Metal/air cells and improved air electrodes for use therein
Assignee: Westinghouse Electric Corp
•
Filing: 1974-10-23
•
Granted: 1976-08-31
•
Expires: 1994-10-23
Abstract
Abstract Air electrodes for use in electrochemical energy cells which comprise a hydrophilic layer and a hydrophobic layer laminated thereto. The hydrophilic layer essentially comprises a hydrophilic composite which includes I. an oxygen absorption/reduction carbon, Ii. a material selected from the group consisting of A. CuWO 4 , NiWO 4 , CoWO 4 and WC with 1-20 wt. % Co. for a unifunctional electrode, or B. WS 2 , WC, and WC with 1-20 Wt.% Co. for a bi-functional electrode, and Iii. a nonwetting agent containing a polytetrafluoroethylene. A metal current collector is molded into the composite to form a substantially flat hydrophilic layer. A catalyst is preferably incorporated into the composite of a bifunctional electrode to increase cycling life. The hydrophobic layer, comprising a sheet of porous fluorinated ethylene propylene, polypropylene or polytetrafluoroethylene, is laminated to the hydrophilic layer to complete the air electrodes of the invention.
Inventors
- 👤 Edward S. Buzzelli
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 20:06
CPC Classifications
H; H01; H01M; H01M4/00; H01M4/86; H01M4/96; H01M4/8605; H01M4/8615; Y; Y02; Y02E; Y02E60/00; Y02E60/30; Y02E60/50
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
153 words
An air electrode for use in electrochemical energy cells comprising: A. a hydrophilic layer consisting essentially of 1. a hydrophilic composite comprising i. about 1 part by weight of oxygen absorption/reduction carbon particles having a total surface area of from about 30 to about 600 sq. meters/gram; ii. about 0.5-4 parts by weight of a low oxygen overvoltage material selected from the group consisting of CuWO 4 , NiWO 4 CoWO 4 , WS 2 , WC and WC fuse sinter coated with 1-20 wt.% Co and mixtures thereof; iii. an effective amount of a bonding/nonwetting agent including at least polytetrafluoroethylene; and iv. an effective amount of a catalyst for oxygen reduction and decomposition of perhydroxides selected from the group consisting of silver, platinum and silver mercury alloy; and 2. a metal current collector molded into said composite to form a hydrophilic layer; and B. a hydrophobic layer laminated to said hydrophilic layer.
Claim 2
Dependent Claim
153 words
An air electrode for use in electrochemical energy cells comprising: A. a hydrophilic layer consisting essentially of 1. a hydrophilic composite comprising i. about 1 part by weight of oxygen absorption/reduction carbon particles having a total surface area of from about 30 to about 600 sq. meters/gram; ii. about 0.5-4 parts by weight of a low oxygen overvoltage material selected from the group consisting of CuWO 4 , NiWO 4 CoWO 4 , WS 2 , WC and WC fuse sinter coated with 1-20 wt.% Co and mixtures thereof; iii. an effective amount of a bonding/nonwetting agent including at least polytetrafluoroethylene; and iv. an effective amount of a catalyst for oxygen reduction and decomposition of perhydroxides selected from the group consisting of silver, platinum and silver mercury alloy; and 2. a metal current collector molded into said composite to form a hydrophilic layer; and B. a hydrophobic layer laminated to said hydrophilic layer.
Claim 3
Dependent Claim
19 words
An electrode as set forth in claim 1 wherein iv. the current collector is a metal fiber current collector.
Claim 4
Dependent Claim
58 words
An electrode as set forth in claim 1 wherein said hydrophobic layer conprises a sheet of porous, plastic selected from the group consisting of polytetrafluoroethylene, polypropylene, fluorinated ethylene propylene and mixtures thereof and the low oxygen overvoltage material is selected from the group consisting of WS 2 , WC and WC fuse sinter coated with 1-20 wt.% Co.
Claim 5
Dependent Claim
20 words
An electrode as set forth in claim 1 wherein said hydrophilic composite is substantially flat and the catalyst is silver.
Claim 6
Dependent Claim
47 words
A metal/air cell comprising a metal electrode selected from the group consisting of iron, zinc, and cadmium; at least one air electrode as set forth in claim 1 spaced apart from said metal electrode; and an alkali hydroxide electrolyte in contact with said metal and air electrode.
Claim 7
Dependent Claim
169 words
An air electrode for use in electrochemical energy cells capable of non destructive charging comprising: A. a hydrophilic layer consisting essentially of 1. a hydrophilic composite comprising i. about 1 part by weight of substantially discrete oxygen absorption/reduction carbon black particles having a particle size range of between about 0.005-0.13 microns and a total probable surface area of from about 30-600 sq. meters/gram.; ii. about 0.5-4 parts by weight of low oxygen over voltage material selected from the group consisting of CuWO 4 , NiWO 4 , CoWO 4 , WS 2 , WC and WC fuse sinter coated with 1-20 wt.% Co. and mixtures thereof; iii. an effective amount of bonding/nonwetting agent including at least polytetrafluoroethylene; and iv. an effective amount of a catalyst for oxygen reduction and decomposition of perhydroxides selected from the group consisting of silver, platinum and silver mercury alloy; and 2. a metal current collector molded into said composite to form a hydrophilic layer; and B. a hydrophobic layer laminated to said hydrophilic layer.
