Treatment of the surfaces of polyphenylene oxide materials
Assignee: MacDermid Europe Ltd
•
Filing: 1974-09-23
•
Granted: 1976-09-28
•
Expires: 1994-09-23
Abstract
Abstract The conventional electroless plating process for polymers involving (1) acid etching (2) activation by a mixture of tin salts and precious metal salts applied jointly or consecutively and (3) electroless deposition on to the activated surface, is improved by an intermediate treatment with a reducing acid solution between stages (1) and (2). Phosphorous, hypophosphorous, ortho-, hypo- and pyrophosphoric acids, preferably in amounts from 25-500 g./l. and optionally with their alkali metal and/or ammonium salts in amounts up to 500 g./l. as buffers can be used for immersions of up to 20 minutes at temperatures up to 70°C. Poly phenylene oxides, ABS polymers, and polyolefins can be treated.
Inventors
- 👤 Philip John Norris
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 11:17
CPC Classifications
C; C23; C23C; C23C18/00; C23C18/16; C23C18/18; C23C18/20; C23C18/22; C23C18/24; H; H05; H05K; H05K1/00; H05K1/02; H05K1/03; H05K1/0313; H05K1/032; H05K1/0326; H05K3/00; H05K3/10; H05K3/18; H05K3/181; H05K3/38; H05K3/381
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
65 words
A process for preparing the surface of a polyphenylene oxide material for electroless deposit of metal prior to activation of the surface thereof, comprising: etching the surface of the material with an etch containing chromic acid, and treating the etched surface with an aqueous solution containing at least one strongly reducing acid selected from the group consisting of phosphorous acid, hypophosphorous acid and hypophosphoric acid.
Claim 2
Dependent Claim
65 words
A process for preparing the surface of a polyphenylene oxide material for electroless deposit of metal prior to activation of the surface thereof, comprising: etching the surface of the material with an etch containing chromic acid, and treating the etched surface with an aqueous solution containing at least one strongly reducing acid selected from the group consisting of phosphorous acid, hypophosphorous acid and hypophosphoric acid.
Claim 3
Dependent Claim
17 words
A process as claimed in claim 1 wherein the acid concentration is from 25 to 500 g./l.
Claim 4
Dependent Claim
25 words
A process as claimed in claim 1 wherein the solution is buffered with at least one salt of at least one of the said acids.
Claim 5
Dependent Claim
42 words
A process as claimed in claim 3 wherein the solution is buffered with up to 500 g./l. of at least one member selected from the group consisting of the alkali metal and ammonium salts of at least one of the said acids.
Claim 6
Dependent Claim
22 words
A process as claimed in claim 1 wherein the surface is immersed for 1 to 10 minutes at 15° to 65° C.
Claim 7
Dependent Claim
21 words
The process of claim 1 wherein said strongly reducing acid is phosphorous acid, said phosphorous acid being buffered with sodium hypophosphite.
References Cited (Backward Citations)
US3702285A
Cited
US3592680A
Cited
US3620804A
Cited
US3704156A
Cited
US3686017A
Cited
US3758332A
Cited
US3790400A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-09-28 | 1980-03-29 | 1980-09-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-09-28 | 1984-03-29 | 1984-09-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-09-28 | 1988-03-29 | 1988-09-28 | $7700.00 | Window Closed / Lapsed |