PTC thermistor composition and method of making the same
Assignee: Panasonic Holdings Corp
•
Filing: 1974-10-09
•
Granted: 1976-08-17
•
Expires: 1994-10-09
Abstract
Abstract A PTC thermistor composition comprising BaTiO3, TiO2, one oxide selected from the group consisting of Nb2O5 and Y2O3, Al2O3, SiO2, Li2CO3, MnO2 and one oxide selected from the group consisting of Sb2O3 and Bi2O3, and process for the production thereof are provided. Said process is characterized by the addition of TiO2 and Nb2O5 to BaTiO3 before calcination and the addition of Al2O3, SiO2, Li2CO3, MnO2 and Sb2O3 after the calcination. This PTC thermistor composition has a high breakdown voltage, a large electric current at the initial moment of a voltage application which current decreases rapidly with continuing voltage application, low specific resistivity and, good stability of resistivity.
Inventors
- 👤 Yoshihiro Matsuo
- 👤 Masanori Fujimura
- 👤 Tomizo Matsuoka
- 👤 Shigeru Hayakawa
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 23:25
CPC Classifications
H; H01; H01B; H01B1/00; H01B1/06; H01B1/08; H01C; H01C1/00; H01C1/14; H01C1/1406; H01C7/00; H01C7/02; H01C7/022; H01C7/023; H01C7/025; H05; H05B; H05B3/00; H05B3/10; H05B3/12; H05B3/14; H05B3/141
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
88 words
A PTC thermistor composition comprising BaTiO 3 as a major element and, as additive elements 0.05 to 1.24 percent by weight of SiO 2 , 0.007 to 0.09 percent by weight of a lithium compound convertible by air firing to lithium oxide, 0.003 to 0.04 percent by weight of MnO 2 or manganese compound convertible by air firing to a manganese oxide, and 0.05 to 0.22 percent by weight of one oxide selected from the group consisting of Nb 2 O 5 and Y 2 O 3 .
Claim 2
Dependent Claim
88 words
A PTC thermistor composition comprising BaTiO 3 as a major element and, as additive elements 0.05 to 1.24 percent by weight of SiO 2 , 0.007 to 0.09 percent by weight of a lithium compound convertible by air firing to lithium oxide, 0.003 to 0.04 percent by weight of MnO 2 or manganese compound convertible by air firing to a manganese oxide, and 0.05 to 0.22 percent by weight of one oxide selected from the group consisting of Nb 2 O 5 and Y 2 O 3 .
Claim 3
Dependent Claim
41 words
A PTC thermistor composition according to claim 1, wherein said lithium compound is one member selected from the group consisting of Li 2 CO 3 , LiNO 3 , Li 2 SO 4 and Li 2 C 2 O 4 .
Claim 4
Dependent Claim
35 words
A PTC thermistor composition according to claim 1, wherein said manganese compound is one member selected from the group consisting of MnCO 3 , Mn(NO 3 ) 2 , and MnC 2 O 4 .
Claim 5
Dependent Claim
21 words
A PTC thermistor composition according to claim 1, which further comprises less than 1.30 percent by weight of TiO 2 .
Claim 6
Dependent Claim
23 words
A PTC thermistor composition according to claim 4, which further comprises less than 1.26 percent by weight of Al 2 O 3 .
Claim 7
Dependent Claim
36 words
A PTC thermistor composition according to claim 5, which further comprises less than 0.12 percent by weight of one member selected from the group consisting of Sb 2 O 3 and Bi 2 O 3 .
Claim 8
Dependent Claim
36 words
A PTC thermistor composition according to claim 4, which further comprises less than 0.12 percent by weight of one member selected from the group consisting of Sb 2 O 3 and Bi 2 O 3 .
Claim 9
Dependent Claim
23 words
A PTC thermistor composition according to claim 1, which further comprises less then 1.26 percent by weight of Al 2 O 3 .
