working stock so as to ensure against the formation of coarse recrystallized grains and the consequent forming of surface cracks or checks in subsequent metal working operations which include segmenting the rod, annealing the segmented parts and thereafter forming such segments into cartridge cases by cupping and wall ironing procedures. The mouth of the case can be annealed for ease of forming a retaining groove about a projectile positioned in the mouth of the case and in some instances for providing resistance to stress corrosion cracking.
Inventors
- 👤 Ralph W. Rogers, Jr.
- 👤 Charles H. Deveney
- 👤 Edsel W. Johnson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-10 02:34
CPC Classifications
C; C22; C22F; C22F1/00; C22F1/04; C22F1/053
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
165 words
A method of fabricating an improved aluminum cartridge case comprising: a. providing a body of aluminum alloy consisting essentially of, by weight, 5.2 to 6.2% Zn, 1.9 to 2.5% Mg, 1.2 to 1.9% Cu, 0.18 to 0.25% Cr, the balance essentially aluminum, b. homogenizing said body of subjecting it to a temperature of 800° to 890°F for a period of 4 to 12 hours, c. following said homogenizing, thermally treating said body at a temperature of 940°F to 1000°F for a period of 6 to 48 hours, d. extruding said body at a temperature of 550° to 800°F to rod or bar, e. annealing said extruded body, f. fabricating said rod or bar into cartridge cases by operations including dividing the rod or bar into segments, impact extruding said segments, thereafter drawing, ironing, and necking a portion to form to a cartridge case configuration, said operations including intermediate anneals with controlled cooling rates, and subsequently solution heat treating, quenching, and artificially aging said cartridge case.
Claim 2
Independent Claim
165 words
A method of fabricating an improved aluminum cartridge case comprising: a. providing a body of aluminum alloy consisting essentially of, by weight, 5.2 to 6.2% Zn, 1.9 to 2.5% Mg, 1.2 to 1.9% Cu, 0.18 to 0.25% Cr, the balance essentially aluminum, b. homogenizing said body of subjecting it to a temperature of 800° to 890°F for a period of 4 to 12 hours, c. following said homogenizing, thermally treating said body at a temperature of 940°F to 1000°F for a period of 6 to 48 hours, d. extruding said body at a temperature of 550° to 800°F to rod or bar, e. annealing said extruded body, f. fabricating said rod or bar into cartridge cases by operations including dividing the rod or bar into segments, impact extruding said segments, thereafter drawing, ironing, and necking a portion to form to a cartridge case configuration, said operations including intermediate anneals with controlled cooling rates, and subsequently solution heat treating, quenching, and artificially aging said cartridge case.
Claim 3
Dependent Claim
38 words
The method of claim 1 wherein said homogenizing is performed at a temperature of 860°F for a period of 6 hours and said thermal treating is performed at a temperature of 960°F for a period of 24 hours.
Claim 4
Dependent Claim
16 words
The method according to claim 1 wherein said extruding rate is about 10 to 16 ft./minute.
Claim 5
Dependent Claim
18 words
The method of claim 1 wherein segments are preformed to shallow cup form prior to said impact extruding.
Claim 6
Dependent Claim
41 words
The method of claim 1 wherein said anneals are provided at a temperature of 675° to 875°F for a period of 1/2 to 4 hours and said cooling rates are about 50°F/hr. to a temperature of about 450°F thereafter air cooled.
Claim 7
Dependent Claim
27 words
The method of claim 1 wherein said solution heat treating is performed at a temperature of 925 to 950°F for a period of 1/2 to 1 hour.
Claim 8
Dependent Claim
27 words
The method according to claim 1 including annealing the necked portion of said cartridge case at a temperature of 550° to 600°F for 30 to 60 seconds.
Claim 9
Dependent Claim
109 words
In the method of producing an aluminum cartridge case wherein elongate rod stock is segmented to provide blanks which are annealed, cupped and wall ironed and necked, the improvements comprising providing working stock in an aluminum alloy cosisting essentially of, by weight, 5.2 to 6.2% Zn, 1.9 to 2.5% Mg, 1.2 to 1.9% Cu, 0.18 to 0.25% Cr, the balance essentially aluminum, and working said stock to provide said rod stock, said working being substantially carried out at metal temperatures of from 550° to 800°F and at relatively slow rates to avoid formation of cracks while avoiding cold working effects which favor formation of large recrystallized grains on annealing.
