Metal recovery method
Assignee: Individual
•
Filing: 1974-06-19
•
Granted: 1976-09-07
•
Expires: 1994-06-19
Abstract
Abstract The present invention is a method of treating sea or land carbonaceous ore or reconstituted, formerly carbonaceous ore to recover therefrom noble metal values. If sea ore is used, noble metal containing composite organic material is first separated from any shells or sand that may be present. Flotation techniques are then utilized to form a carbonaceous concentrate, which is next mixed with a strong oxidizing agent. The mixture may either be heated to provide autogenously ignition or ignition may alternatively be accomplished by compounding the mixture into electrodes and using electric arc. If stoichiometric quantities of the oxidizing agent are used, the oxidation-reduction reaction, which consumes all carbon present, is of sufficient energy to drive the noble metals and/or their compounds into the vapor phase forming a particulate plasma, from which the elemental metals or their compounds may be condensed and/or precipitated. If non-stoichiometric quantities of oxidant are used, recovery of the sought metals may be had from the ash by techniques well known to those skilled in the art.
Inventors
- 👤 Fritz W. Wanzenberg
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 06:59
CPC Classifications
C; C22; C22B; C22B3/00; C22B1/00; C22B11/00; C22B4/00; C22B5/00; C22B5/02; C22B5/16; Y; Y02; Y02P; Y02P10/00; Y02P10/20
Claims Analysis
Total Claims: 41
Claim 1
Independent Claim
189 words
A method of treating noble metal containing sea carbonaceous ore having therein noble metal containing composite organic materials and gangue fractions, including sand and shells, to produce therefrom elemental noble metals, noble metal oxides and other noble metal compounds, said method comprising: stripping said noble metal containing composite organic materials, having therein naturally occurring carbonaceous reducing agent components, from said gangue fractions to form a carbonaceous concentrate; treating said noble metal containing composite organic materials with a strong oxidizing agent in amounts substantially stoichiometrically balanced with said carbonaceous reducing agent components of said composite organic materials; heating said treated composite materials until said materials autogeneously ignite; allowing complete combustion of said carbonaceous reducing agent components and said strong oxidizing agent in said treated composite materials, whereby the energy released by said autogeneous ignition is sufficient to drive all said noble elemental metals, noble metal oxides and other noble metal compounds into the vapor phase to produce thereby a particulate plasma with solid non-combustible residues remaining in the form of an ash; and recovering from the vapor phase said noble elemental metals, noble metal oxides and other noble metal compounds.
Claim 2
Independent Claim
189 words
A method of treating noble metal containing sea carbonaceous ore having therein noble metal containing composite organic materials and gangue fractions, including sand and shells, to produce therefrom elemental noble metals, noble metal oxides and other noble metal compounds, said method comprising: stripping said noble metal containing composite organic materials, having therein naturally occurring carbonaceous reducing agent components, from said gangue fractions to form a carbonaceous concentrate; treating said noble metal containing composite organic materials with a strong oxidizing agent in amounts substantially stoichiometrically balanced with said carbonaceous reducing agent components of said composite organic materials; heating said treated composite materials until said materials autogeneously ignite; allowing complete combustion of said carbonaceous reducing agent components and said strong oxidizing agent in said treated composite materials, whereby the energy released by said autogeneous ignition is sufficient to drive all said noble elemental metals, noble metal oxides and other noble metal compounds into the vapor phase to produce thereby a particulate plasma with solid non-combustible residues remaining in the form of an ash; and recovering from the vapor phase said noble elemental metals, noble metal oxides and other noble metal compounds.
Claim 3
Dependent Claim
23 words
The method claimed in claim 1 wherein said noble metal containing composite organic materials are separated from said gangue fractions by mechanical scrubbing.
Claim 4
Dependent Claim
22 words
The method claimed in claim 1 wherein said noble metal containing composite organic materials are separated from said gangue fractions by flotation.
Claim 5
Dependent Claim
39 words
The method claimed in claim 1 wherein said carbonaceous concentrate is treated with a wetting agent prior to heating, whereby the intimacy of said strong oxidizing agent with said carbonaceous cooncentrate is increased to provide a more efficient combustion.
