Electrolyte for electrochemical machining of nickel base superalloys
Assignee: RTX Corp
•
Filing: 1975-12-05
•
Granted: 1976-08-17
•
Expires: 1995-12-05
Abstract
Abstract An electrolyte useful in the electrochemical machining of the high strength nickel base superalloys is described. The electrolyte is an aqueous solution containing nitric acid, hydrochloric acid and citric acid in specific quantities. Nickel base superalloys electrochemically machined using the electrolyte of the invention possess extremely smooth machined surfaces which are free from smut and other undesirable surface problems.
Inventors
- 👤 Everett John Bergquist
- 👤 Lawrence Joseph Jennings
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 22:00
CPC Classifications
B; B23; B23H; B23H3/00; B23H3/08
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
39 words
An electrolyte for electrochemical machining comprising an aqueous solution containing from about 10 to about 300 ml/gal nitric acid, from about 40 to about 150 ml/gal hydrochloric acid, and from about 0.5 to about 3 lbs/gal of citric acid.
Claim 2
Dependent Claim
39 words
An electrolyte for electrochemical machining comprising an aqueous solution containing from about 10 to about 300 ml/gal nitric acid, from about 40 to about 150 ml/gal hydrochloric acid, and from about 0.5 to about 3 lbs/gal of citric acid.
Claim 3
Dependent Claim
41 words
An electrolyte as in claim 1 useful for the electrochemical machining of nickel base superalloys, wherein the nitric acid concentration is about 60 ml/gal, the hydrochloric acid concentration is about 50 ml/gal and the citric acid concentration is about 1 lb/gal.
Claim 4
Dependent Claim
87 words
A process of electrochemically machining nickel base superalloy articles including the steps of: a. providing the nickel base superalloy article, b. immersing the article in an aqueous solution containing from about 10 to about 300 ml/gal of nitric acid, from about 40 to about 150 ml/gal of hydrochloric acid and from about 0.5 to about 3 lbs/gal of citric acid, c. applying a voltage of from about 7 to about 20 volts between the workpiece and tool, with the workpiece being anodic and the tool being cathodic.
Claim 5
Dependent Claim
87 words
A process of electrochemically machining nickel base superalloy articles including the steps of: a. providing the nickel base superalloy article, b. immersing the article in an aqueous solution containing from about 10 to about 300 ml/gal of nitric acid, from about 40 to about 150 ml/gal of hydrochloric acid and from about 0.5 to about 3 lbs/gal of citric acid, c. applying a voltage of from about 7 to about 20 volts between the workpiece and tool, with the workpiece being anodic and the tool being cathodic.
Claim 6
Dependent Claim
38 words
A process as in claim 3 wherein the nominal composition of the nickel base superalloy is about 9% Cr, 10% Co, 2% Ti, 5% Al, 0.15% C, 12% W, 1% Cb, 2% Hf, 0.015% B, balance essentially nickel.
Claim 7
Dependent Claim
40 words
A process as in claim 3 wherein the nominal composition of the nickel base superalloy is about 16% Cr, 8.5% Co, 3.5% Ti, 3.5% Al, 0.12% C, 2.6% W, 1.75% Ta, 0.8% Cb, 0.012% B, 0.1% Zr, balance essentially nickel.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-08-17 | 1980-02-16 | 1980-08-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-08-17 | 1984-02-16 | 1984-08-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-08-17 | 1988-02-16 | 1988-08-17 | $7700.00 | Window Closed / Lapsed |