Method for treatment of molten steel in a ladle
Assignee: Nippon Steel Corp
•
Filing: 1974-08-21
•
Granted: 1976-07-27
•
Expires: 1994-08-21
Abstract
Abstract Treatment of molten steel in a ladle, which comprises blowing inert gas into the ladle from its bottom, partially immersing a receptacle which covers the portion of the molten steel where the inert gas bubbles out and maintain non-oxidizing atmospheres within the receptacle with the gas so as to prevent oxidation of the molten steel by the slag.
Inventors
- 👤 Kiyoshi Takashima
- 👤 Keizi Arima
- 👤 Takeshi Shozi
- 👤 Hisashi Mori
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 05:27
CPC Classifications
C; C21; C21C; C21C7/00; C21C7/0037; B; B22; B22D; B22D1/00; B22D1/002; B22D1/005
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
188 words
In a method for refining a melt of molten steel by gas blowing in a ladle, said melt having a layer of slag on the surface thereof wherein an inert gas is bubbled upwardly from the bottom of the ladle through the melt to agitate and induce turbulence in the melt and remove impurities therefrom, said process being carried out under atmospheric pressure, the improvement which comprises partially immersing an inverted receptable having side walls into the surface of the melt such that a portion of the interior of the receptacle is above the surface of the melt and to create a slag-free melt surface within the side-walled area of the receptacle which is in contact with said interior portion, said side wall being immersed into the melt to a depth just sufficient to avoid the introduction of said slag into the interior portion due to turbulence of the melt and wherein the receptacle is positioned so as to entrap substantially all of the inert gas bubbles as they escape from the top of the melt and maintaining a non-oxidizing atmosphere within the interior portion of the receptacle.
Claim 2
Dependent Claim
188 words
In a method for refining a melt of molten steel by gas blowing in a ladle, said melt having a layer of slag on the surface thereof wherein an inert gas is bubbled upwardly from the bottom of the ladle through the melt to agitate and induce turbulence in the melt and remove impurities therefrom, said process being carried out under atmospheric pressure, the improvement which comprises partially immersing an inverted receptable having side walls into the surface of the melt such that a portion of the interior of the receptacle is above the surface of the melt and to create a slag-free melt surface within the side-walled area of the receptacle which is in contact with said interior portion, said side wall being immersed into the melt to a depth just sufficient to avoid the introduction of said slag into the interior portion due to turbulence of the melt and wherein the receptacle is positioned so as to entrap substantially all of the inert gas bubbles as they escape from the top of the melt and maintaining a non-oxidizing atmosphere within the interior portion of the receptacle.
Claim 3
Dependent Claim
60 words
The method of claim 1 wherein the receptacle possesses a slag breaker covering its open end, said slag breaker being composed of a disposable material which, once the receptacle is immersed through the slag layer into the melt, the slag breaker dissolves into the melt thereby exposing said slag-free surface of the melt to the interior portion of the receptacle.
Claim 4
Dependent Claim
28 words
The method of claim 1, wherein a gas selected from the group consisting of inert gases and non-oxidizing gases is introduced into the interior portion of the receptacle.
Claim 5
Dependent Claim
18 words
The method of claim 1 wherein a non-oxidizing slag is introduced into the interior portion of the receptacle.
Claim 6
Dependent Claim
24 words
The method of claim 1 wherein an alloy is added to the melt by introducing said alloy into the interior portion of the receptacle.
Claim 7
Dependent Claim
61 words
The method of claim 1 wherein an alloy is added to the melt in the ladle during tapping so as to attain the desired lower limits of said alloy in the final steel composition and wherein any alloy in which the melt is deficient is added to the melt by introducing said deficient alloy through the interior portion of the receptacle.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-07-27 | 1980-01-26 | 1980-07-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-07-27 | 1984-01-26 | 1984-07-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-07-27 | 1988-01-26 | 1988-07-27 | $7700.00 | Window Closed / Lapsed |