Aqueous base-soluble resin compositions
Assignee: Shanco Plastics and Chemicals Inc
•
Filing: 1973-07-30
•
Granted: 1976-09-07
•
Expires: 1993-07-30
Abstract
Abstract Polymerization products of carboxyl-free and carboxylsubstituted ethylenically unsaturated monomers have retained with the resin a reaction solvent mixture of high boiling alcohols, of which about 30 to 60% are normally liquid, waterinsoluble alcohols. These products are solid, hard glass-like resins which may be dissolved in aqueous bases to form clear or cloudy substantially colorless coating solutions useful in the preparation of clear or cloudy aqueous floor polishes which deposit clear protective films on treated floors.
Inventors
- 👤 John W. Brady
- 👤 Franklin D. Strickland
- 👤 Chester C. Longwith
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 17:14
CPC Classifications
C; C09; C09G; C09G1/00; C09G1/06; C09G1/14; C09G1/16; C08; C08F; C08F220/00; C08F220/02; C08F220/04; C08F220/06; C08F222/00; C08F246/00; C08K; C08K5/00; C08K5/04; C08K5/05; C08L; C08L33/00; C08L33/02; C09G1/08; C09G1/10; Y; Y10; Y10S; Y10S524/00; Y10S524/914
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
190 words
An aqueous base-soluble solid resin having an acid number of 120 to 185, which is the reaction product polymer of a reaction mix comprising about 20 to 70 mole percent of at least one carboxyl-free polymerizable ethylenically unsaturated monomer, about 15 to 60 mole percent of at least one carboxyl-substituted polymerizable ethylenically unsaturated monomer of the formula CH 2 =CR 2 COOH, wherein R 2 represents hydrogen or methyl, as a solvent for the reaction mixture, which is retained in the resin, a mixture of saturated alcohols of normal boiling points above about 175°C., which mixture contains about 30 to 60 weight percent of water insoluble liquid alcohol and about 40 to 70 weight percent of water soluble alcohol, the mole percentage of the solvent alcohols being about 10 to 20, and about 0.3 to 1 mole percent of an organic free radical-generating polymerization initiator, the number average molecular weight of the resin corresponding to about 600 to 4,000 at 10 mole percent content of solvent in the reaction mix, and the water insoluble alcohol having a boiling point above 175°C. being a source of such alcohol in the resin.
Claim 2
Dependent Claim
190 words
An aqueous base-soluble solid resin having an acid number of 120 to 185, which is the reaction product polymer of a reaction mix comprising about 20 to 70 mole percent of at least one carboxyl-free polymerizable ethylenically unsaturated monomer, about 15 to 60 mole percent of at least one carboxyl-substituted polymerizable ethylenically unsaturated monomer of the formula CH 2 =CR 2 COOH, wherein R 2 represents hydrogen or methyl, as a solvent for the reaction mixture, which is retained in the resin, a mixture of saturated alcohols of normal boiling points above about 175°C., which mixture contains about 30 to 60 weight percent of water insoluble liquid alcohol and about 40 to 70 weight percent of water soluble alcohol, the mole percentage of the solvent alcohols being about 10 to 20, and about 0.3 to 1 mole percent of an organic free radical-generating polymerization initiator, the number average molecular weight of the resin corresponding to about 600 to 4,000 at 10 mole percent content of solvent in the reaction mix, and the water insoluble alcohol having a boiling point above 175°C. being a source of such alcohol in the resin.
Claim 3
Dependent Claim
150 words
An aqueous base-soluble solid resin having an acid number of 120 to 185, which is a reaction product polymer of a reaction mix comprising about 20 to 70 mole percent of at least one carboxyl-free polymerizable ethylenically unsaturated monomer, about 15 to 60 mole percent of at least one carboxyl-substituted polymerizable ethylenically unsaturated monomer of the formula CH 2 =CR 2 COOH, wherein R 2 represents hydrogen or methyl, an effective polymerization initiating proportion of an organic free radical-generating polymerization initiator and, as a solvent for the reaction mixture, which is retained in the resin, about 5 to 10 mole percent of a water insoluble primary monohydric saturated aliphatic alcohol of 9 to 12 carbon atoms having a boiling point above 175°C., which solid resin has a number average molecular weight corresponding to about 600 to 4,000 at 10 mole percent content of such solvent alcohol in the reaction mix.
