Water dispersible epoxy ether-aminoacrylate polymers
Assignee: DeSoto Inc
•
Filing: 1974-11-13
•
Granted: 1976-08-24
•
Expires: 1994-11-13
Abstract
Abstract Epoxy ether-amino acrylate polymers dispersible in water with the aid of an acid are provided by etherifying a polyepoxide with an ethylenically unsaturated alcohol to provide an unsaturated hydroxy-functional polyether containing from about 1.2 to about 2.0 ethylenically unsaturated ether groups per molecule. This polyether is copolymerized in organic solvent solution with monoethylenically unsaturated monomers including amine-functional monomer to provide an amine copolymer which is solubilized in water with an acid at a pH of 5.0-7.0. These water dispersions which are formed can be electrodeposited at the cathode to form valuable coatings despite the approximately neutral pH of the bath from which they are deposited.
Inventors
- 👤 Kazys Sekmakas
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 10:55
CPC Classifications
C; C09; C09D; C09D5/00; C09D5/44; C09D5/4407; C08; C08G; C08G59/00; C08G59/14; C08G59/1433; C08G59/1438; C08G59/1444; C09D155/00; C09D155/005
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
86 words
A non-gelled, amine-functional polymer dispersible in water with the aid of a solubilizing acid, said polymer being a copolymer of: A. an unsaturated hydroxy functional polyether formed by etherifying a polyepoxide having a 1,2-epoxy equivalency of from 1.2 to about 2.0 with an ethylenically unsaturated monohydric alcohol to consume substantially all of the epoxy functionality in the production of a polyether containing from about 1.2 to about 2.0 ethylenically unsaturated ether groups per molecule; and B. copolymerizable monoethylenically unsaturated monomers, a portion of which is amine-functional.
Claim 2
Dependent Claim
86 words
A non-gelled, amine-functional polymer dispersible in water with the aid of a solubilizing acid, said polymer being a copolymer of: A. an unsaturated hydroxy functional polyether formed by etherifying a polyepoxide having a 1,2-epoxy equivalency of from 1.2 to about 2.0 with an ethylenically unsaturated monohydric alcohol to consume substantially all of the epoxy functionality in the production of a polyether containing from about 1.2 to about 2.0 ethylenically unsaturated ether groups per molecule; and B. copolymerizable monoethylenically unsaturated monomers, a portion of which is amine-functional.
Claim 3
Dependent Claim
40 words
A water dispersible polymer as recited in claim 1 in which said copolymer is formed by copolymerization in organic solvent solution and is soluble in water with the aid of a solubilizing acid at a pH of 5.0 to 7.0.
Claim 4
Dependent Claim
20 words
A water dispersible polymer as recited in claim 1 in which said monoethylenically unsaturated monomers include water soluble reactive monomers.
Claim 5
Dependent Claim
30 words
A water dispersible polymer as recited in claim 3 in which said water soluble reactive monomers provide reactive functionality from the group of amide, N-methylol, etherified N-methylol, and alcoholic hydroxy.
Claim 6
Dependent Claim
30 words
A water dispersible polymer as recited in claim 4 in which said water soluble reactive monomers are present in an amount of 5-30%, based on the weight of the polymer.
Claim 7
Dependent Claim
17 words
A water dispersible polymer as recited in claim 1 in which said polyepoxide is a polyglycidyl ether.
Claim 8
Dependent Claim
31 words
A water dispersible polymer as recited in claim 6 in which said polyglycidyl ether has a 1,2-epoxy equivalency of from 1.4 to 2.0 and a hydroxy equivalency of at least 0.1.
Claim 9
Dependent Claim
32 words
A water dispersible polymer as recited in claim 7 in which said polyglycidyl ether is a polyglycidyl ether of a bisphenol having a molecular weight of from about 350 to about 4000.
Claim 10
Dependent Claim
24 words
A water dispersible polymer as recited in claim 1 in which said monohydric alcohol is selected from oleyl alcohol, linoleyl alcohol and linolenyl alcohol.
Claim 11
Dependent Claim
18 words
A water dispersible polymer as recited in claim 1 in which said solubilizing acid is an organic acid.
Claim 12
Dependent Claim
17 words
A water dispersible polymer as recited in claim 1 in which said organic acid is acetic acid.
Claim 13
Dependent Claim
42 words
A water dispersible polymer as recited in claim 1 in which said monoethylenically unsaturated monomers include acrylamide, and the amide functionality is reacted with formaldehyde to provide N-methylol functionality to enable said polymer to thermoset in the absence of extraneous curing agent.
Claim 14
Dependent Claim
31 words
A water dispersible polymer as recited in claim 1 in which said unsaturated polyether constitutes from 5-75% of the polymer and said copolymer includes from 4-20% of copolymerized monoethylenically unsaturated amine.
Claim 15
Dependent Claim
44 words
A water dispersible polymer as recited in claim 13 in which said unsaturated polyether constitutes from 20-60% of the weight of the polymer, and the balance of the polymer consists essentially of copolymerized monoethylenically unsaturated monomers including from 6-15% of monoethylenically unsaturated tertiary amine.
Claim 16
Dependent Claim
17 words
A water dispersible polymer as recited in claim 14 in which said amine is dimethyl aminoethyl methacrylate.
Claim 17
Dependent Claim
18 words
A water dispersible polymer as recited in claim 14 in which said amine is dimethyl aminopropyl meta acrylamide.
Claim 18
Dependent Claim
29 words
A water dispersion of the polymer defined in claim 1 dispersed in water with the aid of an acid, said dispersion having a pH in the range of 5.0-7.0.
Claim 19
Dependent Claim
21 words
A water dispersion as recited in claim 17 in which said water dispersion further includes an aminoplast or phenolformaldehyde curing agent.
Claim 20
Dependent Claim
21 words
An aqueous electrocoat bath comprising the water dispersion of claim 17 having a resin solids content of from 4-20% by weight.
Claim 21
Dependent Claim
61 words
A method of electrodepositing a physically tough, corrosion resistant coating on the cathode of a unidirectional electrical system from an aqueous bath having a pH of 5.0-7.0 comprising passing a unidirectional electrical current through the bath defined in claim 19 to deposit a coating of said polymer on the cathode, removing the coated cathode from the bath, and baking the same.
References Cited (Backward Citations)
US2792381A
Cited
US2864804A
Cited
US3156674A
Cited
US3247284A
Cited
US3264370A
Cited
US3642939A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-08-24 | 1980-02-23 | 1980-08-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-08-24 | 1984-02-23 | 1984-08-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-08-24 | 1988-02-23 | 1988-08-24 | $7700.00 | Window Closed / Lapsed |