Process for producing alpha alumina monohydrate
Assignee: Vista Chemical Co
•
Filing: 1975-04-03
•
Granted: 1976-08-17
•
Expires: 1995-04-03
Abstract
Abstract Alpha alumina monohydrate wherein a majority of the cumulative pore volume consists of pores from about 30 to about 120 A in diameter and a method for producing such alumina.
Inventors
- 👤 Dennis Jack Royer
- 👤 George G. Hritz
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 11:31
CPC Classifications
B; B01; B01J; B01J35/00; B01J35/60; B01J20/00; B01J20/02; B01J20/06; B01J20/08; B01J21/00; B01J21/02; B01J21/04; C; C01; C01F; C01F7/00; C01F7/02; B01J35/61; B01J35/615; B01J35/63; B01J35/633; B01J35/64; B01J35/647; B01J35/66; B01J35/67; C01P; C01P2006/00; C01P2006/10; C01P2006/12; C01P2006/14; C01P2006/16
Claims Analysis
Total Claims: 4
Claim 1
Independent Claim
138 words
A method for producing alpha alumina monohydrate product having: a. a loose bulk density from about 40 to about 60 lb/ft 3 , b. a surface area from about 100 to about 250 m 2 /g, c. a cumulative pore volume, 0-10,000 A from about 0.3 to about 0.6 cc/g, and d. from about 75 to about 100 percent of said cumulative pore volume in pores from about 30 to about 120 A in diameter; by mixing 100 parts dispersible alpha alumina monohydrate with from about 30 to about 3000 parts water and from about 0.3 to about 40 parts acid, said acid being selected from the group consisting of hdyrochloric acid, nitric acid, acetic acid and monochloroacetic acid to form a mixture of uniform consistency and thereafter drying to produce alpha alumina monohydrate product having said properties.
Claim 2
Independent Claim
138 words
A method for producing alpha alumina monohydrate product having: a. a loose bulk density from about 40 to about 60 lb/ft 3 , b. a surface area from about 100 to about 250 m 2 /g, c. a cumulative pore volume, 0-10,000 A from about 0.3 to about 0.6 cc/g, and d. from about 75 to about 100 percent of said cumulative pore volume in pores from about 30 to about 120 A in diameter; by mixing 100 parts dispersible alpha alumina monohydrate with from about 30 to about 3000 parts water and from about 0.3 to about 40 parts acid, said acid being selected from the group consisting of hdyrochloric acid, nitric acid, acetic acid and monochloroacetic acid to form a mixture of uniform consistency and thereafter drying to produce alpha alumina monohydrate product having said properties.
Claim 3
Dependent Claim
33 words
The method of claim 1 wherein said 100 parts dispersible alpha alumina monohydrate is mixed with from about 200 to about 400 parts water and from about 20 to about 40 parts acid.
Claim 4
Dependent Claim
115 words
The method of claim 1 wherein said 100 parts alpha alumina monohydrate is "DISPAL" alumina and said alumina is mixed with from about 250 to about 350 parts water and from about 0.75 to about 2.0 parts nitric acid to produce a dispersible alpha alumina monohydrate having a. a loose bulk density from about 50 to about 55 lb/ft 3 , b. a surface area from about 200 to about 225 m 2 /g, c. a cumulative pore volume, 0-10,000 A from about 0.3 to about 0.35 m 2 /g, and d. from about 85 to about 95 percent of said cumulative pore volume in pores from about 50 to about 65 A in diameter.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-08-17 | 1980-02-16 | 1980-08-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-08-17 | 1984-02-16 | 1984-08-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-08-17 | 1988-02-16 | 1988-08-17 | $7700.00 | Window Closed / Lapsed |