Assignee: MacDermid Inc
•
Filing: 1974-10-11
•
Granted: 1976-09-21
•
Expires: 1994-10-11
Abstract
Abstract Circuit boards for electronic equipment are produced in which the circuit-forming conductor metal is deposited on a suitably catalyzed and masked resin substrate by all-electroless deposition techniques, wherein the characterizing feature of the invention is the use of a separate acceleration step after catalyzing and prior to application of a resist mask, supplementary of the usual post-masking accelerating step. Improved surface resistivity or insulation resistance in the printed circuit board and improved adhesion of the electrolessly deposited metal are achieved.
Inventors
- 👤 Peter E. Kukanskis
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 04:33
CPC Classifications
C; C23; C23C; C23C18/00; C23C18/16; C23C18/18; C23C18/20; C23C18/28; C23C18/30; C23C18/1601; C23C18/1603; C23C18/1605; C23C18/285; H; H05; H05K; H05K3/00; H05K3/10; H05K3/18; H05K3/181; H05K3/182; H05K3/184; H05K2203/00; H05K2203/07; H05K2203/0703; H05K2203/0716; H05K2203/14; H05K2203/1407
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
171 words
In the plating of a non-conductive substrate by an all-additive electroless plating process wherein the process includes the usual steps in sequence of treating the substrate surface with a precious metal catalyst solution to produce sites catalytic to the reduction thereon of a metal from an electroless metal plating solution, applying a permanently retained resist mask to portions of the catalytically activated surface to define a desired pattern resistive to deposition of electroless metal, accelerating the substrate surface by treatment in a dilute acid or alkali solution to reactivate the unmasked catalyzed areas, and then electrolessly plating the substrate in a reducing solution of the metal to be plated to provide the total desired thickness of metal deposit on the substrate, the improvement in such process which comprises: subjecting the substrate to another accelerating step in dilute acid or alkali solution subsequent to catalyzation but prior to application of the permanent resist mask, whereby to increase the surface resistivity between plated areas of the substrate and improve the plated metal adhesion.
Claim 2
Dependent Claim
171 words
In the plating of a non-conductive substrate by an all-additive electroless plating process wherein the process includes the usual steps in sequence of treating the substrate surface with a precious metal catalyst solution to produce sites catalytic to the reduction thereon of a metal from an electroless metal plating solution, applying a permanently retained resist mask to portions of the catalytically activated surface to define a desired pattern resistive to deposition of electroless metal, accelerating the substrate surface by treatment in a dilute acid or alkali solution to reactivate the unmasked catalyzed areas, and then electrolessly plating the substrate in a reducing solution of the metal to be plated to provide the total desired thickness of metal deposit on the substrate, the improvement in such process which comprises: subjecting the substrate to another accelerating step in dilute acid or alkali solution subsequent to catalyzation but prior to application of the permanent resist mask, whereby to increase the surface resistivity between plated areas of the substrate and improve the plated metal adhesion.
Claim 3
Dependent Claim
19 words
The improved process defined in claim 1, wherein the pre- and post-masking accelerating solutions are of the same composition.
Claim 4
Dependent Claim
26 words
The improved process defined in claim 1, wherein said catalyst solution is a mixed tin-palladium chloride solution and both accelerating solutions are dilute fluoroboric acid solutions.
Claim 5
Dependent Claim
24 words
The improved process defined in claim 1, wherein the non-conductive substrate is a phenolic, paper reinforced phenolic, epoxy or fiber glass reinforced epoxy member.
Claim 6
Dependent Claim
32 words
The improved process defined in claim 1, wherein the accelerating solutions are aqueous solutions of about 10% hydrochloric acid, 10% sulfuric acid, 20% perchloric acid, 10% fluoroboric acid or 5% sodium hydroxide.
Claim 7
Dependent Claim
24 words
The improved process defined in claim 1, wherein said substrate is immersed in said other accelerating solution at ambient temperature for about 2 minutes.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-09-21 | 1980-03-22 | 1980-09-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-09-21 | 1984-03-22 | 1984-09-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-09-21 | 1988-03-22 | 1988-09-21 | $7700.00 | Window Closed / Lapsed |