Process for preparing copolymers of ethylene and vinyl esters or mixtures with other ethylenically unsaturated monomers
Assignee: ExxonMobil Technology and Engineering Co
•
Filing: 1975-08-19
•
Granted: 1976-09-21
•
Expires: 1995-08-19
Abstract
Abstract Polymers of 1,000 to 50,000 and preferably of 1,000 to 2,900 number average molecular weight, comprising 3 to 40 molar proportions of ethylene per molar proportion of an ethylenically unsaturated monomer, are prepared by free radical catalysts in a solvent at temperatures of less than 130 DEG C. in order to minimize ethylene branching, for use as wax crystal modifying agents, e.g. pour depressants and flow improvers for distillate mineral oil, e.g. middle distillate fuel oil.
Inventors
- 👤 Max J. Wisotsky
- 👤 Norman Tunkel
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 20:39
CPC Classifications
C; C08; C08F; C08F210/00; C08F210/02; C08F10/00; C08F218/00; C08F218/02; C08F218/04; C08F218/08; C08F220/00; C08F220/02; C08F220/10; C08F220/12; C10; C10G; C10G73/00; C10G73/02; C10G73/04; C10L; C10L1/00; C10L1/10; C10L1/14; C10L1/18; C10L1/192; C10L1/195; C10L1/196; C10L1/1963; C10L1/1966; C10L1/197; C10L1/1973; C10M; C10M2209/00; C10M2209/02; C10M2209/04; C10M2209/06; C10M2209/062; C10M2209/08; C10M2209/084; C10M2209/086
Claims Analysis
Total Claims: 4
Claim 1
Independent Claim
78 words
A method of copolymerizing about 3 to 20 molar proportions of ethylene per molar proportion of vinyl acetate to form a pour depressant copolymer having less than 6 methyl terminating side branches per 100 methylene groups and having a molecular weight of about 1,000 to 2,900, which comprises copolymerizing said ethylene and vinyl acetate in cyclohexane as solvent at a temperature of about 70° to 130°C. using dilauroyl peroxide catalyst and under pressure of 500 to 3,000 psi.
Claim 2
Independent Claim
78 words
A method of copolymerizing about 3 to 20 molar proportions of ethylene per molar proportion of vinyl acetate to form a pour depressant copolymer having less than 6 methyl terminating side branches per 100 methylene groups and having a molecular weight of about 1,000 to 2,900, which comprises copolymerizing said ethylene and vinyl acetate in cyclohexane as solvent at a temperature of about 70° to 130°C. using dilauroyl peroxide catalyst and under pressure of 500 to 3,000 psi.
Claim 3
Dependent Claim
26 words
A method according to claim 1, wherein said molecular weight is about 1500 to 2500, and said temperature is in the range of 80° to 125°C.
Claim 4
Dependent Claim
37 words
A method according to claim 1, wherein said copolymer is characterized by about two methyl terminating side branches per 100 methylene groups as measured by nuclear magnetic resonance other than the methyl groups on the vinyl acetate.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-09-21 | 1980-03-22 | 1980-09-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-09-21 | 1984-03-22 | 1984-09-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-09-21 | 1988-03-22 | 1988-09-21 | $7700.00 | Window Closed / Lapsed |