Low carbon calcium-sulfur containing free-cutting steel
Assignee: Daido Steel Co Ltd
•
Filing: 1975-09-12
•
Granted: 1976-08-10
•
Expires: 1995-09-12
Abstract
Abstract Low carbon calcium-sulfur containing free-cutting steel exhibiting improved machinability is disclosed. The said steel consists essentially of 0.03 to 0.10% carbon, up to 0.3% silicon, 0.8 to 1.5% manganese, 0.04 to 0.10% phosphorus, 0.20 to 0.45% sulfur, 0.0003 to 0.0050% calcium and the remainder being iron and inherent impurities such as copper, nickel, chromium and nitrogen; and is prepared by regulating the composition of the steel so that the value of theoretical Brinell hardness of the steel matrix, which is determined on the basis of the content of carbon, silicon, manganese, phosphorus, sulfur, copper, nickel, chromium and nitrogen in the steel, to a value between 110 and 130, and by forming and maintaining in the range of from 100 to 500 grams per steel-ton oxide inclusions of type JIS-A2 (ASTM-C) which soften or fuse at a temperature not higher than 1400°C.
Inventors
- 👤 Tetsuro Itoh
- 👤 Tetsuo Takahashi
- 👤 Kiyoichi Yamano
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 17:28
CPC Classifications
C; C22; C22C; C22C38/00; C22C38/60
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
183 words
A low-carbon calcium-sulfur containing free-cutting steel, which consists essentially of 0.03 to 0.10% carbon, up to 0.3% silicon, 0.8 to 1.5% manganese, 0.04 to 0.10% phosphorus, 0.20 to 0.45% sulfur, and 0.0003 to 0.0050% calcium, 0 to 0.25% lead, 0 to 0.10% telurium, 0 to 0.15% bismuth, 0 to 0.2% tin, 0 to 0.2% zinc, 0 to 0.2% arsenic, 0 to 0.2% thallium, and the remainder being iron and impurities; and which may contain copper, nickel chromium and nitrogen as impurities; wherein the content of carbon, silicon, manganese, phosphorus, sulfur, copper, nickel, chromium and nitrogen is regulated within the above ranges so that the value of theoretical Brinell hardness (BHN) of the steel matrix defined by the formula: BHN = 70 + 230[%C] + 560[%N] + 112[%P] + 33[%Si] + 23[%Mn] + 8[%Ni] + 8[%Cu] + 7[%Cr] - 39[%S] falls in the range of 110 to 130; and, wherein the said steel contains in the range of from 100 to 500 grams per steel-ton of oxide inclusions principally of type JIS -A2 (ASTM-C) softening or fusing at a temperature not higher than 1400°C.
Claim 2
Dependent Claim
183 words
A low-carbon calcium-sulfur containing free-cutting steel, which consists essentially of 0.03 to 0.10% carbon, up to 0.3% silicon, 0.8 to 1.5% manganese, 0.04 to 0.10% phosphorus, 0.20 to 0.45% sulfur, and 0.0003 to 0.0050% calcium, 0 to 0.25% lead, 0 to 0.10% telurium, 0 to 0.15% bismuth, 0 to 0.2% tin, 0 to 0.2% zinc, 0 to 0.2% arsenic, 0 to 0.2% thallium, and the remainder being iron and impurities; and which may contain copper, nickel chromium and nitrogen as impurities; wherein the content of carbon, silicon, manganese, phosphorus, sulfur, copper, nickel, chromium and nitrogen is regulated within the above ranges so that the value of theoretical Brinell hardness (BHN) of the steel matrix defined by the formula: BHN = 70 + 230[%C] + 560[%N] + 112[%P] + 33[%Si] + 23[%Mn] + 8[%Ni] + 8[%Cu] + 7[%Cr] - 39[%S] falls in the range of 110 to 130; and, wherein the said steel contains in the range of from 100 to 500 grams per steel-ton of oxide inclusions principally of type JIS -A2 (ASTM-C) softening or fusing at a temperature not higher than 1400°C.
Claim 3
Dependent Claim
27 words
A low-carbon calcium-sulfur containing free-cutting steel according to claim 1, wherein the content of sulfur is 0.25 to 0.45% and the content of calcium 0.0003 to 0.0030%.
Claim 4
Dependent Claim
44 words
A low-carbon calcium-sulfur containing free-cutting steel according to claim 1, wherein the content of sulfur is 0.25 to 0.4%, the content of calcium 0.0003 to 0.0020%, and the content of the oxide inclusion in the range of from 200 to 400 grams per steel-ton.
