Activation of surfaces intended for electroless plating
Assignee: MacDermid Enthone Inc
•
Filing: 1975-01-08
•
Granted: 1976-08-24
•
Expires: 1995-01-08
Abstract
Abstract Surfaces intended to be electrolessly metal plated, for instance the surfaces of through holes on through hole printed circuit boards, are treated with a colloidal catalyst metal-free acid liquid solution of a soluble, lower alkanol-modified noble metal-tin chloride complex until the surface is rendered catalytic. The noble metal of the complex is a noble metal which is catalytic to the deposition of the metal destined to be electrolessly plated on the surface.
Inventors
- 👤 Earl J. Fadgen, Jr.
- 👤 Juan Hajdu
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 21:18
CPC Classifications
C; C23; C23C; C23C18/00; C23C18/16; C23C18/18; C23C18/20; C23C18/28
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
227 words
A process for the electroless metal plating of a surface which comprises contacting an object surface intended to be electrolessly metal plated with a substantially colloidal metal particle-free acid liquid solution of a soluble lower alkanol-modified noble metal-tin chloride complex until the surface is rendered catalytic, the noble metal of the complex being a noble metal catalytic to the chemical reduction deposition of the metal desired to be plated on said surface, and electrolessly plating the metal on the thus-obtained catalytic surface by contacting the catalytic surface with a chemical reduction metal plating bath, the soluble lower alkanol-modified noble metal-tin chloride complex being obtained by mixing together a lower alkanol, a soluble noble metal chloride, stannous chloride, and hydrochloric acid, and maintaining the thus-obtained liquid mixture at a reaction temperature of at least about 160°F. but below that temperature at which an excessive amount of noble metal is precipitated for a period sufficient to obtain a catalytically effective solution containing the soluble lower alkanol-modified noble metal-tin chloride complex, the stannous chloride being present in excess of the amount thereof required to reduce the noble metal chloride to zero valent noble metal, the molar ratio of stannous chloride to the noble metal chloride (calculated as palladium chloride) being initially at least about 9-10:1 respectively, and the lower alkanol being present in amount sufficient to obtain a soluble complex.
Claim 2
Dependent Claim
227 words
A process for the electroless metal plating of a surface which comprises contacting an object surface intended to be electrolessly metal plated with a substantially colloidal metal particle-free acid liquid solution of a soluble lower alkanol-modified noble metal-tin chloride complex until the surface is rendered catalytic, the noble metal of the complex being a noble metal catalytic to the chemical reduction deposition of the metal desired to be plated on said surface, and electrolessly plating the metal on the thus-obtained catalytic surface by contacting the catalytic surface with a chemical reduction metal plating bath, the soluble lower alkanol-modified noble metal-tin chloride complex being obtained by mixing together a lower alkanol, a soluble noble metal chloride, stannous chloride, and hydrochloric acid, and maintaining the thus-obtained liquid mixture at a reaction temperature of at least about 160°F. but below that temperature at which an excessive amount of noble metal is precipitated for a period sufficient to obtain a catalytically effective solution containing the soluble lower alkanol-modified noble metal-tin chloride complex, the stannous chloride being present in excess of the amount thereof required to reduce the noble metal chloride to zero valent noble metal, the molar ratio of stannous chloride to the noble metal chloride (calculated as palladium chloride) being initially at least about 9-10:1 respectively, and the lower alkanol being present in amount sufficient to obtain a soluble complex.
Claim 3
Dependent Claim
24 words
The process of claim 1 wherein the liquid solution of the lower alkanol-modified noble metal-tin chloride complex has a pH of less than 1.
Claim 4
Dependent Claim
11 words
The process of claim 2 wherein the lower alkanol is methanol.
Claim 5
Dependent Claim
19 words
The process of claim 3 wherein the reaction temperature is in the range of about 160°F. to about 185°F.
Claim 6
Dependent Claim
32 words
The process of claim 3 wherein the methanol is present in amount sufficient to obtain a soluble complex but insufficient to result in excessive by-produce formation with attendant excessive gas pressure build-up.
