Process of applying non-adhesive coatings to plastics
Assignee: BASF SE
•
Filing: 1974-07-01
•
Granted: 1976-08-03
•
Expires: 1994-07-01
Abstract
Abstract A process for coating moldings of plastics which tend to stick together at room temperature by applying solutions containing a nonadhesive resin of (1) a copolymer of at least one member of the group consisting of styrene and methylstyrene and a monoester of at least one member of the group consisting of maleic and fumaric acid or (2) a reaction product of at least one member of the group consisting of cyclohexanone and methylcyclohexanone with formaldehyde or acetaldehyde, said non-adhesive resin having a monoscope yield point or more than 80°C. and a ball indentation hardness of from 310 to 800 kp/cm 2 at 10 seconds and thereafter evaporating the solvent at a temperature which is lower than the softening point of the material to be coated.
Inventors
- 👤 Heinz Mueller-Tamm
- 👤 Oskar Buechner
- 👤 Volker Gierth
- 👤 Karl-Heinz Fauth
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 01:03
CPC Classifications
C; C08; C08J; C08J3/00; C08J3/12; C08J3/124; B; B29; B29B; B29B9/00; B29B9/16; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2982; Y10T428/2991; Y10T428/2993; Y10T428/2996; Y10T428/2998
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
194 words
A process for coating plastics which tend to agglomerate at ambient temperature selected from the group consisting of copolymers of ethylene which contain more than 20% by weight of polymerized units of a polar ethylenically unsaturated compound, polyisobutylene having a viscosity average molecular weight of from 3 × 10 5 to 6 × 10 6 and mixtures of bitumen and ethylene copolymers by applying to them a solution consisting essentially of a nonadhesive resin and a solvent having a temperature of from about 50° to 110°C and evaporating the solvent at a temperature which is lower than the softening point of the plastics to be coated, wherein said nonadhesive resin consists of 1. a copolymer of at least one member of the group consisting of styrene and methylstyrene and a monoester of at least one member of the group consisting of maleic and fumaric acid or 2. a reaction product of at least one member of the group consisting of cyclohexanone and methylcyclohexanone with formaldehyde or acetaldehyde, said nonadhesive resin having a monoscope yield point of more than 80°C and a ball indentation hardness of from 310 to 800 kp/cm 2 at 10 seconds.
Claim 2
Dependent Claim
194 words
A process for coating plastics which tend to agglomerate at ambient temperature selected from the group consisting of copolymers of ethylene which contain more than 20% by weight of polymerized units of a polar ethylenically unsaturated compound, polyisobutylene having a viscosity average molecular weight of from 3 × 10 5 to 6 × 10 6 and mixtures of bitumen and ethylene copolymers by applying to them a solution consisting essentially of a nonadhesive resin and a solvent having a temperature of from about 50° to 110°C and evaporating the solvent at a temperature which is lower than the softening point of the plastics to be coated, wherein said nonadhesive resin consists of 1. a copolymer of at least one member of the group consisting of styrene and methylstyrene and a monoester of at least one member of the group consisting of maleic and fumaric acid or 2. a reaction product of at least one member of the group consisting of cyclohexanone and methylcyclohexanone with formaldehyde or acetaldehyde, said nonadhesive resin having a monoscope yield point of more than 80°C and a ball indentation hardness of from 310 to 800 kp/cm 2 at 10 seconds.
Claim 3
Dependent Claim
19 words
A process as claimed in claim 1 wherein the boiling point of the solvent is from 60° to 90°C.
Claim 4
Dependent Claim
22 words
A process as claimed in claim 1 wherein the solution of the nonadhesive resin has a viscosity of 2 to 100 centistokes.
Claim 5
Dependent Claim
15 words
A process as claimed in claim 1 wherein the plastics to be coated are granules.
Claim 6
Dependent Claim
54 words
A process as claimed in claim 1 wherein the solution of the resin contains an inorganic substance having a particle size of less than 100 microns dispersed therein, said inorganic substance being selected from the group consisting of silicon dioxide, calcium carbonate, talc, mica, glass microspherules, kaolin, carbon black, coal dust and graphite dust.
Claim 7
Dependent Claim
29 words
A process as claimed in claim 5 wherein the inorganic substance is used in an amount of from 0.1 to 2% by weight of the material to be coated.
Claim 8
Dependent Claim
57 words
A process as claimed in claim 1 wherein the non-adhesive resin contains from 45 to 55 parts by weight of at least one member of the group consisting of styrene and methylstyrene and from 60 to 70 parts by weight of a monoester of at least one member of the group consisting of maleic and fumaric acid.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-08-03 | 1980-02-02 | 1980-08-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-08-03 | 1984-02-02 | 1984-08-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-08-03 | 1988-02-02 | 1988-08-03 | $7700.00 | Window Closed / Lapsed |