Glass fiber material having strength retention in a moist environment

Claim 2

In a glass fiber bundle suitable for reinforcing a host elastomeric material comprising: a bundle of sized glass fibers having disposed about and throughout the bundle a coating composition containing a phenolic resin and an elastomer selected from the group consisting of styrene-butadiene-vinylpyridine terpolymers and styrene butadiene copolymers as essential ingredients, the improvement comprising: said coating composition having therein a treated diatomaceous earth selected from the group consisting of magnesium silicate and calcium silicate diatomaceous earths in an amount effective to provide for substantially retained tensile strength of the glass fiber bundle after exposure to a moist environment of 95 percent relative humidity and about 100° F. for a period of at least 8 days, and wherein said coated glass fiber bundle contains no 2,6-ditert-butyl-4-phenylphenol therein.

Claim 3

The glass fiber bundle of claim 1 wherein the phenolic resin of said coating composition is selected from the group consisting of resorcinol-formaldehyde resin, phenol-formaldehyde resin and mixtures thereof.

Claim 4

The glass fiber bundle of claim 1 wherein the diatomaceous earth is present from about 0.02 to about 2.0 percent by weight of the phenolic resin and elastomer containing coating composition.

Claim 5

The glass fiber bundle of claim 1 wherein the coating composition is present from about 15 to about 40 percent by weight of the glass in the bundle.

Claim 6

The glass fiber bundle of claim 1 wherein the coating composition further comprises a microcrystalline wax.

Claim 7

An elastomeric material reinforced with the glass fiber bundle of claim 1.

Claim 8

In the preparation of phenolic resin and elastomer coated glass fiber materials for rubber reinforecement, wherein said elastomer is selected from the group consisting of styrene-butadiene-vinyl pyridine terpolymers and styrene-butadiene copolymers, wherein said coated glass fiber material contains no 2,6-ditert-butyl-4-phenyl-phenol therein and further, wherein the coated materials are subject to degradation under conditions of high humidity and high ambient temperature the improvement whereby the degradation is retarded comprising coating the glass fiber material with a phenolic resin and elastomer containing coating composition having therein as an essential ingredient, a treated diatomaceous earth selected from the group consisting of magnesium silicate and calcium silicate diatomaceous earths in an efective amount to retard the degradation of said glass fiber coated material after said material is exposed to a moist environment of 95 percent relative humidity at about 100° F. for a period of at least 8 days.

Claim 9

In the preparation of phenolic resin and elastomer coated glass fiber materials for rubber reinforecement, wherein said elastomer is selected from the group consisting of styrene-butadiene-vinyl pyridine terpolymers and styrene-butadiene copolymers, wherein said coated glass fiber material contains no 2,6-ditert-butyl-4-phenyl-phenol therein and further, wherein the coated materials are subject to degradation under conditions of high humidity and high ambient temperature the improvement whereby the degradation is retarded comprising coating the glass fiber material with a phenolic resin and elastomer containing coating composition having therein as an essential ingredient, a treated diatomaceous earth selected from the group consisting of magnesium silicate and calcium silicate diatomaceous earths in an efective amount to retard the degradation of said glass fiber coated material after said material is exposed to a moist environment of 95 percent relative humidity at about 100° F. for a period of at least 8 days.