Abstract A system is proposed for the purification of exhaust gases from internal combustion engines, preferably the reduction of nitrogen oxides in exhaust gases from internal combustion engines in which nitrogen is selectively formed as substantially the only nitrogen-containing product. The exhaust gas is contacted at an elevated temperature with a noble metal in a reducing atmosphere, wherein nitrogen oxides are selectively converted to nitrogen as substantially the only nitrogen containing product, and/or is contacted with a noble metal in an oxidizing atmosphere, wherein carbon monoxide and unburned hydrocarbons are converted to carbon dioxide and water, said noble metal being distended on a microporous glass body. In a preferred embodiment the exhaust gas is contacted at an elevated temperature in a reducing atmosphere with ruthenium supported on a microporous glass body comprising a leached, phase-separated alkali borosilicate.
A microporous glass body suitable for converting nitrogen oxides in auto exhaust gases at low temperatures without the formation of appreciable amounts of ammonia carrying substantially solely ruthenium, said glass body consisting essentially of the following composition: Component Weight Per Cent
______________________________________
SiO.sub.2 80-97
B.sub.2 O.sub.3 3-15
K.sub.2 O
0.3-1
Na.sub.2 O
Al.sub.2 O.sub.3 0.3-1.5
______________________________________ wherein the surface area of said glass body is in the range of about 40 to about 300 square meters per gram, with the pore radius thereof being from about 10 to about 70 A, the ruthenium being distended on said glass body and covering about 20 to about 0.3 per cent of the surface thereof with a thickness of about 1 to about 10 monomolecular layers of said metal.
Claim 2
Dependent Claim
126 words
A microporous glass body suitable for converting nitrogen oxides in auto exhaust gases at low temperatures without the formation of appreciable amounts of ammonia carrying substantially solely ruthenium, said glass body consisting essentially of the following composition: Component Weight Per Cent
______________________________________
SiO.sub.2 80-97
B.sub.2 O.sub.3 3-15
K.sub.2 O
0.3-1
Na.sub.2 O
Al.sub.2 O.sub.3 0.3-1.5
______________________________________ wherein the surface area of said glass body is in the range of about 40 to about 300 square meters per gram, with the pore radius thereof being from about 10 to about 70 A, the ruthenium being distended on said glass body and covering about 20 to about 0.3 per cent of the surface thereof with a thickness of about 1 to about 10 monomolecular layers of said metal.
Claim 3
Dependent Claim
28 words
The glass body of claim 1 wherein the surface area of the glass body is in the range of about 60 to about 200 square meters per gram.
Claim 4
Dependent Claim
21 words
The glass body of claim 1 wherein the pore radius is within the range of about 16 to about 50 A.
Claim 5
Dependent Claim
23 words
The glass body of claim 1 wherein the glass body is spherical and has a diameter of about 1/16 to about 1/2 inch.
Claim 6
Dependent Claim
23 words
The glass body of claim 1 wherein the glass body is spherical and has a diameter of about 1/8 to about 1/4 inch.
Claim 7
Dependent Claim
27 words
The glass body of claim 1 wherein the weight per cent of metal on the glass body is in the range of about 0.03 to about 2.0.
Claim 8
Dependent Claim
30 words
The glass body of claim 1 wherein the weight per cent of metal on the glass body is in the range of about 0.05 to about one weight per cent.