Thermoplastic elastomer compositions

Assignee: ExxonMobil Technology and Engineering Co
•
Filing: 1974-11-18
•
Granted: 1976-08-10
•
Expires: 1994-11-18
📄 Original PDF 🌐 Google Patents 🔄 Sync Now

Abstract

Abstract This invention relates to processable ionic elastomer compositions having improved compression set properties, especially at elevated temperatures. In this invention an intractable ionic elastomer, for example, a sulfonated elastomer is blended with from 10 to 70 parts per hundred of a crystalline polyolefin to yield novel compositions having the above properties. Preferably the ionic elastomer is a sulfonated ethylene propylene terpolymer having from about 0.2 to 20 mole percent sulfonate groups, at least 95% of which are combined with counterions selected from the group consisting of Groups IA, IIA, IB, and IIB of the Periodic Table of Elements, aluminum, antimony, lead, and mixtures thereof. The sulfonated polymer is combined with said counterions by neutralization of a polysulfonic acid precurser with a basic material in which the desired counterion is present as the cation thereof. The anion of said basic material is preferably selected from the group consisting of oxide, hydroxide, and lower alkanoates, for example, acetate, formate, and propionate.

Inventors

  • 👤 Jan Bock
  • 👤 Robert D. Lundberg
  • 👤 Robert R. Phillips
  • 👤 Henry S. Makowski

Bibliographic Details

Application Number —
Jurisdiction US
Data Source google_patents
Last Synchronized 2026-10-26 20:53
CPC Classifications
C; C08; C08L; C08L23/00; C08L23/26; C08L23/32

Claims Analysis

Total Claims: 13
Claim 1
Independent Claim 84 words
A composition of matter which comprises a blend of an intractable ionic elastomer, said elastomer consists essentially of sulfonated nonaromatic hydrocarbon polymers, said elastomer comprising a continuous phase of said blend and said elastomer being characterized as having a shear stress as measured at a shear rate of 0.74 sec.sup. -1 of at least 1 × 10 6 dynes/cm 2 at 200°C, and from 10 to 90 parts per hundred elastomer of a crystalline polyolefin having a degree of crystallinity of at least 25%.
Claim 2
Dependent Claim 84 words
A composition of matter which comprises a blend of an intractable ionic elastomer, said elastomer consists essentially of sulfonated nonaromatic hydrocarbon polymers, said elastomer comprising a continuous phase of said blend and said elastomer being characterized as having a shear stress as measured at a shear rate of 0.74 sec.sup. -1 of at least 1 × 10 6 dynes/cm 2 at 200°C, and from 10 to 90 parts per hundred elastomer of a crystalline polyolefin having a degree of crystallinity of at least 25%.
Claim 3
Dependent Claim 52 words
Composition of claim 1 wherein said sulfonated polymer comprises from about 0.2 to about 20 mole % sulfonate groups at least 95% of which are combined with a counterion selected from the group consisting of Groups I and II of the Periodic Table of the Elements, aluminum, zinc, lead and mixtures thereof.
Claim 4
Dependent Claim 20 words
The composition of claim 2 wherein said sulfonated polymer comprises from about 0.2 to about 5.0 mole % sulfonate groups.
Claim 5
Dependent Claim 30 words
Composition of claim 2 wherein said crystalline polyolefin is selected from the group consisting of polyethylene, polypropylene, and ethylene propylene copolymers, having a degree of crystallinity of at least 40%.
Claim 6
Dependent Claim 50 words
The composition of claim 2 wherein said sulfonated elastomer is prepared by neutralizing a sulfonic acid polymer with a basic material wherein the cation is selected from the group consisting of Groups IA, IB, IIA, and IIB of the Periodic Table of the Elements, aluminum, antimony, lead and mixtures thereof.
Claim 7
Dependent Claim 23 words
Composition of claim 2 wherein said crystalline polyolefin is added at a level of from 20 to 90 parts per hundred sulfonated elastomer.
Claim 8
Dependent Claim 22 words
Composition of claim 2 wherein said sulfonated polymer is selected from the group consisting of sulfonated butyl polymers and sulfonated ethylene-propylene terpolymers.
Claim 9
Dependent Claim 13 words
Composition of claim 7 wherein said sulfonated polymer is a sulfonated ethylene-propylene terpolymer.
Claim 10
Dependent Claim 16 words
Composition of claim 8 wherein said crystalline polyolefin has a melting point of at least 70°C.
Claim 11
Dependent Claim 10 words
Composition of claim 9 wherein said crystalline polyolefin is polypropylene.
Claim 12
Dependent Claim 11 words
The composition of claim 9 wherein the crystalline polyolefin is polyethylene.
Claim 13
Dependent Claim 11 words
The composition of claim 9 wherein said crystalline polyolefin is polybutene-l.

References Cited (Backward Citations)

US3642728A Cited
US3758643A Cited

USPTO Annuity & Maintenance Windows

Annuity Stage Window Opens Payment Deadline Surcharge Period Until Estimated Fee Status
3.5 Years (Year 4) 1979-08-10 1980-02-09 1980-08-10 $2000.00 Window Closed / Lapsed
7.5 Years (Year 8) 1983-08-10 1984-02-09 1984-08-10 $3760.00 Window Closed / Lapsed
11.5 Years (Year 12) 1987-08-10 1988-02-09 1988-08-10 $7700.00 Window Closed / Lapsed

Assigned Categories & Tags

No categories assigned to this patent yet.

Assign Category Tag