Finishing of cellulose fabrics with N-methylol amide crosslinking agents, magnesium sulfate and sulfuric acid

Claim 2

In a process of finishing cellulose-containing fabrics to impart durable press properties by treatment with aqueous formulations containing N-methylol amide crosslinking agents, crosslinking catalysts, and, other compatible additives or agents to enhance properties other than durable press or strengh properties, the improvement consisting of: a. adding to aqueous formulations as the sole crosslinking catalyst, a mixture of sulfuric acid and magnesium sulfate in amounts such that for every 100 parts by weight of said formulation there are about from 5 to 20 parts by weight N-methylol amide crosslinking agent, about from 0.2 to 2 parts by weight of sulfuric acid, and about from 0.3 to 2.5 parts by weight of magnesium sulfate; b. impregnating a cellulose-containing textile with the formulation from a; and Serial No. 513,361 c. curing the wet, impregnated textile by heat treatment at from about 60°C to about 100°C for about from 2 minutes to about 8 minutes to obtain a moisture content in the treated textile of about 2 to 5%; and d. washing and drying the textile.

Claim 3

In a process of finishing cellulose-containing fabrics to impart durable press properties by treatment with aqueous formulations containing an N-methylol amide crosslinking agent selected from the group consisting of dimethylol dihydroxyethyleneurea and dimethylol methyl carbamate, crosslinking catalysts, and, other compatible additives or agents to enhance properties other than durable press or strength properties, the improvement consisting of: a. adding to aqueous formulations as the sole crosslinking catalyst a mixture of sulfuric acid and magnesium sulfate in amounts such that for every 100 parts by weight of said formulation there are about from 9 to 15 parts by weight of the N-methylol amide crosslinking agent, about from 0.5 to 1.5 parts by weight sulfuric acid, and about from 0.6 to 1.8 parts by weight of magnesium sulfate; b. impregnating the cellulose-containing textile with said formulation; c. curing the wet, impregnated textile by heat treatment at from about 60°C to about 100°C for about from 2 minutes to about 8 minutes to obtain a moisture content in the treated textile of about 2 to 5%; and d. washing and drying the textile.

Claim 4

In a process of finishing cellulose-containing fabrics to impart durable press properties by treatment with aqueous formulations containing an N-methylol amide crosslinking agent selected from the group consisting of dimethylol dihydroxyethyleneurea and dimethylol methyl carbamate, crosslinking catalysts, and, other compatible additives or agents to enhance properties other than durable press or strength properties, the improvement consisting of: a. adding to aqueous formulations as the sole crosslinking catalyst a mixture of sulfuric acid and magnesium sulfate in amounts such that for every 100 parts by weight of said formulation there are about from 9 to 15 parts by weight of the N-methylol amide crosslinking agent, about from 0.5 to 1.5 parts by weight sulfuric acid, and about from 0.6 to 1.8 parts by weight of magnesium sulfate; b. impregnating the cellulose-containing textile with said formulation; c. curing the wet, impregnated textile by heat treatment at from about 60°C to about 100°C for about from 2 minutes to about 8 minutes to obtain a moisture content in the treated textile of about 2 to 5%; and d. washing and drying the textile.

Claim 5

The process of claim 2 wherein the N-methylol amide crosslinking agent is dimethylol dihydroxyethyleneurea.

Claim 6

The process of claim 2 wherein the N-methylol amide crosslinking agent is dimethylol methyl carbamate.