Copper base alloys
Assignee: Materion Brush Inc
•
Filing: 1975-02-27
•
Granted: 1976-08-03
•
Expires: 1995-02-27
Abstract
Abstract Copper-base alloys are disclosed which are characterized by unusually low melting points combined with good tensile strength and ductility in the as-cast condition, excellent founding characteristics, high hardness and strength in the as-cast plus heat treated condition, ability to be used as brazing alloys, and excellent wrought characteristics. These alloys can possess an attractive pale gold or silvery appearance as cast in sand, permanent mold and investment mold, and comprise the following constituents in the ranges and ratios specified: Percent by Weight Manganese 12 to 36 Zinc 4 to 28 Beryllium 0.10 to 1.00 Copper 50.0 + (10 × Be content) to 58.0 + (14 × Be content). Up to 2% lead may be usefully incorporated in these alloys to improve machinability.
Inventors
- 👤 Patrick D. Renschen
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 23:57
CPC Classifications
C; C22; C22C; C22C9/00; C22C9/04; C22C9/05
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
75 words
A heat-treated copper-base alloy article consisting essentially of the following constituents in the proportions and ratios specified: Percent by weight
Manganese 12 to 36
Zinc 4 to 28
Beryllium 0.10 to 1.00
Copper 50.0 + (10 × Be content)
58.0 + (14 × Be content), and such that the manganese-to-zinc ratio is between 0.4 and 10, said alloy article having excellent founding characteristics, ability to replicate mold surfaces with great detail, and improved mechanical properties.
Claim 2
Dependent Claim
75 words
A heat-treated copper-base alloy article consisting essentially of the following constituents in the proportions and ratios specified: Percent by weight
Manganese 12 to 36
Zinc 4 to 28
Beryllium 0.10 to 1.00
Copper 50.0 + (10 × Be content)
58.0 + (14 × Be content), and such that the manganese-to-zinc ratio is between 0.4 and 10, said alloy article having excellent founding characteristics, ability to replicate mold surfaces with great detail, and improved mechanical properties.
Claim 3
Dependent Claim
46 words
A copper-base alloy article according to claim 1, additionally characterized by a low liquidus point of between about 1480° and 1600° F. wherein said manganese-to-zinc ratio is between 0.5 and 3.8, said beryllium is between 0.6 and 0.75%, and said copper is between 58 and 62.5%.
Claim 4
Dependent Claim
46 words
A copper-base alloy article according to claim 1, further characterized by a low liquidus point of between about 1480° and 1600° F., wherein the manganese-to-zinc ratio is between 0.5 and 3.8, the beryllium is between 0.1 and 0.7%, and the copper is between 52 and 60%.
Claim 5
Dependent Claim
58 words
A copper-base alloy article according to claim 1, wherein said manganese-to-zinc ratio is between 3.5 and 10, the beryllium is between 0.6 and 0.75%, and the copper is between 58 and 62.5%, said alloy having an ultimate tensile strength of at least 80 ksi, a yield strength of at least 35 ksi, and at least 10 percent elongation.
Claim 6
Dependent Claim
22 words
A copper-base alloy article according to claim 1, wherein said beryllium is between 0.1 and 0.125% and said copper is about 54%.
Claim 7
Dependent Claim
26 words
A copper-base alloy article according to claim 1, wherein the beryllium content is between 0.25 and 1.0%, and wherein the manganese-to-zinc ratio is less than 1.
Claim 8
Dependent Claim
25 words
A copper-base alloy article according to claim 1, wherein the beryllium content is 0.5% and above, and wherein the manganese-to-zinc ratio is greater than 1.
Claim 9
Dependent Claim
22 words
A copper-base alloy article according to claim 1, further characterized by a lustrous surface wherein the manganese-to-zinc ratio is less than 4.
Claim 10
Dependent Claim
30 words
A copper-base alloy article according to claim 1, further characterized by optimum ability to withstand dealloying, wherein the manganese-to-zinc ratio is about 1.2, and the beryllium content is about 0.25%.
Claim 11
Dependent Claim
37 words
A copper-base alloy article according to claim 1, characterized by its ability to serve as a brazing material, wherein the manganese-to-zinc ratio is about 1, the copper content is about 60%, and the beryllium is about 0.32%.
Claim 12
Dependent Claim
42 words
A copper-base alloy article according to claim 1, further characterized by its ability to serve as a brazing material, wherein the manganese is from 18 to 19%, the zinc is from 20.5 to 21.5% and the beryllium is from 0.2 to 0.35%.
Claim 13
Dependent Claim
41 words
A copper-base alloy article according to claim 1, further characterized by its ability to be wrought, wherein the manganese-to-zinc ratio is from 0.6 to 0.8, the beryllium is not greater than 0.4%, and the copper content is not less than 60%.
Claim 14
Independent Claim
106 words
A method of heat treating a copper-base alloy article comprising the steps of providing a copper-base alloy consisting essentially of the following constituents in the proportions specified: Percent by Weight
Manganese 12 to 36
Zinc 4 to 28
Beryllium 0.10 to 1.00
Copper 50.0 + (10 × Be content)
58.0 + (14 × Be content), solution heat treating said alloy at a temperature of about 1400° F. for about one hour, quenching said alloy, ageing said alloy at a temperature between about 600° and 800° F. selected to yield elongation of at least 10% and for about three hours, and cooling the alloy in still air.
Claim 15
Independent Claim
106 words
A method of heat treating a copper-base alloy article comprising the steps of providing a copper-base alloy consisting essentially of the following constituents in the proportions specified: Percent by Weight
Manganese 12 to 36
Zinc 4 to 28
Beryllium 0.10 to 1.00
Copper 50.0 + (10 × Be content)
58.0 + (14 × Be content), solution heat treating said alloy at a temperature of about 1400° F. for about one hour, quenching said alloy, ageing said alloy at a temperature between about 600° and 800° F. selected to yield elongation of at least 10% and for about three hours, and cooling the alloy in still air.
Claim 16
Independent Claim
97 words
A method of heat treating a copper-base alloy article comprising the steps of providing a copper-base alloy consisting essentially of the following constituents in the proportions specified: Percent by Weight
Manganese 12 to 36
Zinc 4 to 28
Beryllium 0.10 to 1.00
Copper 52 to 72, solution heat treating said alloy at a temperature of about 1400° F. for about one hour, quenching said alloy, aging said alloy at a temperature between about 600° and 800° F. selected to yield elongation of at least 10% and for about 3 hours, and cooling the alloy in still air.
Claim 17
Independent Claim
97 words
A method of heat treating a copper-base alloy article comprising the steps of providing a copper-base alloy consisting essentially of the following constituents in the proportions specified: Percent by Weight
Manganese 12 to 36
Zinc 4 to 28
Beryllium 0.10 to 1.00
Copper 52 to 72, solution heat treating said alloy at a temperature of about 1400° F. for about one hour, quenching said alloy, aging said alloy at a temperature between about 600° and 800° F. selected to yield elongation of at least 10% and for about 3 hours, and cooling the alloy in still air.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-08-03 | 1980-02-02 | 1980-08-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-08-03 | 1984-02-02 | 1984-08-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-08-03 | 1988-02-02 | 1988-08-03 | $7700.00 | Window Closed / Lapsed |