Claim 10
Dependent Claim
109 words
In the method of producing an aluminum cartridge case wherein elongate rod stock is segmented to provide blanks which are annealed, cupped and wall ironed and necked, the improvements comprising providing working stock in an aluminum alloy cosisting essentially of, by weight, 5.2 to 6.2% Zn, 1.9 to 2.5% Mg, 1.2 to 1.9% Cu, 0.18 to 0.25% Cr, the balance essentially aluminum, and working said stock to provide said rod stock, said working being substantially carried out at metal temperatures of from 550° to 800°F and at relatively slow rates to avoid formation of cracks while avoiding cold working effects which favor formation of large recrystallized grains on annealing.
Claim 11
Independent Claim
212 words
A method of fabricating an improved aluminum cartridge case comprising: a. providing a body of aluminum alloy consisting essentially of 5.2-6.2% Zn, 1.9-2.5% Mg, 1.2-1.9% Cu, 0.18-0.25% Cr, the balance essentially aluminum, b. homogenizing said body at a temperature of about 800°-890°F for a period of 4 to 12 hours, c. thermally treating said body at a temperature of 940°F to 1000°F for a period of 6 to 48 hours, d. extruding said body at a temperature of 550°-800°F to rod, e. dividing said rod into segments, f. annealing said segments at a temperature of about 675°-875°F for about 1/2 to 2 hours and cooling said segments slowly thereafter, g. impact extruding said segments to thick walled cups, h. annealing said cups at about 675°-875°F for about 1/2 to 2 hours and cooling at a rate of 50°F/hr. to a temperature of about 450°F, i. drawing and ironing said cups to form a cylindrical shaped case having one end thereof closed and the other end open to provide a mouth section, j. necking a portion of said case adjacent the mouth, thereby providing a cartridge case configuration, k. solution heat treating said case at 925° to 950°F for a period of 1/2 to 1 hour, l. quenching, m. artificially aging said case.
Claim 12
Independent Claim
212 words
A method of fabricating an improved aluminum cartridge case comprising: a. providing a body of aluminum alloy consisting essentially of 5.2-6.2% Zn, 1.9-2.5% Mg, 1.2-1.9% Cu, 0.18-0.25% Cr, the balance essentially aluminum, b. homogenizing said body at a temperature of about 800°-890°F for a period of 4 to 12 hours, c. thermally treating said body at a temperature of 940°F to 1000°F for a period of 6 to 48 hours, d. extruding said body at a temperature of 550°-800°F to rod, e. dividing said rod into segments, f. annealing said segments at a temperature of about 675°-875°F for about 1/2 to 2 hours and cooling said segments slowly thereafter, g. impact extruding said segments to thick walled cups, h. annealing said cups at about 675°-875°F for about 1/2 to 2 hours and cooling at a rate of 50°F/hr. to a temperature of about 450°F, i. drawing and ironing said cups to form a cylindrical shaped case having one end thereof closed and the other end open to provide a mouth section, j. necking a portion of said case adjacent the mouth, thereby providing a cartridge case configuration, k. solution heat treating said case at 925° to 950°F for a period of 1/2 to 1 hour, l. quenching, m. artificially aging said case.
Claim 13
Dependent Claim
22 words
The method of claim 9, including annealing said neck portion at a temperature of 550° to 600°F for 30 to 60 seconds.
References Cited (Backward Citations)
US2736085A
Cited
US2220652A
Cited
US3498221A
Cited
US3614816A
Cited
US3761322A
Cited
US3765297A
Cited
US3791880A
Cited
US3802931A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-10-05 | 1980-04-05 | 1980-10-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-10-05 | 1984-04-05 | 1984-10-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-10-05 | 1988-04-05 | 1988-10-05 | $7700.00 | Window Closed / Lapsed |