Claim 7
Dependent Claim
32 words
The process of claim 4 wherein the methanol is present in amount sufficient to obtain a soluble complex but insufficient to result in excessive by-product formation with attendant excessive gas pressure build-up.
Claim 8
Dependent Claim
34 words
The process of claim 2 wherein the mixture is maintained at the temperature of about 160°F. or higher for a period of at least about 4-9 hours and sufficient to obtain said soluble complex.
Claim 9
Dependent Claim
38 words
The process of claim 4 wherein the mixture is maintained at the temperature in the range of about 160°F. to about 185°F. for a period of at least about 9 hours and sufficient to obtain said soluble complex.
Claim 10
Dependent Claim
26 words
The process of claim 4 wherein the methanol is added in the formation of the reaction mixture prior to the addition of the noble metal chloride.
Claim 11
Dependent Claim
26 words
The process of claim 5 wherein the methanol is added in the formation of the reaction mixture prior to the addition of the noble metal chloride.
Claim 12
Dependent Claim
25 words
The process of claim 1 wherein the catalytic surface of the object is contacted with a dilute HCl solution prior to the electroless metal plating.
Claim 13
Dependent Claim
20 words
The process of claim 4 wherein the reaction temperature is maintained in the range of about 170°F. to about 185°F.
Claim 14
Dependent Claim
23 words
The process of claim 2 wherein the noble metal of the complex is palladium and the soluble noble metal chloride is palladium chloride.
Claim 15
Dependent Claim
13 words
The process of claim 2 wherein the stannous chloride is added in increments.
Claim 16
Dependent Claim
26 words
The process of claim 2 wherein a soluble alkali stannate is mixed together with the lower alkanol, soluble noble metal chloride, stannous chloride and hydrochloric acid.
Claim 17
Dependent Claim
16 words
The process of claim 15 wherein the soluble alkali stannate is a soluble alkali metal stannate.
Claim 18
Dependent Claim
13 words
The process of claim 16 wherein the alkali metal stannate is sodium stannate.
Claim 19
Dependent Claim
189 words
The process of claim 2 wherein the soluble lower alkanol-modified noble metal-tin chloride complex is obtained by introducing water and a soluble alkali metal stannate into a reaction zone, agitating the resulting mixture until the alkali metal stannate is dissolved in the water, adding to the thus-obtained aqueous solution a solution containing stannous chloride and hydrochloric acid, agitating the resulting mixture, adding hydrochloric acid to the thus-obtained mixture, adding a lower alkanol to the thus-obtained mixture, heating the resulting mixture to a reaction temperature in the range of about 170°F. to about 185°C. while agitating said mixture, slowly adding at a controlled rate a solution of an acid-soluble noble metal chloride in hydrochloric acid to the thus-obtained mixture, adding to the resulting mixture increments of a solution of stannous chloride in hydrochloric acid, separately adding to the thus-obtained mixture hydrochloric acid and stannous chloride, maintaining the resulting mixture at a reaction temperature in the range of about 170°F. to about 185°F. for a period of at least about 4 hours and sufficient to obtain the soluble complex, agitating the resulting mixture, and cooling the thus-obtained mixture to room temperature.
Claim 20
Dependent Claim
11 words
The process of claim 18 wherein the lower alkanol is methanol.
Claim 21
Dependent Claim
58 words
The process of claim 19 wherein the noble metal is palladium, the noble metal chloride is palladium chloride, the alkali metal stannate is sodium stannate, and the cooling of the thus-obtained mixture is by permitting said mixture to cool to room temperature without agitation of the mixture, and thereafter agitating the thus-obtained solution for at least 15 minutes.
Claim 22
Dependent Claim
19 words
The process of claim 2 wherein the electrolessly metal plated surface is electroplated with one or more desired metals.
References Cited (Backward Citations)
US3767583A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-08-24 | 1980-02-23 | 1980-08-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-08-24 | 1984-02-23 | 1984-08-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-08-24 | 1988-02-23 | 1988-08-24 | $7700.00 | Window Closed / Lapsed |