Article having a poly(arylene sulfide) coating and method of producing
Assignee: Phillips Petroleum Co
•
Filing: 1975-05-14
•
Granted: 1976-09-07
•
Expires: 1995-05-14
Abstract
Abstract Addition of a siliceous material having a particle size of less than 10 microns to a poly(arylene sulfide) coating formulation yields a coating with improved surface characteristics for use as a release coating in conjunction with high temperature molding, extruding, or material handling equipment.
Inventors
- 👤 David E. Higbee
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 21:13
CPC Classifications
C; C09; C09D; C09D181/00; C09D181/02; B; B29; B29C; B29C33/00; B29C33/56; B29C33/60; B29C33/62; Y; Y10; Y10T; Y10T428/00; Y10T428/25; Y10T428/251; Y10T428/252; Y10T428/259; Y10T428/31504; Y10T428/31533
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
53 words
A coated article comprising a substrate having a coating bonded thereto of a composition comprising a normally solid poly(arylene sulfide) and from about 0.3 percent to about 4 percent by weight, based on the weight of poly(arylene sulfide), of a finely divided siliceous material having a particle size less than about 10 microns.
Claim 2
Dependent Claim
53 words
A coated article comprising a substrate having a coating bonded thereto of a composition comprising a normally solid poly(arylene sulfide) and from about 0.3 percent to about 4 percent by weight, based on the weight of poly(arylene sulfide), of a finely divided siliceous material having a particle size less than about 10 microns.
Claim 3
Dependent Claim
22 words
The article of claim 1 wherein said siliceous material is selected from the group consisting of silica, silicates, alumino-silicates, and combinations thereof.
Claim 4
Dependent Claim
14 words
The article of claim 2 wherein the normally solid poly(arylene sulfide) is poly(phenylene sulfide).
Claim 5
Dependent Claim
48 words
The article of claim 2 wherein said composition contains from about 0.5 percent to about 100 percent by weight titanium dioxide based on the weight of poly(arylene sulfide) and from about 0.5 percent to about 75 percent by weight fluorocarbon polymer based on the weight of poly(arylene sulfide.
Claim 6
Dependent Claim
93 words
The article of claim 4 wherein said fluorocarbon polymer is polytetrafluoroethylene, wherein said poly(arylene sulfide) is poly(phenylene sulfide), wherein said composition contains from about 10 to about 50 percent by weight titanium dioxide based on the weight of poly(phenylene sulfide), from about 5 to about 35 percent by weight polytetrafluoroethylene based on the weight of poly(phenylene sulfide), and from about 0.4 to about 2 percent by weight of said siliceous material based on the weight of poly(phenylene sulfide), and wherein the particle size of said siliceous material is less than about 2 microns.
Claim 7
Dependent Claim
12 words
The article of claim 5 wherein said siliceous material is bentonite clay.
Claim 8
Independent Claim
98 words
The method of producing a glossy poly(arylene sulfide) coating of substantially uniform thickness comprising: covering the surface of the article to be coated with a slurry containing poly(arylene sulfide) and from about 0.3 to about 4 weight percent of a finely divided siliceous material having a particle size less than about 10 microns, based on the weight of poly(arylene sulfide); and curing the thus-covered surface in oxygen-containing atmosphere at a temperature within the range of about 500° F. to about 900° F. for a period of time within the range of about 5 minutes to about 12 hours.
Claim 9
Independent Claim
98 words
The method of producing a glossy poly(arylene sulfide) coating of substantially uniform thickness comprising: covering the surface of the article to be coated with a slurry containing poly(arylene sulfide) and from about 0.3 to about 4 weight percent of a finely divided siliceous material having a particle size less than about 10 microns, based on the weight of poly(arylene sulfide); and curing the thus-covered surface in oxygen-containing atmosphere at a temperature within the range of about 500° F. to about 900° F. for a period of time within the range of about 5 minutes to about 12 hours.
Claim 10
Dependent Claim
22 words
The method of claim 7 wherein said siliceous material is selected from the group consisting of silica, silicates, alumino-silicates, and combinations thereof.
Claim 11
Dependent Claim
12 words
The method of claim 8 wherein said poly(arylene sulfide) is poly(phenylene sulfide).
Claim 12
Dependent Claim
81 words
The method of claim 8 wherein said slurry comprises, in addition, from about 10 percent to about 50 percent by weight titanium dioxide based on the weight of poly(phenylene sulfide) and from about 5 percent to about 35 percent by weight of polytetrafluoroethylene based on the weight of poly(phenylene sulfide), and wherein said siliceous material is present in said slurry in an amount in the range of about 0.5 to about 1 weight percent based on the weight of poly(phenylene sulfide).
References Cited (Backward Citations)
US3492125A
Cited
US3487454A
Cited
US3622376A
Cited
US3634125A
Cited
US3652327A
Cited
US3925530A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-09-07 | 1980-03-08 | 1980-09-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-09-07 | 1984-03-08 | 1984-09-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-09-07 | 1988-03-08 | 1988-09-07 | $7700.00 | Window Closed / Lapsed |