Claim 4
Dependent Claim
150 words
An aqueous base-soluble solid resin having an acid number of 120 to 185, which is a reaction product polymer of a reaction mix comprising about 20 to 70 mole percent of at least one carboxyl-free polymerizable ethylenically unsaturated monomer, about 15 to 60 mole percent of at least one carboxyl-substituted polymerizable ethylenically unsaturated monomer of the formula CH 2 =CR 2 COOH, wherein R 2 represents hydrogen or methyl, an effective polymerization initiating proportion of an organic free radical-generating polymerization initiator and, as a solvent for the reaction mixture, which is retained in the resin, about 5 to 10 mole percent of a water insoluble primary monohydric saturated aliphatic alcohol of 9 to 12 carbon atoms having a boiling point above 175°C., which solid resin has a number average molecular weight corresponding to about 600 to 4,000 at 10 mole percent content of such solvent alcohol in the reaction mix.
Claim 5
Dependent Claim
91 words
A resin according to claim 1 wherein the structural formula of the carboxyl-free monomer(s) is CH 2 =CR-Z wherein R represents hydrogen or methyl and Z represents a carboxy-lower alkoxy group or an aryl radical selected from the group consisting of phenyl and lower alkyl substituted phenyl, wherein the lower alkoxy and lower alkyl groups are of 1 to 4 carbon atoms with the proviso that when Z is aryl, R is hydrogen, and the alcohol(s) of the solvent is/are selected from the group consisting of monohydric alcohols, diols and triols.
Claim 6
Dependent Claim
91 words
A resin according to claim 3 wherein there is present as carboxyl-free monomers a mixture of compounds corresponding to the structural formula CH 2 =CR-Z, in one of said compounds Z being aryl and in remaining compound(s) being carbo-lower alkoxy, the alcohols of the solvent are saturated aliphatic alcohols and have normal boiling points above about 205°C. and there is present in the reaction mixture about 0.3 to 0.9 mole percent of initiator selected from the group consisting of aroyl peroxides and lower akyl esters of aliphatic and/or aromatic carboxylic peracids.
Claim 7
Dependent Claim
82 words
A resin according to claim 4 wherein there is present as the carboxy-free monomers a mixture of styrene and a lower akyl acrylate or methacrylate in a molar ratio of about 1.6:1 to 3:1, the molar ratio of carboxyl-free monomers to carboxyl-substituted monomers being in the range of about 1.2:1 to 2.7:1, the solvent contains 40 to 55 weight percent of water insoluble alcohol(s) and about 45 to 60 weight percent of water soluble alcohol(s) and the initiator is an aroyl peroxide.
Claim 8
Dependent Claim
57 words
A resin according to claim 5 wherein there is present as the carboxyl-free monomers a mixture of styrene and methyl methacrylate, the carboxyl-substituted monomer is methacrylic acid, the solvent consists essentially of about 50 weight percent of a water soluble alcohol and about 50 weight percent of a water insoluble alcohol and the initiator is benzoyl peroxide.
Claim 9
Dependent Claim
37 words
A resin according to claim 6 wherein the water soluble alcohol of the solvent is a diol and the water insoluble alcohol is a primary monohydric aliphatic alcohol or mixture thereof of 9 to 12 carbon atoms.
Claim 10
Dependent Claim
80 words
A resin according to claim 7 wherein the molar ratio of styrene to methyl methacrylate is about 2:1, the molar ratio of carboxyl-free monomer(s) to carboxyl-substituted monomer(s) is about 1.5:1, the water soluble diol is 2,2,4-trimethyl-1,3-pentane diol, the water insoluble monohydric primary alkanol is n-decyl alcohol, the mole percent of benzoyl peroxide in the mixture being about 0.3 and the resulting resin having an acid number of 120 to 185 and a number average molecular weight of 900 to 2,500.
Claim 11
Dependent Claim
55 words
A resin according to claim 2 wherein there is present with the monohydric alcohol of 9 to 12 carbon atoms a water soluble alcohol having a boiling point above 175°C. and the weight percentages of water insoluble alcohol and water soluble alcohol are 30 to 60 and 70 to 40, respectively, in the mixture thereof.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-09-07 | 1980-03-08 | 1980-09-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-09-07 | 1984-03-08 | 1984-09-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-09-07 | 1988-03-08 | 1988-09-07 | $7700.00 | Window Closed / Lapsed |