Powder molding process for producing thermoplastic articles
Assignee: Asahi Kasei Corp
•
Filing: 1974-12-20
•
Granted: 1976-07-13
•
Expires: 1994-12-20
Abstract
Abstract A novel powder molding process for producing thermoplastic articles having improved surface properties and the molded articles produced thereby. Molding compositions comprising a thermoplastic polymer in the powder state and a curable additive selected from the reactive monomers and prepolymers thereof, which are liquid at the melting or softening temperatures of the thermoplastic polymers, are subjected to powder molding wherein the heating rate of the molding composition during the linear portion of the temperature-time curve after the initiation of melting or softening of the thermoplastic polymer is maintained at a very low rate, i.e., less than 25°C. per minute. A curing agent may be added to the molding composition in order to control the curing time of the curable additives. The obtained thermoplastic articles have a cured thin surface layer of the curable additives, said surface layer being strongly combined with an inner layer of the thermoplastic articles.
Inventors
- 👤 Yasuo Horiuchi
- 👤 Toraichi Katsube
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 13:03
CPC Classifications
C; C08; C08J; C08J5/00; B; B29; B29C; B29C39/00; C08J3/00; C08J3/24; C08J3/245
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
146 words
A powder molding process for producing thermoplastic articles having improved surface properties which comprises dry blending a powdery thermoplastic polymer and a curable additive selected from reactive monomers and prepolymers thereof, said curable additive being a liquid at the melting or softening temperature of the thermoplastic polymer and being capable of bleeding to the surface of the thermoplastic polymer during molding, to form a moldable composition, and powder molding said composition by heating it in a mold to initiate melting or softening of the thermoplastic polymer, said heating being controlled at a heating rate of less than 25°C. per minute during the linear portion of the temperature-time curve after the initiation of melting or softening of the thermoplastic polymer, whereby said curable additive bleeds to the surface of the thermoplastic polymer during molding and cures at said surface so as to improve the surface characteristics thereof.
Claim 2
Dependent Claim
146 words
A powder molding process for producing thermoplastic articles having improved surface properties which comprises dry blending a powdery thermoplastic polymer and a curable additive selected from reactive monomers and prepolymers thereof, said curable additive being a liquid at the melting or softening temperature of the thermoplastic polymer and being capable of bleeding to the surface of the thermoplastic polymer during molding, to form a moldable composition, and powder molding said composition by heating it in a mold to initiate melting or softening of the thermoplastic polymer, said heating being controlled at a heating rate of less than 25°C. per minute during the linear portion of the temperature-time curve after the initiation of melting or softening of the thermoplastic polymer, whereby said curable additive bleeds to the surface of the thermoplastic polymer during molding and cures at said surface so as to improve the surface characteristics thereof.
Claim 3
Dependent Claim
16 words
The process of claim 1, wherein said heating rate is about 10° to 20°C. per minute.
Claim 4
Dependent Claim
31 words
The process of claim 1, wherein the amount of curable additive in the molding composition is from about 0.5% to 15.0% by weight, based on the weight of the thermoplastic polymer.
Claim 5
Dependent Claim
42 words
The process of claim 1, wherein said heating rate is about 10° to 20°C. per minute, and the amount of curable additive in the molding composition is from about 0.5% to 15.0% by weight, based on the weight of the thermoplastic polymer.
Claim 6
Dependent Claim
31 words
The process of claim 1, wherein the amount of curable additive in the molding composition is from about 1.0% to 10.0% by weight, based on the weight of the thermoplastic polymer.
Claim 7
Dependent Claim
13 words
The process of claim 1, wherein the molding composition includes a curing agent.
Claim 8
Dependent Claim
30 words
The process of claim 6, wherein the amount of curing agent in the molding composition is about 0.01% to 5.0% by weight, based on the weight of the thermoplastic polymer.
Claim 9
Dependent Claim
33 words
The process of claim 1, wherein the thermoplastic polymer is selected from the group consisting of polyolefins, copolymers of olefins, polyamides, polycarbonates, polyoxymethylene, polyvinyl chloride, polystyrene, acrylonitrile-butadiene-styrene copolymers, butyrate resins and acrylic resins.
Claim 10
Dependent Claim
64 words
The process of claim 1, wherein the curable additive is selected from the group consisting of allyl ester monomers and prepolymers thereof, diene polymers and modified diene polymers having an absolute viscosity of 1 to 10,000 poise at 25°C., unsaturated polyester oligomers, acrylic prepolymers, polyisocyanates and/or polyols and prepolymers thereof, urea-formaldehyde precondensates, epoxy-containing prepolymers, furan resin precondensates, resol resin precondensates and xylene resin precondensates.
Claim 11
Dependent Claim
15 words
The process of claim 1, wherein the molding process is carried out by rotational molding.
References Cited (Backward Citations)
US2887728A
Cited
US3336244A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-07-13 | 1980-01-12 | 1980-07-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-07-13 | 1984-01-12 | 1984-07-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-07-13 | 1988-01-12 | 1988-07-13 | $7700.00 | Window Closed / Lapsed |