US3975224A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Dimensionally stable, high-tenacity non-woven webs and process
Assignee: Lutravil Spinnvlies GmbH and Co
•
Filing: 1973-08-16
•
Granted: 1976-08-17
•
Expires: 1993-08-16
Abstract
Abstract Dimensionally stable, high-tenacity non-woven webs and process for their manufacture. The non-woven webs of the invention are distinguished by a relative grab-tensile strength of at least 200 p/g/m 2 , a breaking extension of not more than 50% and a shrinkage of not more than 1%, as measured at 160°C, and are primarily useful as reinforceing and backing materials in the manufacture of needle-punched and tufted carpets.
Inventors
- 👤 Ivo Ruzek
- 👤 Guenther Worf
- 👤 Ludwig Hartmann
- 👤 Paul Maahs
- 👤 Lueder Gerking
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 23:41
CPC Classifications
D; D04; D04H; D04H3/00; D04H3/005; D04H3/009; D04H3/011; D01; D01D; D01D5/00; D01D5/08; D01D5/098; D01D5/0985; D01D5/12; D01D5/14; D01D5/28; D01D5/30; D01D5/36; D04H3/007; D04H3/08; D04H3/14; D04H3/153; D04H3/16; D05; D05C; D05C17/00; D05C17/02; D05C17/023; D10; D10B; D10B2321/00; D10B2321/02; D10B2331/00; D10B2331/02; D10B2331/04; D10B2331/10; Y; Y10; Y10T; Y10T442/00; Y10T442/60; Y10T442/681; Y10T442/69; Y10T442/692
Claims Analysis
Total Claims: 28
Claim 1
Independent Claim
224 words
A process for the manufacture of dimensionally stable, high-tenacity non-woven webs using a spinning system comprising a groupwise arrangement of elongated spinnerets through which two different types of synthetic filaments are simultaneously spun in the form of rows forming bundles, wherein parallel linear bundles of a. matrix filaments of a melt-spinnable polyester and b. binder filaments of a melt-spinnable polymer having a melting point above 160°C but not above the temperature which is 30°C below the melting point of the matrix filaments are spun downwardly at a throughput rate of from 3.5 to 10 g/min per spinneret hole, the ratio of the number of the binder filaments to the number of the matrix filaments being in the range of 1:1 to 1:5 and the ratio by weight between said matrix and binder filaments being in the range of 10:90 to 30:70, the bundles of filaments then being cooled below the holes and simultaneously being drawn, in groups, through a common narrow slot in a slotted aerodynamic haul-off device by means of flowing gas media at a filament speed of from 2,000 to 15,000 m/min with thermosetting and simultaneous mixing in said device as combined parallel bundles, which are then laid down below the aerodynamic haul-off device to form a random web, which is then thermally bonded in one or more stages of increasing temperature.
Claim 2
Dependent Claim
224 words
A process for the manufacture of dimensionally stable, high-tenacity non-woven webs using a spinning system comprising a groupwise arrangement of elongated spinnerets through which two different types of synthetic filaments are simultaneously spun in the form of rows forming bundles, wherein parallel linear bundles of a. matrix filaments of a melt-spinnable polyester and b. binder filaments of a melt-spinnable polymer having a melting point above 160°C but not above the temperature which is 30°C below the melting point of the matrix filaments are spun downwardly at a throughput rate of from 3.5 to 10 g/min per spinneret hole, the ratio of the number of the binder filaments to the number of the matrix filaments being in the range of 1:1 to 1:5 and the ratio by weight between said matrix and binder filaments being in the range of 10:90 to 30:70, the bundles of filaments then being cooled below the holes and simultaneously being drawn, in groups, through a common narrow slot in a slotted aerodynamic haul-off device by means of flowing gas media at a filament speed of from 2,000 to 15,000 m/min with thermosetting and simultaneous mixing in said device as combined parallel bundles, which are then laid down below the aerodynamic haul-off device to form a random web, which is then thermally bonded in one or more stages of increasing temperature.
Claim 3
Dependent Claim
29 words
A process as claimed in claim 1, wherein the binder filaments are spun from a member from the group consisting of polyamides, copolyamides, polyesters, copolyesters, isotactic polyolefins and polyurethanes.
Claim 4
Dependent Claim
15 words
A process as claimed in claim 1, wherein the binder filaments are spun from polycaprolactam.
Claim 5
Dependent Claim
28 words
A process as claimed in claim 1, wherein the binder filaments are spun from a copolyamide consisting of caprolactam with not more than 20% molar of hexamethylene adipamide.
Claim 6
Dependent Claim
32 words
A process as claimed in claim 1, wherein the binder filaments are spun from a copolyester of ethylene terephthalate and ethylene isophthalate containing from 5 to 30% molar of isophthalic acid units.
