Polyurethane elastomers having improved sag resistance
Assignee: Texaco Inc
•
Filing: 1974-09-23
•
Granted: 1976-09-07
•
Expires: 1994-09-23
Abstract
Abstract The use of small amounts of an amine-terminated polyether in the B-component of a two-component polyurethane composition results in the immediate thickening of the A and B-components upon mixing to provide an elastomer precursor with improved sag resistance without substantially affecting the workability of the mixed components or the properties of the cured elastomer. These elastomers are useful as sealants, caulks and surface coatings.
Inventors
- 👤 Richard Lee Rowton
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 22:35
CPC Classifications
C; C08; C08G; C08G18/00; C08G18/06; C08G18/28; C08G18/40; C08G18/48; C08G18/50; C08G18/5021; C08G18/5051; C08G18/2805; C08G18/2815; C08G18/283; C08G18/4804; C08G18/482; C08G18/5024; C08G2190/00
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
148 words
In a polyurethane elastomer composition prepared by admixing and reacting an organic polyisocyanate compound having free isocyanate moieties, a polyether polyol compound and a selected urethane catalyst, the improvement which comprises: adding to said admixture from about 1 to about 50 equivalents per 100 equivalents of said polyether polyol of a polyoxyalkylene polyamine of the formula: ##EQU1## wherein R is the nucleus of an oxyalkylation-susceptible saturated polyhydric alcohol containing 2 to 12 carbon atoms and 2 to 8 hydroxyl groups and R consists of hydrogen and carbon, Z is an alkyl group containing 1 to 18 carbon atoms, X and Y independently are hydrogen or Z, A is cyano-loweralkyl of 1 to 2 carbon atoms or hydrogen, n has an average value of 0 to 50 and m is an integer of 2 to 8 corresponding to the number of hydroxyl groups originally present in the polyhydric alcohol.
Claim 2
Dependent Claim
148 words
In a polyurethane elastomer composition prepared by admixing and reacting an organic polyisocyanate compound having free isocyanate moieties, a polyether polyol compound and a selected urethane catalyst, the improvement which comprises: adding to said admixture from about 1 to about 50 equivalents per 100 equivalents of said polyether polyol of a polyoxyalkylene polyamine of the formula: ##EQU1## wherein R is the nucleus of an oxyalkylation-susceptible saturated polyhydric alcohol containing 2 to 12 carbon atoms and 2 to 8 hydroxyl groups and R consists of hydrogen and carbon, Z is an alkyl group containing 1 to 18 carbon atoms, X and Y independently are hydrogen or Z, A is cyano-loweralkyl of 1 to 2 carbon atoms or hydrogen, n has an average value of 0 to 50 and m is an integer of 2 to 8 corresponding to the number of hydroxyl groups originally present in the polyhydric alcohol.
Claim 3
Dependent Claim
37 words
A polyurethane composition according to claim 1 wherein said polyoxyalkylene polyamine is present in said polyether polyol in amounts from about 5 to about 15 equivalents of the polyoxyalkylene polyamine per 100 equivalents of said polyether polyol.
Claim 4
Dependent Claim
38 words
A polyurethane composition according to claim 2 wherein the polyoxyalkylene polyamine is a polyoxypropylene polyamine wherein Z is methyl, Y is hydrogen, X is Z, n is from 1 to 16 and m is from 2 to 4.
Claim 5
Dependent Claim
46 words
A polyurethane composition according to claim 3 wherein the polyoxypropylene polyamines are polyoxypropylene diamines of the formula ##STR4## wherein R is 1,2-propylene radical, m is 2, n is from about 2 to about 16 and A is hydrogen or cyano-lower-alkyl having 1 to 2 carbon atoms.
Claim 6
Dependent Claim
17 words
A polyurethane composition according to claim 4 wherein A is cyanoethyl and n is 2 to 16.
Claim 7
Dependent Claim
52 words
A polyurethane composition according to claim 3 wherein the polyoxypropylene polyamines are polyoxypropylene triamines of the formula ##STR5## wherein R is the nucleus of trimethylolpropane, m is 3, x, y and z independently are integers of from 1 to 10, with the sum of x+y+z being from about 3 to about 30.
Claim 8
Dependent Claim
23 words
A polyurethane composition according to claim 6 wherein A is cyanoethyl and the sum of x+y+z is from about 4.6 to about 9.8.
Claim 9
Dependent Claim
28 words
A polyurethane composition according to claim 2 wherein the organic polyisocyanate compound is a polymethylene polyphenyl polyisocyanate having an average functionality of from about 2.2 to about 2.8.
Claim 10
Dependent Claim
26 words
The polyurethane composition of claim 8 wherein said polyether polyol is a polyether polyol having an average molecular weight of from about 1,000 to about 7,000.
Claim 11
Dependent Claim
32 words
The polyurethane composition of claim 9 wherein said polyether polyol is a mixture of a polyether diol and a polyether triol having a molecular weight of from about 4,500 to about 6,500.
Claim 12
Dependent Claim
17 words
The polyurethane composition of claim 2 wherein the isocyanate index is from about 0.9 to about 1.4.
Claim 13
Dependent Claim
17 words
The polyurethane composition according to claim 4 wherein A is hydrogen and n is 2 to 16.
Claim 14
Dependent Claim
22 words
The polyurethane composition of claim 6 wherein A is hydrogen and the sum of x+y+z is from about 4.6 to about 9.8.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-09-07 | 1980-03-08 | 1980-09-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-09-07 | 1984-03-08 | 1984-09-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-09-07 | 1988-03-08 | 1988-09-07 | $7700.00 | Window Closed / Lapsed |