Claim 6
Dependent Claim
40 words
The method claimed in claim 1 wherein said carbonaceous concentrate is placed under greater than atmospheric pressure prior to heating, whereby the intimacy of said strong oxidizing agent with said carbonaceous concentrate is increased to provide a more efficient combustion.
Claim 7
Dependent Claim
42 words
The method as claimed in claim 1 wherein said recovery is carried out by means of fractional condensation whereby said noble elemental metals, noble metal oxides, and other noble metal compounds are sequentially recovered in approximate declining order of their transition temperatures.
Claim 8
Dependent Claim
20 words
The method as claimed in claim 6 wherein said recovery by fractional condensation is carried out by means of scrubbers.
Claim 9
Dependent Claim
21 words
The method as claimed in claim 6 wherein said recovery by fractional condensation is carried out by means of electrostatic precipitors.
Claim 10
Dependent Claim
20 words
The method as claimed in claim 6 wherein said recovery by fractional condensation is carried out by means of cyclones.
Claim 11
Dependent Claim
23 words
The method as claimed in claim 1 further comprising collecting said solid noncombustible residues remaining from said combustion and recovering therefrom refractory metals.
Claim 12
Dependent Claim
15 words
The method claimed in claim 1 wherein said strong oxidizing agent is an inorganic chlorate.
Claim 13
Dependent Claim
14 words
The method as claimed in claim 11 wherein said inorganic chlorate comprises perchloryl fluoride.
Claim 14
Dependent Claim
15 words
The method claimed in claim 1 wherein said strong oxidizing agent is an inorganic perchlorate.
Claim 15
Dependent Claim
15 words
The method claimed in claim 1 wherein said strong oxidizing agent is an inorganic nitrate.
Claim 16
Dependent Claim
23 words
The method as claimed in claim 1 wherein said strong oxidizing agent is selected from the group consisting of: oxygen, ozone and fluorine.
Claim 17
Dependent Claim
54 words
The method as claimed in claim 1 further comprising, adding prior to said combustion a reducing agent, at least a portion of which is in the form of a high initial flash point liquid hydrocarbon, wherein said reducing agent serves to augment said naturally occurring carbonaceous reducing agent components of said composite organic materials.
Claim 18
Dependent Claim
24 words
The method as claimed in claim 1 further comprising providing an oxygen atmosphere to said treated composite organic materials prior to said autogeneous ignition.
Claim 19
Dependent Claim
23 words
The method as claimed in claim 1 further comprising grinding said composite organic materials to approximately 100 mesh prior to said autogeneous ignition.
Claim 20
Dependent Claim
17 words
The method as claimed in claim 1 wherein said strong oxidizing agent is produced autogeneously by electrolysis.
Claim 21
Dependent Claim
28 words
The method as claimed in claim 1 further comprising treating said sea carbonaceous ore with chlorine, whereby said separation of composite organic materials from said gangue is enhanced.
Claim 22
Dependent Claim
33 words
The method as claimed in claim 20 further comprising treating said sea carbonaceous ore with an hydroxide together with said chlorine and heating, whereby said strong oxidizing agent is produced in hot solution.
Claim 23
Dependent Claim
33 words
The method as claimed in claim 1 further comprising providing gaseous hydrogen to said treated composite materials prior to ignition thereof to react with chlorine or fluorine gas present or produced during combustion.
Claim 24
Dependent Claim
46 words
The method as claimed in claim 22 wherein said provided gaseous hydrogen is contained in an encapsulating foam substance, whereby said hydrogen may react with said carbonaceous solids in a stoichiometric solid-gas reaction to drive said noble metals and noble metal compounds into the vapor phase.
Claim 25
Dependent Claim
31 words
The method as claimed in claim 1 wherein said strong oxidizing agent is selected from the group consisting of: an inorganic chlorate, an inorganic perchlorate, an inorganic hypochlorite, and a permanganate.
