Process of solidifying molten metal
Assignee: Olsson International Inc
•
Filing: 1974-12-30
•
Granted: 1976-07-27
•
Expires: 1994-12-30
Abstract
Abstract To take advantage of the fact that molten metal which first solidifies against a mold surface has better grain structure and closer chemical identity to the molten metal than the inner portions of a casting, a skin or thin layer of metal forming on a cold surface, such as a revolving water-cooled roll partly immersed in molten metal, is continuously stripped from said surface and almost immediately welded or fused under pressure to the surface of similarly-formed layers to make a unitary finished or semi-finished product. The layers so welded together may be separately formed, or comprise parts of a single layer folded or bent into surface-to-surface contact.
Inventors
- 👤 Erik Allan Olsson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 08:21
CPC Classifications
B; B22; B22D; B22D11/00; B22D11/06; B22D11/0611; B22D11/0614; B22D11/008; B23; B23K; B23K3/00; B23K3/06; B23K3/0607; B23K3/0638; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/4998; Y10T29/49988; Y10T29/49991
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
185 words
A metallurgical process for the production of a semi-finished product for subsequent rolling or forging into a finished product, wherein a. a melt of molten steel is simultaneously and continuously formed on moving chill surfaces into a plurality of layers of substantially uniformly fine grain structure throughout the thickness of each layer and stripping the layers from the chill surfaces as they are formed, b. bringing such layers together in face-to-face contact when they are at the solidus temperature where the metal in the layers shows no apparent liquid at the surface but before it has developed sufficient plasticity for hot rolling, c. pressing the contacting layers together with a pressure only sufficient to reduce the thickness of the combined layers not more than 2% of the combined thickness, and d. effecting the forming of the layers, the bringing them together and pressing them being effected in a common enclosure in which the hot metal is constantly protected by an inert atmosphere and removing the composite body so formed from said atmosphere only when it has cooled to at least a normal hot rolling temperature.
Claim 2
Dependent Claim
185 words
A metallurgical process for the production of a semi-finished product for subsequent rolling or forging into a finished product, wherein a. a melt of molten steel is simultaneously and continuously formed on moving chill surfaces into a plurality of layers of substantially uniformly fine grain structure throughout the thickness of each layer and stripping the layers from the chill surfaces as they are formed, b. bringing such layers together in face-to-face contact when they are at the solidus temperature where the metal in the layers shows no apparent liquid at the surface but before it has developed sufficient plasticity for hot rolling, c. pressing the contacting layers together with a pressure only sufficient to reduce the thickness of the combined layers not more than 2% of the combined thickness, and d. effecting the forming of the layers, the bringing them together and pressing them being effected in a common enclosure in which the hot metal is constantly protected by an inert atmosphere and removing the composite body so formed from said atmosphere only when it has cooled to at least a normal hot rolling temperature.
Claim 3
Dependent Claim
25 words
The process defined in claim 1 in which there are a plurality of layers in excess of two which are simultaneously formed and brought together.
Claim 4
Dependent Claim
25 words
The process defined in claim 2 in which the number and widths of the layers, when initially pressed together, form a body of square section.
Claim 5
Dependent Claim
46 words
The method of converting molten metal into a semi-finished product as defined in claim 1 in which the continuously formed layers of metal are separately formed on separate constantly-moving chilled surfaces and the said layers are of a thickness of from 5 mm. to 12 mm.
Claim 6
Dependent Claim
79 words
The method of converting molten metal into semi-finished products as defined in claim 1 in which the constantly-moving chilled surfaces are provided by the peripheries of separate rolls having their lower portions dipping into a common bath of molten metal and having their upper surfaces clear of the bath of molten metal with the layers being stripped tangentially in a horizontal direction from the surfaces of the rolls whereby the effect of gravity on the solidifying metal is minimized.
Claim 7
Dependent Claim
80 words
The method defined in claim 1 in which there are at least three separately formed layers of metal formed on spaced rotating rolls immersed in the same vessel of molten metal and sequentially united into a unitary body with the thickness of each layer ranging between 5 mm. and 12 mm. and the total reduction in thickness resulting from the fuse-welding of the several layers is in the range of 0.2% of the combined thickness of the layers to 2%.
Claim 8
Dependent Claim
45 words
The method defined in claim 1 which comprises forming a single continuous casting comprised of several layers in side-by-side relation, folding portions of said single casting into a composite body having a plurality of layers and fuse-welding the several layers into a single continuous casting.
Claim 9
Dependent Claim
134 words
The metallurgical process in which several layers of metal are continuously formed from solidification of several layers of metal on a chilled surface having a ridge and valley contour where the layers formed thereon are joined along their side edges alternately at the peaks and valleys, the layers so formed being stripped from the surface on which they are formed and, as they solidify to the solidus state but are still above a plastic hot rolling state, being then pressed into flat face-to-face contact with a pressure sufficient to effect welding of the layers into an integral body but to an extent where the metal, still too hot to have the required plastic structure for hot rolling undergoes a reduction in the range of 0.2% to 2% of the combined thickness of the layers.
Claim 10
Dependent Claim
134 words
The metallurgical process in which several layers of metal are continuously formed from solidification of several layers of metal on a chilled surface having a ridge and valley contour where the layers formed thereon are joined along their side edges alternately at the peaks and valleys, the layers so formed being stripped from the surface on which they are formed and, as they solidify to the solidus state but are still above a plastic hot rolling state, being then pressed into flat face-to-face contact with a pressure sufficient to effect welding of the layers into an integral body but to an extent where the metal, still too hot to have the required plastic structure for hot rolling undergoes a reduction in the range of 0.2% to 2% of the combined thickness of the layers.
References Cited (Backward Citations)
US3089208A
Cited
US3542116A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-07-27 | 1980-01-26 | 1980-07-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-07-27 | 1984-01-26 | 1984-07-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-07-27 | 1988-01-26 | 1988-07-27 | $7700.00 | Window Closed / Lapsed |