Intumescent fire-retardant coating compositions containing amide-polyphosphates
Assignee: Sumitomo Chemical Co Ltd
•
Filing: 1975-03-06
•
Granted: 1976-07-13
•
Expires: 1995-03-06
Abstract
Abstract An intumescent fire-retardant coating composition containing, as a fire-retardant ingredient and an intumescent solid, a substantially water-insoluble amide polyphosphate condensate is disclosed.
Inventors
- 👤 Kozo Fukuba
- 👤 Yasutomo Ogushi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 00:06
CPC Classifications
C; C09; C09D; C09D5/00; C09D5/18; Y; Y10; Y10S; Y10S260/00; Y10S260/24; Y10S428/00; Y10S428/92; Y10S428/921
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
168 words
An intumescent fire-retardant coating composition comprising an aqueous dispersion of (A) a substantially water-insoluble amide polyphosphate condensate comprising the heat-condensation product of a phosphoric acid-containing material selected from the group consisting of ammonium orthophosphate, orthophosphoric acid, polyphosphoric acid, phosphoric anhydride, urea phosphate and mixtures thereof with a cyanamide derivative selected from the group consisting of melamine, dicyanamide or mixtures thereof, as nitrogen source in the presence of a condensing agent selected from the group consisting of urea, urea phosphate and a mixture thereof in a molar ratio of 0.8:1:0.05 to 1.5:1:1 of urea : phosphoric acid-containing material (as H 3 PO 4 ) : cyanamide derivative at a temperature of from about 150° to 350°C, (B) a film forming binder comprising a polymer solution in an organic solvent or an aqueous emulsified polymer solution, and (C) a carbonific material selected from the group consisting of a saccharide and a polyhydric alcohol, with (A), (B) and (C) comprising from about 20 to 90% by weight of the total composition.
Claim 2
Dependent Claim
168 words
An intumescent fire-retardant coating composition comprising an aqueous dispersion of (A) a substantially water-insoluble amide polyphosphate condensate comprising the heat-condensation product of a phosphoric acid-containing material selected from the group consisting of ammonium orthophosphate, orthophosphoric acid, polyphosphoric acid, phosphoric anhydride, urea phosphate and mixtures thereof with a cyanamide derivative selected from the group consisting of melamine, dicyanamide or mixtures thereof, as nitrogen source in the presence of a condensing agent selected from the group consisting of urea, urea phosphate and a mixture thereof in a molar ratio of 0.8:1:0.05 to 1.5:1:1 of urea : phosphoric acid-containing material (as H 3 PO 4 ) : cyanamide derivative at a temperature of from about 150° to 350°C, (B) a film forming binder comprising a polymer solution in an organic solvent or an aqueous emulsified polymer solution, and (C) a carbonific material selected from the group consisting of a saccharide and a polyhydric alcohol, with (A), (B) and (C) comprising from about 20 to 90% by weight of the total composition.
Claim 3
Dependent Claim
37 words
The composition according to claim 1, wherein said amide polyphosphate condensate is present in an amount of about 5 to 90% by weight on a solids basis to the total weight of solids present in said composition.
Claim 4
Dependent Claim
34 words
The composition according to claim 2, wherein said amide polyphosphate condensate is present in an amount of from 10 to 80% by weight based on the total weight of solids present in said composition.
Claim 5
Dependent Claim
40 words
The composition according to claim 1, wherein said film forming binder is present in an amount of from about 2 to 60% by weight on a solids basis based on the total weight of the solids present in said composition.
Claim 6
Dependent Claim
39 words
The composition according to claim 4, wherein said film forming binder is present in an amount of from 4 to 50% by weight on a solids basis based on the total weight of the solids present in said composition.
Claim 7
Dependent Claim
46 words
The composition according to claim 1, wherein said film forming binder is an emulsion containing polyvinyl acetate, polyacrylonitrile, polyvinyl chloride, polyvinylidene chloride, a copolymer of vinyl acetate and an acrylate, a copolymer of vinyl acetate and ethylene, or a copolymer of vinyl chloride and an acrylate.
Claim 8
Dependent Claim
22 words
The composition according to claim 6, wherein said film forming binder is an emulsion containing a copolymer of vinyl acetate and ethylene.
Claim 9
Dependent Claim
14 words
The composition according to claim 1, wherein said carbonific material is starch or pentaerythritol.
Claim 10
Dependent Claim
35 words
The composition according to claim 1, wherein said carbonific material is present in an amount of not less than about 2% by weight based on the total weight of the solids present in said composition.
Claim 11
Dependent Claim
34 words
The composition according to claim 9, wherein said carbonific material is present in an amount of from 2 to 50% by weight based on the total weight of the solids present in said composition.
Claim 12
Dependent Claim
37 words
The composition according to claim 1, wherein said composition additionally contains a thermosetting resin in an amount of not more than about 70% by weight based on the total weight of the solids present in said composition.
Claim 13
Dependent Claim
34 words
The composition according to claim 11, wherein the thermosetting resin is present in an amount of from 2 to 40% by weight based on the total weight of the solids present in said composition.
Claim 14
Dependent Claim
39 words
The composition according to claim 1, wherein said composition additionally contains at least one of an inorganic fiber, a dye, a pigment, a swelling agent, a wetting agent, a dispersing agent, an anti-foaming agent, a fungicide and a bactericide.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-07-13 | 1980-01-12 | 1980-07-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-07-13 | 1984-01-12 | 1984-07-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-07-13 | 1988-01-12 | 1988-07-13 | $7700.00 | Window Closed / Lapsed |