Claim 26
Independent Claim
195 words
A method of treating noble metal containing land carbonaceous or having therein noble metal containing composite organic materials including naturally occurring carbonaceous reducing agent components to produce therefrom elemental noble metals, noble metal oxides and other noble metal compounds, said method comprising: crushing said mined noble metal containing land carbonaceous ore to produce ore particles; fracturing along mineralized boundaries of said ore particles to remove magnetite from said crushed land carbonaceous ore; floating said crushed, demagnetized land carbonaceous ore; treating said noble metal containing composite organic materials with a strong oxidizing agent, said oxidizing in amounts substantially stoichiometrically balanced with said carbonaceous reducing agent components of said composite organic materials; heating said treated composite materials until said materials autogenously ignite; allowing complete combustion of said carbonaceous reducing agent components and said strong oxidizing agent in said treated composite materials, whereby the energy released by said autogenous ignition is sufficient to drive all said noble metal compounds into the vapor phase to produce thereby a particulate plasma with solid non-combustible residues remaining in the form of an ash; and recovering from the vapor phase said noble elemental metals, noble metal oxides and other noble metal compounds.
Claim 27
Independent Claim
195 words
A method of treating noble metal containing land carbonaceous or having therein noble metal containing composite organic materials including naturally occurring carbonaceous reducing agent components to produce therefrom elemental noble metals, noble metal oxides and other noble metal compounds, said method comprising: crushing said mined noble metal containing land carbonaceous ore to produce ore particles; fracturing along mineralized boundaries of said ore particles to remove magnetite from said crushed land carbonaceous ore; floating said crushed, demagnetized land carbonaceous ore; treating said noble metal containing composite organic materials with a strong oxidizing agent, said oxidizing in amounts substantially stoichiometrically balanced with said carbonaceous reducing agent components of said composite organic materials; heating said treated composite materials until said materials autogenously ignite; allowing complete combustion of said carbonaceous reducing agent components and said strong oxidizing agent in said treated composite materials, whereby the energy released by said autogenous ignition is sufficient to drive all said noble metal compounds into the vapor phase to produce thereby a particulate plasma with solid non-combustible residues remaining in the form of an ash; and recovering from the vapor phase said noble elemental metals, noble metal oxides and other noble metal compounds.
Claim 28
Independent Claim
219 words
A method of treating noble metal containing noncarbonaceous land ore having therein noble metal containing composite organic materials, but substantially lacking in carbonaceous reducing agent components to produce therefrom noble elemental metals, noble metal oxides and other noble metal compounds, said method comprising: crushing said noncarbonaceous land ore to produce ore particles; fracturing along mineralized boundaries of said ore particles to remove magnetite from said crushed noncarbonaceous land ore; adding a reducing agent to establish a reducing agent content sufficient to permit an autogenous oxidation-reduction reaction of a temperature above the transition temperature of said noble elemental metals, noble metal oxides and other noble metal compounds sought to be recovered; treating said noble metal containing composite organic materials with a strong oxidizing agent in amounts substantially stoichiometrically balanced with said added reducing agent; heating said treated composite materials until said materials autogenously ignite; allowing complete combustion of said added reducing agent and said oxidizing agent, whereby the energy released by said autogenous ignition is sufficient to drive all said noble elemental metals, noble metal oxides and other noble metal compounds into the vapor phase to produce thereby a particulate plasma with solid noncombustible residues remaining in the form of an ash; and recovering from the vapor phase said noble elemental metals, noble metal oxides and other noble metal compounds.
Claim 29
Independent Claim
219 words
A method of treating noble metal containing noncarbonaceous land ore having therein noble metal containing composite organic materials, but substantially lacking in carbonaceous reducing agent components to produce therefrom noble elemental metals, noble metal oxides and other noble metal compounds, said method comprising: crushing said noncarbonaceous land ore to produce ore particles; fracturing along mineralized boundaries of said ore particles to remove magnetite from said crushed noncarbonaceous land ore; adding a reducing agent to establish a reducing agent content sufficient to permit an autogenous oxidation-reduction reaction of a temperature above the transition temperature of said noble elemental metals, noble metal oxides and other noble metal compounds sought to be recovered; treating said noble metal containing composite organic materials with a strong oxidizing agent in amounts substantially stoichiometrically balanced with said added reducing agent; heating said treated composite materials until said materials autogenously ignite; allowing complete combustion of said added reducing agent and said oxidizing agent, whereby the energy released by said autogenous ignition is sufficient to drive all said noble elemental metals, noble metal oxides and other noble metal compounds into the vapor phase to produce thereby a particulate plasma with solid noncombustible residues remaining in the form of an ash; and recovering from the vapor phase said noble elemental metals, noble metal oxides and other noble metal compounds.