Claim 8
Dependent Claim
169 words
An air electrode for use in electrochemical energy cells capable of non destructive charging comprising: A. a hydrophilic layer consisting essentially of 1. a hydrophilic composite comprising i. about 1 part by weight of substantially discrete oxygen absorption/reduction carbon black particles having a particle size range of between about 0.005-0.13 microns and a total probable surface area of from about 30-600 sq. meters/gram.; ii. about 0.5-4 parts by weight of low oxygen over voltage material selected from the group consisting of CuWO 4 , NiWO 4 , CoWO 4 , WS 2 , WC and WC fuse sinter coated with 1-20 wt.% Co. and mixtures thereof; iii. an effective amount of bonding/nonwetting agent including at least polytetrafluoroethylene; and iv. an effective amount of a catalyst for oxygen reduction and decomposition of perhydroxides selected from the group consisting of silver, platinum and silver mercury alloy; and 2. a metal current collector molded into said composite to form a hydrophilic layer; and B. a hydrophobic layer laminated to said hydrophilic layer.
Claim 9
Dependent Claim
35 words
An air electrode as set forth in claim 6 wherein said oxygen absorption/reduction carbon black has an interlayer spacing between about 7.0 to 7.2A and the particles have a pore diameter between about 0.005-0.002 microns.
Claim 10
Dependent Claim
64 words
An air electrode as set forth in claim 6 wherein said oxygen absorption/reduction carbon consists essentially of an acetylene black having a total surface area of between about 30-450 sq. meters/gram, and is in a form wherein generally spherical particles are separated from each other and joined together in a three dimensional fashion by carbon-oxygen complexes which provide links between the separated carbon particles.
Claim 11
Dependent Claim
45 words
An air electrode as set forth in claim 6 wherein the current collector is a metal fiber current collector and the low oxygen overvoltage material is selected from the group consisting of WS 2 , WC and WC fuse sinter coated with 1-20 wt.% Co.
Claim 12
Dependent Claim
33 words
An air electrode as set forth in claim 7 wherein said hydrophobic layer comprises a sheet of porous, plastic selected from the group consisting of polytetrafluoroethylene, polypropylene, fluorinated ethylene propylene and mixtures thereof.
Claim 13
Dependent Claim
24 words
An air electrode as set forth in claim 9 wherein said hydrophilic composite is substantially flat and includes 0.15-1.5 parts by weight of catalyst.
Claim 14
Dependent Claim
47 words
A metal/air cell comprising a metal electrode selected from the group consisting of iron, zinc, and cadmium; at least one air electrode as set forth in claim 9 spaced apart from said metal electrode; and an alkali hydroxide electrolyte in contact with said metal and air electrode.
Claim 15
Dependent Claim
140 words
A metal/air battery comprising a metal electrode selected from the group consisting of iron, zinc and cadmium; at least one electrode, effective to allow non destructive battery charging at between about 0.50-0.75 volts above a Hg/HgO reference electrode, spaced apart from said metal electrode, the electrode comprising: A. a hydrophilic layer consisting essentially of 1. a hydrophilic composite comprising i. acetylene black carbon; ii. a low oxygen over voltage material selected from the group consisting of CuWO 4 , NiWO 4 , CoWO 4 , WS 2 , WC and WC fuse sinter coated with 1-20 wt.% Co. and mixtures thereof; iii. an effective amount of bonding/non-wetting agent including at least polytetrafluoroethylene; and iv. an effective amount of a catalyst for oxygen reduction and decomposition of perhydroxides selected from the group consisting of silver, platinum and silver mercury alloy; and
Claim 16
Dependent Claim
140 words
A metal/air battery comprising a metal electrode selected from the group consisting of iron, zinc and cadmium; at least one electrode, effective to allow non destructive battery charging at between about 0.50-0.75 volts above a Hg/HgO reference electrode, spaced apart from said metal electrode, the electrode comprising: A. a hydrophilic layer consisting essentially of 1. a hydrophilic composite comprising i. acetylene black carbon; ii. a low oxygen over voltage material selected from the group consisting of CuWO 4 , NiWO 4 , CoWO 4 , WS 2 , WC and WC fuse sinter coated with 1-20 wt.% Co. and mixtures thereof; iii. an effective amount of bonding/non-wetting agent including at least polytetrafluoroethylene; and iv. an effective amount of a catalyst for oxygen reduction and decomposition of perhydroxides selected from the group consisting of silver, platinum and silver mercury alloy; and
Claim 17
Dependent Claim
44 words
A metal current collector molded into said composite to form a substantially flat hydrophilic layer; and B. a hydrophobic layer laminated to said hydrophilic layer; and an alkali hydroxide electrolyte in contact with said metal electrode and the hydrophilic layer of said air electrode.
Claim 18
Dependent Claim
44 words
A metal current collector molded into said composite to form a substantially flat hydrophilic layer; and B. a hydrophobic layer laminated to said hydrophilic layer; and an alkali hydroxide electrolyte in contact with said metal electrode and the hydrophilic layer of said air electrode.
Claim 19
Dependent Claim
110 words
The metal/air battery as set forth in claim 13 wherein said hydrophilic composite includes about 0.5-4 parts by weight low oxygen overvoltage material for each part carbon, (iv) 0.15-1.5 parts by weight of catalyst, the acetylene black carbon is in a form wherein generally spherical particles are separated from each other and joined together in a three dimensional fashion by carbon-oxygen complexes which provide links between the separated carbon particles, said acetylene black carbon having a particle size range of between about 0.005-0.13 microns and a total surface area from about 30-300 sq. meters/gram and the low oxygen over voltage material is WC fuse sinter coated with 10-15 wt.% Co.
Claim 20
Dependent Claim
35 words
The metal/air battery as set forth in claim 13 wherein the low oxygen overvoltage material is selected from the group consisting of WS 2 , WC and WC fuse sintered coated with 1-20 wt.% Co.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-08-31 | 1980-03-01 | 1980-08-31 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-08-31 | 1984-03-01 | 1984-08-31 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-08-31 | 1988-03-01 | 1988-08-31 | $7700.00 | Window Closed / Lapsed |