Synthetic amorphous silicas of predetermined pore distribution method of producing same
Assignee: Mobil Oil AS
•
Filing: 1974-03-14
•
Granted: 1976-09-28
•
Expires: 1994-03-14
Abstract
Abstract Novel amorphous siliceous materials having shape-selective sorption properties are prepared by a novel process of (1) hydrolyzing an organosilicon compound of the formula R[Si]X3 alone or in the presence of one or more compounds either of the formula R'nMYm, wherein R and R' are non-hydrolyzable organic groups, X is a hydrolyzable group, Y is the same as X or oxygen, [Si] is silicon or -Si(R)2-O-Si , M is metal or non-metal, including silicon, of any group of the Periodic Table other than IA, IIA, VIIA or O, m is a number over 0 and up to 8 and n is 0 or a number less than 8, or an inorganic compound consisting of an anionic portion made up of M and y and a cationic portion of either hydrogen, alkali or alkaline earth metal or ammonium; (2) effecting condensation polymerization of the hydrolyzed product; and (3) calcining the resulting polymerized product to convert all the R and R' groups to hydroxy or hydrogen. Pore size distribution of the final composition is primarily controlled by appropriate selection of the R group of the R[Si]X3 precursor. The amorphous synthetic solids of this invention are useful in such conversion processes as shape-selective cracking, hydrocracking, hydrogenation-dehydrogenation, oxidation, and methanation processes. They are also useful as sorbents and catalyst supports.
Inventors
- 👤 Thomas O. Mitchell
- 👤 Darrell Duayne Whitehurst
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 17:08
CPC Classifications
C; C10; C10G; C10G45/00; C10G45/58; C10G45/60; B; B01; B01J; B01J21/00; B01J21/06; B01J21/08; B01J37/00; C07; C07C; C07C1/00; C07C1/32; C07C1/321; C07C1/322; C07C4/00; C07C4/02; C07C4/06; C07C5/00; C07C5/02; C07C5/03; C08; C08G; C08G77/00; C08G77/04; C08G77/06; C08G77/38; C10G45/02; C10G45/04; C07C2521/00; C07C2521/02; C07C2521/06; C07C2523/00; C07C2523/38; C07C2523/40; C07C2523/44; C07C2523/70; C07C2523/74; C07C2523/75; C07C2523/755; C10G2400/00; C10G2400/26
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
115 words
A synthetic amorphous solid having shape selective properties prepared by the steps of (1) hydrolyzing and (2) polymerizing at up to 200°C. in the presence of water a silane having the formula R[Si]X 3 wherein X is a hydrolyzable group R is a nonhydrolyzable group and [Si] is selected from the group consisting of --Si and --Si(R) 2 --O--Si and (3) calcining the polymerized product wherein there is also present in the final calcined product in addition to silicon at least one member selected from the group consisting of groups IIIA, IVA, IVB, VA, VB, VIB VIIB and VIII of the Periodic Table the source of said member being present in the initial hydrolyzing step.
Claim 2
Dependent Claim
115 words
A synthetic amorphous solid having shape selective properties prepared by the steps of (1) hydrolyzing and (2) polymerizing at up to 200°C. in the presence of water a silane having the formula R[Si]X 3 wherein X is a hydrolyzable group R is a nonhydrolyzable group and [Si] is selected from the group consisting of --Si and --Si(R) 2 --O--Si and (3) calcining the polymerized product wherein there is also present in the final calcined product in addition to silicon at least one member selected from the group consisting of groups IIIA, IVA, IVB, VA, VB, VIB VIIB and VIII of the Periodic Table the source of said member being present in the initial hydrolyzing step.
Claim 3
Dependent Claim
27 words
The solid of claim 1 wherein R is selected from the group consisting of alkyl, cycloalkyl, aryl, alkenyl, cycloalkenyl and the said groups hydroxy-substituted, halogen-substituted and amino-substituted.
Claim 4
Dependent Claim
32 words
The solid of claim 1 wherein X is selected from the group consisting of halogen and alkoxy of from 1 to 10 carbon atoms, alkali metal-oxy, alkaline earth metal-oxy, carboxy and amino.
Claim 5
Dependent Claim
9 words
The solid of claim 3 wherein X is chlorine.