Claim 30
Dependent Claim
16 words
The method as claimed in claim 26 wherein said added reducing agent comprises a carbonaceous substance.
Claim 31
Independent Claim
118 words
A method of treating ores comprised of metal-containing composite organic materials and associated inorganic materials to produce therefrom elemental metals and other metal compounds, said method comprising: separating said composite organic materials from said associated inorganic materials by applying ultrasonic energy to water in which said ores are immersed to bring about separation of said composite organic materials from said inorganic materials. treating said composite materials with a predetermined amount of an oxidizing agent to produce a treated composite material; igniting said materials and allowing substantially complete combustion thereof; and collecting the solid combustion residues of said materials for subsequent reduction of a portion thereof to the elemental metals which formed the metal component of said composite materials.
Claim 32
Independent Claim
118 words
A method of treating ores comprised of metal-containing composite organic materials and associated inorganic materials to produce therefrom elemental metals and other metal compounds, said method comprising: separating said composite organic materials from said associated inorganic materials by applying ultrasonic energy to water in which said ores are immersed to bring about separation of said composite organic materials from said inorganic materials. treating said composite materials with a predetermined amount of an oxidizing agent to produce a treated composite material; igniting said materials and allowing substantially complete combustion thereof; and collecting the solid combustion residues of said materials for subsequent reduction of a portion thereof to the elemental metals which formed the metal component of said composite materials.
Claim 33
Independent Claim
143 words
A method of treating noble metal-containing, composite organic materials to produce therefrom elemental noble metals, noble metal oxides and other noble metal compounds, said method comprising: treating a mass of said composite materials with a water-immiscible, volatile organic cleaning agent; removing at least a major portion of said cleaning agent after said materials and said cleaning agent have been in contact with each other; treating said composite materials with a strong oxidizing agent; heating said treated composite materials to at least 200°C to remove substantially all of said oxidizing agent remaining after treatment of said materials; continuing to heat said materials at at least about 200°C until said materials spontaneously ignite; allowing complete combustion of said materials; and collecting the solid combustion residues of said materials for subsequent reduction to the noble metals which formed the noble metal component of said composite materials.
Claim 34
Independent Claim
143 words
A method of treating noble metal-containing, composite organic materials to produce therefrom elemental noble metals, noble metal oxides and other noble metal compounds, said method comprising: treating a mass of said composite materials with a water-immiscible, volatile organic cleaning agent; removing at least a major portion of said cleaning agent after said materials and said cleaning agent have been in contact with each other; treating said composite materials with a strong oxidizing agent; heating said treated composite materials to at least 200°C to remove substantially all of said oxidizing agent remaining after treatment of said materials; continuing to heat said materials at at least about 200°C until said materials spontaneously ignite; allowing complete combustion of said materials; and collecting the solid combustion residues of said materials for subsequent reduction to the noble metals which formed the noble metal component of said composite materials.
Claim 35
Independent Claim
219 words
A method of recovering and treating noble metal-containing, composite organic materials to produce therefrom elemental metals and other metal compounds, said method comprising: separating said composite organic materials from whole ores by flotation of said composite organic materials atop a mass of water; treating said composite materials with a water-immiscible, volatile organic solvent while said materials are atop said mass of water to clean associated inorganic materials from said organic composite material for density difference separation of said inorganic materials after removal thereof; removing said cleaned organic composite materials and said solvent, after solvent treatment of said composite materials, to remove a major portion of said solvent from said composite materials while allowing a substantial portion of any water associated with said composite materials to remain associated therewith; treating said composite materials with an aqueous solution of a strong oxidizing agent; heating said thus treated composite materials to a temperature of from about 200°C to about 250°C to remove therefrom substantially all of said oxidizing agent remaining after treatment of said materials; continuing to heat said materials at said 200°C to 250°C until said materials spontaneously ignite; allowing complete combustion of said materials; and collecting the solid combustion residues of said materials for subsequent reduction to the noble metals which formed the noble metal component of said composite materials.
