Method of manufacturing high-frequency raster with irregular structure of raster elements
Assignee: Individual
•
Filing: 1974-03-15
•
Granted: 1976-08-24
•
Expires: 1994-03-15
Abstract
Abstract What is proposed is a high-frequency raster with an irregular structure of raster elements. This raster is a plane-parallel glass plate with transparent roughnesses on its surface characterized by a value Ra equal to 0.20-0.26 mu. A method of manufacturing a high-frequency raster with an irregular structure of raster elements, in which a glass plate is ground at two sides to obtain a uniform structure of the surface. The ground plate is subjected to etching to obtain transparent microroughnesses with a value Ra equal to 0.20-0.26 mu. The raster proposed by the present invention is characterized by a high resolving power in the order of 25 mm - 1 , transmits a normal interval of optical densities of 1.0 to 1.2 and is capable of reproducing an image with a finely grained discrete structure.
Inventors
- 👤 Viktoria Ivanovna Andreeva
- 👤 Alexandra Ljudovikovna Popova
- 👤 Veniamin Semenovich Lapatukhin
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 18:45
CPC Classifications
C; C03; C03C; C03C15/00; G; G03; G03F; G03F5/00; G03F5/02; G03F5/12
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
137 words
A method of manufacturing an optical high-frequency raster with an irregular structure of raster elements, the raster comprising a substantially plane-parallel glass plate having microroughnesses with a value Ra equal to 0.20 to 0.26 mu on both surfaces; the method comprising the steps of mechanically grinding the glass plate with an abrasive compound at both sides, each for about 40 minutes, to obtain a uniform surface structure; thoroughly washing the ground glass plate with water; and subjecting the ground and washed glass plate to multiple etching, at least three times, to obtain transparent microroughnesses with a value Ra equal to 0.20 to 0.26 mu; whereby the resulting optical high-frequency raster has a high resolving power of at least 25 mm.sup. -1 , and is capable of transmitting an interval of optical densities between approx. 1.0 and 1.2.
Claim 2
Independent Claim
137 words
A method of manufacturing an optical high-frequency raster with an irregular structure of raster elements, the raster comprising a substantially plane-parallel glass plate having microroughnesses with a value Ra equal to 0.20 to 0.26 mu on both surfaces; the method comprising the steps of mechanically grinding the glass plate with an abrasive compound at both sides, each for about 40 minutes, to obtain a uniform surface structure; thoroughly washing the ground glass plate with water; and subjecting the ground and washed glass plate to multiple etching, at least three times, to obtain transparent microroughnesses with a value Ra equal to 0.20 to 0.26 mu; whereby the resulting optical high-frequency raster has a high resolving power of at least 25 mm.sup. -1 , and is capable of transmitting an interval of optical densities between approx. 1.0 and 1.2.
Claim 3
Dependent Claim
33 words
The method as defined in claim 1, wherein said etching step is carried out in a solution containing 4 parts by volume of hydrofluoric acid and 1 part by volume of sulphuric acid.
Claim 4
Dependent Claim
33 words
The method as defined in claim 1, wherein said etching step is carried out in a solution containing 3 parts by volume of hydrofluoric acid and 1 part by volume of phosphoric acid.
Claim 5
Dependent Claim
39 words
The method as defined in claim 1, wherein said etching step is carried out in a solution containing 4 parts by volume of hydrofluoric acid, 1 part by volume of sulphuric acid and 1 part by volume of water.
Claim 6
Dependent Claim
61 words
The method as defined in claim 1, wherein said mechanical grinding step includes partial mechanical abrasion with the aid of electrically produced corundum, mixed with water in a ratio of 1 to 3, the solution being renewed in the partial abrasion each 10 to 12 minutes, to obtain intermediate transparent micro-roughnesses with a value Ra equal to 0.40 to 0.46 mu.
Claim 7
Dependent Claim
31 words
The method as defined in claim 1, wherein said mechanical grinding and said washing steps are alternated at least twice within the multiple etching that is performed at least three times.
References Cited (Backward Citations)
US2189988A
Cited
US2370214A
Cited
US2670279A
Cited
US2999013A
Cited
US3374130A
Cited
US3527628A
Cited
US3647583A
Cited
US3813568A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-08-24 | 1980-02-23 | 1980-08-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-08-24 | 1984-02-23 | 1984-08-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-08-24 | 1988-02-23 | 1988-08-24 | $7700.00 | Window Closed / Lapsed |