Alumina-zircon bond for refractory grains
Assignee: Valley Mineral Products Corp
•
Filing: 1974-03-04
•
Granted: 1976-08-03
•
Expires: 1994-03-04
Abstract
Abstract This disclosure concerns a thermo-chemical bonded refractory product which comprises inactive refractory grains bonded together by mullite. The refractory is emplaced in a furnace or other pyro-processing unit by pressing, ramming, gunning, casting, etc. The refractory product is made by mixing inactive refractory grains with a mixture of zircon and alumina powders and a small amount of an alkaline earth oxide catalyst. The catalyst breaks the zircon down into ZrO 2 and SiO 2 at relatively low temperatures. The SiO 2 thus liberated is unusually reactive and reacts with the alumina to form mullite and the ZrO 2 adsorbs the alkaline earth oxide.
Inventors
- 👤 John P. Holt
- 👤 Theodore Paul Cash
- 👤 Delbert E. Day
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 00:37
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/01; C04B35/10; C04B35/101; C04B35/106
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
69 words
A refractory composition comprising: A. from about 30% to about 80% inactive refractory grain aggregate, B. from about 6% to about 20% zircon, C. from about 0.5% to about 10% alkaline earth oxide catalyst, D. from about 5% to about 45% alumina, and E. finely ground silica in amount sufficient to prevent formation of low melting alumina-zircon compounds, said silica being present in amount of at least about 5%.
Claim 2
Dependent Claim
69 words
A refractory composition comprising: A. from about 30% to about 80% inactive refractory grain aggregate, B. from about 6% to about 20% zircon, C. from about 0.5% to about 10% alkaline earth oxide catalyst, D. from about 5% to about 45% alumina, and E. finely ground silica in amount sufficient to prevent formation of low melting alumina-zircon compounds, said silica being present in amount of at least about 5%.
Claim 3
Dependent Claim
31 words
The composition of claim 1 wherein the zircon is about 90% to about 100% smaller than 200 mesh and the alumina is about 90% to about 100% smaller than 325 mesh.
Claim 4
Dependent Claim
28 words
The composition of claim 1 wherein the inactive refractory grain is selected from the group consisting of zirconia, fused zirconia-alumina-silica, pyrophyllite, fused alumina, fused mullite and mixtures thereof.
Claim 5
Dependent Claim
23 words
The composition of claim 1 wherein the alkaline earth oxide catalyst is selected from the group consisting of magnesium oxide and calcium oxide.
Claim 6
Dependent Claim
25 words
The composition of claim 2 wherein the amounts of alumina and zircon are selected to provide an alumina-silica molar ratio of about 3 to 2.
Claim 7
Independent Claim
133 words
A method of making a chemically bonded refractory object comprising the steps of a. combining about 30% to about 80% inactive aggregate refractory grains, about 6% to about 20% zircon, about 5% to about 45% alumina, finely ground silica in amount sufficient to prevent formation of low melting alumina-zircon compounds, said silica being present in amount of at least about 5%, and about 0.5% to about 10% alkaline earth oxide catalyst with a binder, b. forming the mixture into a refractory object and heating at a temperature below the melting point of mullite and for a time sufficient so that the zircon degrades under the catalytic action of the alkaline earth oxide to yield zirconia and silica and said silica combines with the alumina present in the mixture to form a mullite bond.
Claim 8
Independent Claim
133 words
A method of making a chemically bonded refractory object comprising the steps of a. combining about 30% to about 80% inactive aggregate refractory grains, about 6% to about 20% zircon, about 5% to about 45% alumina, finely ground silica in amount sufficient to prevent formation of low melting alumina-zircon compounds, said silica being present in amount of at least about 5%, and about 0.5% to about 10% alkaline earth oxide catalyst with a binder, b. forming the mixture into a refractory object and heating at a temperature below the melting point of mullite and for a time sufficient so that the zircon degrades under the catalytic action of the alkaline earth oxide to yield zirconia and silica and said silica combines with the alumina present in the mixture to form a mullite bond.
Claim 9
Dependent Claim
26 words
The method of claim 6 wherein the inactive refractory grain is selected from the group consisting of zirconia, fused zirconia-alumina-silica, pyrophyllite, fused alumina and fused mullite.
Claim 10
Dependent Claim
23 words
The method of claim 6 wherein the alkaline earth oxide catalyst is selected from the group consisting of magnesium oxide and calcium oxide.
References Cited (Backward Citations)
US2830348A
Cited
US2842447A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-08-03 | 1980-02-02 | 1980-08-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-08-03 | 1984-02-02 | 1984-08-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-08-03 | 1988-02-02 | 1988-08-03 | $7700.00 | Window Closed / Lapsed |