Claim 5
Dependent Claim
153 words
A low-carbon calcium-sulfur containing free-cutting steel, which consists essentially of 0.03 to 0.10% carbon, up to 0.3% silicon, 0.8 to 1.5% manganese, 0.04 to 0.10% phosphorus, 0.20 to 0.45% sulfur, 0.0003 to 0.0050% calcium, and the remainder being iron and impurities; and which may contain copper, nickel, chromium and nitrogen as impurities; wherein the content of carbon, silicon, manganese, phosphorus, sulfur, copper, nickel, chromium and nitrogen is regulated within the above ranges so that the value of theoretical Brinell hardness (BHN) in the steel matrix defined by the formula: BHN = 70 + 230[%C] + 560[%N] + 112[%P] + 33[%Si] + 23[%Mn] + 8[%Ni] + 8[%Cu] + 7[%Cr] - 39[%S] falls in the range of 110 to 130; and wherein the said steel contains in the range of from 100 to 500 grams per steel-ton of oxide inclusions principally of type JIS-A2 (ASTM-C) softening or fusing at a temperature not higher than 1400°C.
Claim 6
Dependent Claim
153 words
A low-carbon calcium-sulfur containing free-cutting steel, which consists essentially of 0.03 to 0.10% carbon, up to 0.3% silicon, 0.8 to 1.5% manganese, 0.04 to 0.10% phosphorus, 0.20 to 0.45% sulfur, 0.0003 to 0.0050% calcium, and the remainder being iron and impurities; and which may contain copper, nickel, chromium and nitrogen as impurities; wherein the content of carbon, silicon, manganese, phosphorus, sulfur, copper, nickel, chromium and nitrogen is regulated within the above ranges so that the value of theoretical Brinell hardness (BHN) in the steel matrix defined by the formula: BHN = 70 + 230[%C] + 560[%N] + 112[%P] + 33[%Si] + 23[%Mn] + 8[%Ni] + 8[%Cu] + 7[%Cr] - 39[%S] falls in the range of 110 to 130; and wherein the said steel contains in the range of from 100 to 500 grams per steel-ton of oxide inclusions principally of type JIS-A2 (ASTM-C) softening or fusing at a temperature not higher than 1400°C.
Claim 7
Dependent Claim
27 words
A low-carbon calcium-sulfur containing free-cutting steel according to claim 4, wherein the content of sulfur is 0.25 to 0.45% and the content of calcium 0.0003 to 0.0030%.
Claim 8
Dependent Claim
44 words
A low-carbon calcium-sulfur containing free-cutting steel according to claim 4, wherein the content of sulfur is 0.25 to 0.40%, the content of calcium 0.0010 to 0.0020%, and the content of the oxide inclusions in the range of from 200 to 400 grams per steel-ton.
Claim 9
Dependent Claim
173 words
A low-carbon calcium-sulfur containing free-cutting steel, which consists essentially of 0.03 to 0.10% carbon, up to 0.3% silicon, 0.8 to 1.5% manganese, 0.04 to 0.10% phosphorus, 0.20 to 0.45% sulfur, 0.0003 to 0.0050% calcium and at least one of 0.05 to 0.25% lead, 0.02 to 0.10% telurium and 0.02 to 0.15% bismuth (total amount of Pb, Te and Bi being up to 0.25%), the remainder being iron and impurities; and which may contain copper, nickel, chromium and nitrogen as impurities; wherein the content of carbon, silicon, manganese, phosphorus, sulfur, copper, nickel, chromium and nitrogen is regulated within the above ranges so that the value of theoretical Brinell hardness (BHN) in the steel matrix defined by the formula: BHN = 70 + 230[%C]+ 560[%N]+ 112[%P] + 33[%Si]+ 23[%Mn]+ 8[%Ni]+ 8[%Cu]+ 7[%Cr]-39[%S] falls in the range of 110 to 130; and wherein the said steel contains in the range of from 100 to 500 grams per steel-ton of oxide inclusions principally of type JIS-A2 (ASTM-C) softening or fusing at a temperature not higher than 1400°C.