Claim 36
Independent Claim
219 words
A method of recovering and treating noble metal-containing, composite organic materials to produce therefrom elemental metals and other metal compounds, said method comprising: separating said composite organic materials from whole ores by flotation of said composite organic materials atop a mass of water; treating said composite materials with a water-immiscible, volatile organic solvent while said materials are atop said mass of water to clean associated inorganic materials from said organic composite material for density difference separation of said inorganic materials after removal thereof; removing said cleaned organic composite materials and said solvent, after solvent treatment of said composite materials, to remove a major portion of said solvent from said composite materials while allowing a substantial portion of any water associated with said composite materials to remain associated therewith; treating said composite materials with an aqueous solution of a strong oxidizing agent; heating said thus treated composite materials to a temperature of from about 200°C to about 250°C to remove therefrom substantially all of said oxidizing agent remaining after treatment of said materials; continuing to heat said materials at said 200°C to 250°C until said materials spontaneously ignite; allowing complete combustion of said materials; and collecting the solid combustion residues of said materials for subsequent reduction to the noble metals which formed the noble metal component of said composite materials.
Claim 37
Dependent Claim
37 words
A method as defined in claim 30 which further includes, prior to separation of said organic composite material from said whole ores, treating an aqueous mixture of said whole ores with a minor proportion of hydrochloric acid.
Claim 38
Independent Claim
203 words
A method of treating noble metal containing sea carbonaceous ore having therein noble metal containing composite organic materials and gangue fractions, including sand and shells to produce therefrom elemental noble metals, noble metal oxides and other noble metal compounds, said method comprising: stripping said noble metal containing composite organic materials having therein naturally occurring carbonaceous reducing agent components from said gangue fractions to form a carbonaceous concentrate; treating said noble metal containing composite organic materials with a strong oxidizing agent in amounts substantially stoichiometrically balanced with said carbonaceous reducing agent components of said composite organic materials; adding graphite to said so treated noble metal containing composite organic materials in an amount sufficient to conduct electricity and substantiallly agitating sufficient to form a mixture; forming electrodes from said graphite and composite organic materials mixture; igniting said electrodes autogeneously by electric arc, wherein the energy released by said autogenous ignition is sufficient to drive all said noble elemental metals, noble metal oxides and other noble metal compounds into the vapor phase to produce thereby a particulate plasma with solid noncombustible residues remaining in the form of an ash; and recovering from the vapor phase said noble elemental metals, noble metal oxides and other noble compounds.
Claim 39
Independent Claim
203 words
A method of treating noble metal containing sea carbonaceous ore having therein noble metal containing composite organic materials and gangue fractions, including sand and shells to produce therefrom elemental noble metals, noble metal oxides and other noble metal compounds, said method comprising: stripping said noble metal containing composite organic materials having therein naturally occurring carbonaceous reducing agent components from said gangue fractions to form a carbonaceous concentrate; treating said noble metal containing composite organic materials with a strong oxidizing agent in amounts substantially stoichiometrically balanced with said carbonaceous reducing agent components of said composite organic materials; adding graphite to said so treated noble metal containing composite organic materials in an amount sufficient to conduct electricity and substantiallly agitating sufficient to form a mixture; forming electrodes from said graphite and composite organic materials mixture; igniting said electrodes autogeneously by electric arc, wherein the energy released by said autogenous ignition is sufficient to drive all said noble elemental metals, noble metal oxides and other noble metal compounds into the vapor phase to produce thereby a particulate plasma with solid noncombustible residues remaining in the form of an ash; and recovering from the vapor phase said noble elemental metals, noble metal oxides and other noble compounds.
Claim 40
Dependent Claim
47 words
The method claimed in claim 32 further comprising placing said graphite-composite mixture electrodes in an oxygen atmosphere prior thereof said autogenous ignition t hereof by said electric arc, whereby ozone is created to produce very high energy particulate plasma levels thereby to oxidize entirely said composite material.
Claim 41
Dependent Claim
20 words
The method as claimed in claim 32 wherein said vapor phase is collected in a reducing atmosphere immediately following vaporization.
References Cited (Backward Citations)
US3819363A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-09-07 | 1980-03-08 | 1980-09-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-09-07 | 1984-03-08 | 1984-09-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-09-07 | 1988-03-08 | 1988-09-07 | $7700.00 | Window Closed / Lapsed |