Method of forming uniform density articles from powder metals
Assignee: RTX Corp
•
Filing: 1974-05-31
•
Granted: 1976-09-28
•
Expires: 1994-05-31
Abstract
Abstract The present invention provides a method and apparatus for powder metal formation in which a plated shell is formed corresponding to the appropriate calculated pre press size of the final part being formed; the electroplate shell is filled with powder metal to be formed; the shell is surrounded by a pressure transferring support media and compacted using a suitable force transmitter such as an isostatic press; and the support media is removed leaving the final product within the electroplate shell which may or may not be removed as desired.
Inventors
- 👤 Joseph M. Wentzell
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 17:45
CPC Classifications
B; B22; B22F; B22F3/00; B22F3/12; B22F3/14; B22F3/15; B22F3/02; B22F3/04; B22F3/1208; B22F3/1258; B22F3/1275
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
128 words
A method for forming a powder metal article of uniform density comprising the steps of: a. forming a metallic shell on form having the appropriate prepress size of the desired article, the form being made of a selectively removable material; b. surrounding the form having the metallic shell thereon with a support media; c. selectively removing the form from the metallic shell, the shell remaining surrounded by the support media and defining a cavity having the appropriate prepress size of the desired article; d. filling the cavity defined by the shell with powder metal; e. pressing the support media and filled shell to compact the powder metal into the desired article; and f. removing the support media from the compacted article, the article having the metallic shell thereon.
Claim 2
Independent Claim
128 words
A method for forming a powder metal article of uniform density comprising the steps of: a. forming a metallic shell on form having the appropriate prepress size of the desired article, the form being made of a selectively removable material; b. surrounding the form having the metallic shell thereon with a support media; c. selectively removing the form from the metallic shell, the shell remaining surrounded by the support media and defining a cavity having the appropriate prepress size of the desired article; d. filling the cavity defined by the shell with powder metal; e. pressing the support media and filled shell to compact the powder metal into the desired article; and f. removing the support media from the compacted article, the article having the metallic shell thereon.
Claim 3
Dependent Claim
18 words
The method of claim 1 including the additional step of removing the metallic shell from the compacted article.
Claim 4
Dependent Claim
117 words
The method of claim 1 wherein the form is provided in the appropriate prepress size of the desired article by: a. providing a pattern having the dimensions of the desired article multiplied by the reciprocal of the cube root of the tap density of the powder metal to be formed; b. forming a female mold around the pattern; c. removing the female mold from the pattern, the mold having developed the desired strength and having a cavity in the shape of the pattern; d. filling the mold cavity with casting material; e. solidifying the casting material in the mold cavity; and f. removing the formed casting from the mold, the casting having the shape of the pattern.
Claim 5
Dependent Claim
17 words
The method of claim 1 wherein the metallic shell is formed by electroplating an electrically conductive form.
Claim 6
Dependent Claim
14 words
The method of claim 1 wherein the metallic shell is formed by vapor deposition.
Claim 7
Dependent Claim
11 words
The method of claim 1 wherein the metallic shell is nickel.
Claim 8
Dependent Claim
34 words
The method of claim 1 wherein the support media is powdered material pressed to a percentage of theoretical density substantially equal to the percentage of theoretical density of the powder metal to be formed.
Claim 9
Dependent Claim
13 words
The method of claim 1 wherein the support media is sintered iron powder.
Claim 10
Dependent Claim
12 words
The method of claim 1 wherein the support media is ceramic grit.
Claim 11
Dependent Claim
12 words
The method of claim 1 wherein the support media is liquid material.
Claim 12
Dependent Claim
12 words
The method of claim 1 wherein the powder metal is superalloy powder.
Claim 13
Dependent Claim
18 words
The method of claim 1 wherein the support media and filled shell are compacted by hot isostatic pressing.
Claim 14
Dependent Claim
16 words
The method of claim 1 wherein the support media and filled shell are compacted by forging.
Claim 15
Independent Claim
160 words
A method of forming a powder metal article of uniform density comprising the steps of: a. providing a nonconductive form in the appropriate prepress size of the desired article, the form being made of a selectively removable material; b. coating the form with a layer of conductive material, said conductive material being selectively removable; c. electroplating the conductive layer to form a metallic shell; d. surrounding the form having the conductive layer and metallic shell thereon with a support media; e. selectively removing the form and conductive layer from the metallic shell, the shell remaining surrounded by the support media and defining a cavity having the appropriate prepress size of the article to be formed; f. filling the cavity defined by the shell with powder metal; g. pressing the support media and filled shell to compact the powder metal into the desired article; and h. removing the support media from the compacted article, the article having the metallic shell thereon.
Claim 16
Independent Claim
160 words
A method of forming a powder metal article of uniform density comprising the steps of: a. providing a nonconductive form in the appropriate prepress size of the desired article, the form being made of a selectively removable material; b. coating the form with a layer of conductive material, said conductive material being selectively removable; c. electroplating the conductive layer to form a metallic shell; d. surrounding the form having the conductive layer and metallic shell thereon with a support media; e. selectively removing the form and conductive layer from the metallic shell, the shell remaining surrounded by the support media and defining a cavity having the appropriate prepress size of the article to be formed; f. filling the cavity defined by the shell with powder metal; g. pressing the support media and filled shell to compact the powder metal into the desired article; and h. removing the support media from the compacted article, the article having the metallic shell thereon.
Claim 17
Dependent Claim
18 words
The method of claim 14 including the additional step of removing the metallic shell from the compacted article.
Claim 18
Dependent Claim
120 words
The method of claim 14 wherein the form is provided in the appropriate prepress size of the article to be formed by: a. providing a pattern having the dimensions of the desired article multiplied by the reciprocal of the cube root of the tap density of the powder metal to be formed; b. forming a female mold around the pattern; c. removing the female mold from the pattern, the mold having developed the desired strength and having a cavity in the shape of the pattern; d. filling the mold cavity with nonconductive casting material; e. solidifying the casting material in the mold cavity; and f. removing the formed casting from the mold, the casting having the shape of the pattern.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-09-28 | 1980-03-29 | 1980-09-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-09-28 | 1984-03-29 | 1984-09-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-09-28 | 1988-03-29 | 1988-09-28 | $7700.00 | Window Closed / Lapsed |