Claim 10
Dependent Claim
173 words
A low-carbon calcium-sulfur containing free-cutting steel, which consists essentially of 0.03 to 0.10% carbon, up to 0.3% silicon, 0.8 to 1.5% manganese, 0.04 to 0.10% phosphorus, 0.20 to 0.45% sulfur, 0.0003 to 0.0050% calcium and at least one of 0.05 to 0.25% lead, 0.02 to 0.10% telurium and 0.02 to 0.15% bismuth (total amount of Pb, Te and Bi being up to 0.25%), the remainder being iron and impurities; and which may contain copper, nickel, chromium and nitrogen as impurities; wherein the content of carbon, silicon, manganese, phosphorus, sulfur, copper, nickel, chromium and nitrogen is regulated within the above ranges so that the value of theoretical Brinell hardness (BHN) in the steel matrix defined by the formula: BHN = 70 + 230[%C]+ 560[%N]+ 112[%P] + 33[%Si]+ 23[%Mn]+ 8[%Ni]+ 8[%Cu]+ 7[%Cr]-39[%S] falls in the range of 110 to 130; and wherein the said steel contains in the range of from 100 to 500 grams per steel-ton of oxide inclusions principally of type JIS-A2 (ASTM-C) softening or fusing at a temperature not higher than 1400°C.
Claim 11
Dependent Claim
27 words
A low-carbon calcium-sulfur containing free-cutting steel according to claim 7, wherein the content of sulfur is 0.25 to 0.45% and the content of calcium 0.0003 to 0.0030%.
Claim 12
Dependent Claim
44 words
A low-carbon calcium-sulfur containing free-cutting steel according to claim 7, wherein the content of sulfur is 0.25 to 0.40%, the content of calcium 0.0010 to 0.0020%, and the content of the oxide inclusions in the range of from 200 to 400 grams per steel-ton.
Claim 13
Dependent Claim
174 words
A low-carbon calcium-sulfur containing free-cutting steel which consists essentially of 0.03 to 0.10 carbon, up to 0.3% silicon, 0.8 to 1.5% manganese, 0.04 to 0.10% phosphorus, 0.20 to 0.45% sulfur, 0.0003 to 0.0050% calcium, at least one of 0.05 to 0.2% tin, 0.05 to 0.2% zinc, 0.05 to 0.2% arsenic and 0.05 to 0.2% thallium (total amount of Sn, Z, As and Tl; being up tp 0.25%), the remainder being iron and impurities; and which may contain copper, nickel, chromium and nitrogen as impurities; wherein content of carbon, silicon, manganese, phosphorus, sulfur, copper, nickel, chromium and nitrogen is regulated within the above ranges so that the value of theoretical Brinell hardness (BHN) in the steel matrix defined by the formula: BHN = 70 + 230[%C]+ 560[%N]+ 112[%P]+ 33[%Si]+ 23[%Mn]+ 8[%Ni]+8[%Cu]+ 7[%Cr]-39[%S] falls in the range of 110 to 130; and wherein the said steel contains in the range of from 100 to 500 grams per steel-ton of oxide inclusions principally of type JIS-A2 (ASTM-C) softening or fusing at a temperature not higher than 1400°C.
Claim 14
Dependent Claim
174 words
A low-carbon calcium-sulfur containing free-cutting steel which consists essentially of 0.03 to 0.10 carbon, up to 0.3% silicon, 0.8 to 1.5% manganese, 0.04 to 0.10% phosphorus, 0.20 to 0.45% sulfur, 0.0003 to 0.0050% calcium, at least one of 0.05 to 0.2% tin, 0.05 to 0.2% zinc, 0.05 to 0.2% arsenic and 0.05 to 0.2% thallium (total amount of Sn, Z, As and Tl; being up tp 0.25%), the remainder being iron and impurities; and which may contain copper, nickel, chromium and nitrogen as impurities; wherein content of carbon, silicon, manganese, phosphorus, sulfur, copper, nickel, chromium and nitrogen is regulated within the above ranges so that the value of theoretical Brinell hardness (BHN) in the steel matrix defined by the formula: BHN = 70 + 230[%C]+ 560[%N]+ 112[%P]+ 33[%Si]+ 23[%Mn]+ 8[%Ni]+8[%Cu]+ 7[%Cr]-39[%S] falls in the range of 110 to 130; and wherein the said steel contains in the range of from 100 to 500 grams per steel-ton of oxide inclusions principally of type JIS-A2 (ASTM-C) softening or fusing at a temperature not higher than 1400°C.
Claim 15
Dependent Claim
27 words
A low-carbon calcium-sulfur containing free-cutting steel according to claim 10, wherein the content of sulfur is 0.25 to 0.45% and the content of calcium 0.0003 to 0.0030%.