Claim 10
Dependent Claim
28 words
A PTC thermistor composition according to claim 8, which further comprises less than 0.12 percent by weight of Sb 2 O 3 and Bi 2 O 3 .
Claim 11
Dependent Claim
28 words
A PTC thermistor composition according to claim 1, which further comprises less than 0.12 percent by weight of Sb 2 O 3 and Bi 2 O 3 .
Claim 12
Dependent Claim
25 words
A PTC thermistor composition according to claim 1, wherein Ba in BaTiO 3 is replaced by an amount of Sr less than 40 atomic percent.
Claim 13
Dependent Claim
25 words
A PTC thermistor composition according to claim 1, wherein Ba in BaTiO 3 is replaced by an amount of Pb less than 30 atomic percent.
Claim 14
Dependent Claim
25 words
A PTC thermistor composition according to claim 1, wherein Ti in BaTiO 3 is replaced by an amount of Sn less than 30 atomic percent.
Claim 15
Dependent Claim
37 words
A PTC thermistor composition according to claim 1, wherein Ba in BaTiO 3 is replaced by an amount of 1 to 30 atomic percent of Sr and by an amount 1 to 20 atomic percent of Pb.
Claim 16
Dependent Claim
41 words
A PTC thermistor composition according to claim 1, wherein Ba in BaTiO 3 is replaced by an amount of 1 to 20 atomic percent of Pb and Ti is replaced by an amount of 1 to 30 atomic percent of Sn.
Claim 17
Independent Claim
213 words
A method of producing a PTC thermistor comprising preparing a mixture consisting of BaCO 3 and TiO 2 to be converted into 99.89 to 95.73 percent by weight of BaTiO 3 , less than 1.30 percent by weight of TiO 2 and 0.05 to 0.22 percent by weight of one oxide selected from the group consisting of Nb 2 O 5 and Y 2 O 3 , calcining the mixture at a temperature of 900 to 1250°C, milling the calcined material with additives of less than 1.26 percent by weight of Al 2 O 3 , 0.05 to 1.24 percent by weight of SiO 2 , 0.007 to 0.09 percent by weight of Li 2 CO 3 , 0.003 to 0.04 percent by weight of MnO 2 and less than 0.12 percent by weight of one oxide selected from the group consisting of Sb 2 O 3 and Bi 2 O 3 , pressing the mixture of the calcined material and said additives into a pressed body, firing the pressed body at a temperature of 1240°C to 1400°C for 0.5 to 5 hours, thereafter cooling the fired body to a temperature less than 800°C at a cooling rate lower than 300°C per hour, and thereafter cooling the thus cooled body to room temperature.
Claim 18
Independent Claim
213 words
A method of producing a PTC thermistor comprising preparing a mixture consisting of BaCO 3 and TiO 2 to be converted into 99.89 to 95.73 percent by weight of BaTiO 3 , less than 1.30 percent by weight of TiO 2 and 0.05 to 0.22 percent by weight of one oxide selected from the group consisting of Nb 2 O 5 and Y 2 O 3 , calcining the mixture at a temperature of 900 to 1250°C, milling the calcined material with additives of less than 1.26 percent by weight of Al 2 O 3 , 0.05 to 1.24 percent by weight of SiO 2 , 0.007 to 0.09 percent by weight of Li 2 CO 3 , 0.003 to 0.04 percent by weight of MnO 2 and less than 0.12 percent by weight of one oxide selected from the group consisting of Sb 2 O 3 and Bi 2 O 3 , pressing the mixture of the calcined material and said additives into a pressed body, firing the pressed body at a temperature of 1240°C to 1400°C for 0.5 to 5 hours, thereafter cooling the fired body to a temperature less than 800°C at a cooling rate lower than 300°C per hour, and thereafter cooling the thus cooled body to room temperature.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-08-17 | 1980-02-16 | 1980-08-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-08-17 | 1984-02-16 | 1984-08-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-08-17 | 1988-02-16 | 1988-08-17 | $7700.00 | Window Closed / Lapsed |