Claim 6
Dependent Claim
35 words
The solid of claim 4 wherein R[Si]X 3 is selected from the group consisting of phenyl trichlorosilane, (C 6 H 5 ) 3 Si--O--SiCl 3 , methyl trichlorosilane, ethyl trichlorosilane, dodecyl trichlorosilane and mixtures thereof.
Claim 7
Dependent Claim
22 words
The solid of claim 1 wherein the calcination step is carried out in a stepwise heating up to a temperature about 550°C.
Claim 8
Dependent Claim
100 words
The solid of claim 1 wherein there is also present in the hydrolysis and polymerization step a second compound R' n MY m wherein R' is selected from the group consisting of the same groups as R, Y is selected from the group consisting of the same groups as X and oxygen, M is at least one member selected from the group consisting of Groups IIIA, IVA, IVB, VA, VB, VIB, VIIB and VIII of the Periodic Table, m is any number greater than 0 and up to 8 and n is from 0 to any number less than 8.
Claim 9
Dependent Claim
25 words
The solid of claim 7 wherein M is selected from the group consisting of aluminum, phosphorus, nickel, cobalt, vanadium, titanium, platinum, palladium, tin and boron.
Claim 10
Dependent Claim
31 words
The solid of claim 8 wherein M is aluminum and hydrolysis and polymerization are carried out in the presence of a minor amount sufficient to promote polymerization of an organic amine.
Claim 11
Dependent Claim
18 words
The solid of claim 9 wherein the amine is selected from the group consisting of pyridine and triethylamine.
Claim 12
Dependent Claim
24 words
The solid of claim 1 wherein hydrolysis and polymerization are carried out in the presence of a mixture of water and an organic solvent.
Claim 13
Dependent Claim
20 words
The solid of claim 7 wherein the second compound is an aluminum alkoxide of from 1 to 10 carbon atoms.
Claim 14
Dependent Claim
12 words
The solid of claim 7 wherein the second compound is aluminum chloride.
Claim 15
Dependent Claim
24 words
The solid of claim 1 wherein there is present in the final structure a member selected from the group consisting of platinum and palladium.
Claim 16
Dependent Claim
26 words
The solid of claim 1 wherein there is present in the final structure aluminum and a member selected from the group consisting of cobalt and nickel.
Claim 17
Dependent Claim
43 words
The solid of claim 7 wherein there is present in the hydrolysis and polymerization step an inorganic compound consisting of an anion of M and Y and a cation selected from the group consisting of hydrogen, alkali metal, alkaline earth metal and ammonium.
Claim 18
Dependent Claim
25 words
The solid of claim 16 wherein the compound is selected from the group consisting of boric acid, sodium ethyl chloroplatinate, chloroplatinic acid and sodium aluminate.
Claim 19
Dependent Claim
39 words
The solid of claim 1 wherein silanes selected from the group consisting of SiX 4 , R 2 [Si]X 2 and R 3 [Si]X are also present, the concentration of R[Si]X 3 being at least 33 percent by weight.
Claim 20
Dependent Claim
11 words
The solid of claim 11 wherein the organic solvent is methanol.
Claim 21
Dependent Claim
64 words
A process of preparing the solid of claim 1 by the steps of hydrolyzing R[Si]X 3 wherein R is selected from the group consisting of alkyl, aryl and the said groups halogen-substituted and amino-substituted with water or water plus organic solvent, effecting polymerization of said hydrolyzed product and calcining the polymer by heating to 550°C. at the rate of 10° to 300°C. per hour.
Claim 22
Dependent Claim
45 words
The process of claim 20 wherein there is present in the hydrolyzing and polymerization step a second component whereby the final calcined product contains at least one member selected from the group consisting of aluminum, phosphorus, nickel, cobalt, vanadium, titanium, platinum, palladium, tin and boron.
Claim 23
Dependent Claim
12 words
The solid of claim 11 wherein the organic solvent is an alcohol.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-09-28 | 1980-03-29 | 1980-09-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-09-28 | 1984-03-29 | 1984-09-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-09-28 | 1988-03-29 | 1988-09-28 | $7700.00 | Window Closed / Lapsed |