Claim 7
Dependent Claim
32 words
A process as claimed in claim 1, wherein the binder filaments are spun from a copolyester of ethylene terephthalate and ethylene adiptate containing from 5 to 40% molar of adipic acid units.
Claim 8
Dependent Claim
16 words
A process as claimed in claim 1, wherein the binder filaments are spun from isotactic polypropylene.
Claim 9
Dependent Claim
16 words
A process as claimed in claim 1, wherein the binder filaments are spun from linear polyurethane.
Claim 10
Dependent Claim
39 words
A process as claimed in claim 1, wherein the resulting random web is initially compressed to a thickness of from 0.05 to 1.0 mm and simultaneously prebonded by means of heated rollers at temperatures of from 70° to 110°C.
Claim 11
Dependent Claim
37 words
A process as claimed in claim 1, wherein the random web is bonded in a condition of fixed area under pressure by means of a flow of gaseous heating medium at temperatures of from 160° to 245°C.
Claim 12
Dependent Claim
32 words
A process as claimed in claim 1, wherein a coating composition is applied to the random web before bonding, which composition consists of a mixture of lubricants, antistatic agents and wetting agents.
Claim 13
Dependent Claim
29 words
A process as claimed in claim 1, wherein bonding is carried out in stages and the said coating composition is applied to one side only of the random web.
Claim 14
Dependent Claim
34 words
A process as claimed in claim 1, wherein a dye liquor containing a dye suitable for thermosoling is applied to the random web before bonding thermosoling being carried out simultaneously with the bonding operation.
Claim 15
Dependent Claim
47 words
Dimensionally stable, high-strength non-woven webs as prepared by the process claimed in claim 1 and having a relative grabtensile strength of at least ##EQU4## and preferably more than ##EQU5## a breaking extension of not more than 50% and shrinkage values of not more than 1% at 160°C.
Claim 16
Dependent Claim
14 words
A process as claimed in claim 1 wherein said melt-spinnable polyester is polyethylene terephthalate.
Claim 17
Dependent Claim
23 words
A process as claimed in claim 1 wherein said throughput rate is in the range of 4.0 to 7.0 g/min per spinneret hole.
Claim 18
Dependent Claim
32 words
A process as claimed in claim 1 wherein said random web is treated with at least one of a coating composition and a dye before bonding or between the individual bonding stages.
Claim 19
Dependent Claim
43 words
A process as claimed in claim 1 wherein said ratio of the number of binder filaments to the number of matrix filaments is in the range of 1:1.5 to 1:2.5, and said ratio by weight is in the range of 15:85 to 25:75.
Claim 20
Dependent Claim
21 words
A process as claimed in claim 4 wherein the molar amount of said hexamethylene adipamide is not more than 15% molar.
Claim 21
Dependent Claim
20 words
A process as claimed in claim 6 wherein said isophthalic acid units in said copolyester constitute 8 to 25% molar.
Claim 22
Dependent Claim
20 words
A process as claimed in claim 6 wherein said adipic acid units in said copolyester constitute 10 to 30% molar.
Claim 23
Dependent Claim
14 words
A process as claimed in claim 10 wherein said gaseous heating medium is steam.
Claim 24
Dependent Claim
17 words
A process as claimed in claim 10 wherein said gaseous heating medium is hot air and steam.
Claim 25
Dependent Claim
25 words
A process as claimed in claim 1 wherein the filaments contained in said random web have an individual tenacity strength of at least 20 ponds.
Claim 26
Dependent Claim
30 words
A process as claimed in claim 1 wherein the filaments in said random web have an individual tenacity strength of more than 30 ponds and weigh more than 8 dtex.
Claim 27
Dependent Claim
34 words
A process as claimed in claim 1 wherein the filaments in said random web have relative filament tenacities between 2.4 and 4.0 ponds/dtex, and the filaments being spun are of at least 6 dtex.
Claim 28
Dependent Claim
67 words
A process as claimed in claim 1 wherein the filaments are spun downwardly into a protective shaft immediately below said elongated spinnerets, the bundles of said filaments being cooled below said spinneret holes in a cross flow current of gaseous cooling medium in said shaft, and said filaments being drawn through said shaft solely by means of said flowing gas media of said slotted aerodynamic haul-off device.
References Cited (Backward Citations)
US3255064A
Cited
US3546328A
Cited
GB1055187A
Cited
GB1089414A
Cited
US3423266A
Cited
US3368934A
Cited
US3441468A
Cited
US3659989A
Cited
US3509009A
Cited
US3433857A
Cited
US3841933A
Cited
US3673295A
Cited
US3692618A
Cited
US3669788A
Cited
DE1965054A1
Cited
US3803284A
Cited
US3776796A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-08-17 | 1980-02-16 | 1980-08-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-08-17 | 1984-02-16 | 1984-08-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-08-17 | 1988-02-16 | 1988-08-17 | $7700.00 | Window Closed / Lapsed |