Claim 16
Dependent Claim
40 words
A low-carbon calcium-sulfur containing free-cutting steel according to claim 10, wherein the content of sulfur is 0.25 to 0.40%, the content of calcium 0.0010 to 0.0020%, and the content of the oxide inclusions from 200 to 400 grams per steel-ton.
Claim 17
Dependent Claim
203 words
A low-carbon calcium-sulfur containing free-cutting steel which consists essentially of 0.03 to 0.10% carbon, up to 0.3% silicon, 0.8 to 1.5% manganese, 0.04 to 0.10% phosphorus, 0.20 to 0.45% sulfur, 0.0003 to 0.0050% calcium, and at least one of 0.05 to 0.25% lead, 0.02 to 0.10% telurium and 0.02 to 0.15% bismuth (total amount of Pb, Te and Bi: being up to 0.25%), and at least one of 0.05 to 0.2% tin, 0.05 to 0.2% zinc, 0.05 to 0.2% arsenic and 0.05 to 0.2% thallium (total amount of Sn, Zn, As and Tl: being up to 0.25%) and the remainder being iron and impurities; and which may contain copper, nickel, chromium and nitrogen as impurities; wherein content of carbon, silicon, manganese, phosphorus, sulfur, copper, nickel, chromium and nitrogen is regulated within the above ranges so that the value of theoretical Brinell hardness (BHN) defined by the formula: BHN = 70 + 230[%C]+ 560[%N]+ 112[%P]+ 33[%Si]+ 23 [%Mn]+ 8[% Ni]+ 8[%Cu]+ 7[%Cr]-39[%S] falls in the range of 110 to 130; and wherein the said steel contains in the range of 100 to 500 grams per steel-ton of oxide inclusions principally of type JIS-A2 (ASTM-C) softening or fusing at a temperature not higher than 1400°C.
Claim 18
Dependent Claim
203 words
A low-carbon calcium-sulfur containing free-cutting steel which consists essentially of 0.03 to 0.10% carbon, up to 0.3% silicon, 0.8 to 1.5% manganese, 0.04 to 0.10% phosphorus, 0.20 to 0.45% sulfur, 0.0003 to 0.0050% calcium, and at least one of 0.05 to 0.25% lead, 0.02 to 0.10% telurium and 0.02 to 0.15% bismuth (total amount of Pb, Te and Bi: being up to 0.25%), and at least one of 0.05 to 0.2% tin, 0.05 to 0.2% zinc, 0.05 to 0.2% arsenic and 0.05 to 0.2% thallium (total amount of Sn, Zn, As and Tl: being up to 0.25%) and the remainder being iron and impurities; and which may contain copper, nickel, chromium and nitrogen as impurities; wherein content of carbon, silicon, manganese, phosphorus, sulfur, copper, nickel, chromium and nitrogen is regulated within the above ranges so that the value of theoretical Brinell hardness (BHN) defined by the formula: BHN = 70 + 230[%C]+ 560[%N]+ 112[%P]+ 33[%Si]+ 23 [%Mn]+ 8[% Ni]+ 8[%Cu]+ 7[%Cr]-39[%S] falls in the range of 110 to 130; and wherein the said steel contains in the range of 100 to 500 grams per steel-ton of oxide inclusions principally of type JIS-A2 (ASTM-C) softening or fusing at a temperature not higher than 1400°C.
Claim 19
Dependent Claim
27 words
A low-carbon calcium-sulfur containing free-cutting steel according to claim 13, wherein the content of sulfur is 0.25 to 0.45% and the content of calcium 0.0003 to 0.0030%.
Claim 20
Dependent Claim
27 words
A low-carbon calcium-sulfur containing free-cutting steel according to claim 13, wherein the content of sulfur is 0.25 to 0.45% and the content of calcium 0.0003 to 0.0030%.
Claim 21
Dependent Claim
40 words
A low-carbon calcium-sulfur containing free-cutting steel according to claim 13, wherein the content of sulfur is 0.25 to 0.40%, the content of calcium 0.0010 to 0.0020%, and the content of the oxide inclusions from 200 to 400 grams per steel-ton.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-08-10 | 1980-02-09 | 1980-08-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-08-10 | 1984-02-09 | 1984-08-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-08-10 | 1988-02-09 | 1988-08-10 | $7700.00 | Window Closed / Lapsed |