Method of manufacturing a stainless steel boiler tube with anticorrosive coating
Assignee: Hitachi Ltd
•
Filing: 1975-01-15
•
Granted: 1976-07-13
•
Expires: 1995-01-15
Abstract
Abstract A boiler tube and a method for manufacturing the same are disclosed in which an inner surface of the boiler tube used in the center of a high-temperature, high-pressure boiler is formed with a spinel layer consisting of an oxide of iron, chromium and nickel, which is exposed. The specific method of the manufacture is that after the boiler tube is brought into contact with high temperature steam, a magnetic iron (Fe3O4) layer produced on the inner surface is removed.
Inventors
- 👤 Katsumi Suzuki
- 👤 Toshio Kawakami
- 👤 Osamu Asai
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 20:18
CPC Classifications
F; F22; F22B; F22B37/00; F22B37/02; F22B37/04; F16; F16L; F16L58/00; F16L58/02; Y; Y10; Y10S; Y10S122/00; Y10S122/13
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
127 words
A method for manufacturing a stainless steel boiler tube with an anticorrosive coating comprising the steps of providing a boiler tube of a stainless steel selected from iron-chromium stainless steel with a chromium content of at least 9% and iron-chromium-nickel stainless steel containing iron as a major component and chromium and nickel as minor components, heat-treating at least a inner surface of said boiler tube under a steam environment at 500° to 1,100°C. until an anticorrosive coating having a thickness of at least 40 μ is formed and subsequently removing a Fe 3 O 4 layer formed on the anticorrosive coating during heat treatment of said at least the inner surface of said boiler tube by subjecting the Fe 2 O 3 layer to an exfoliating treatment.
Claim 2
Independent Claim
127 words
A method for manufacturing a stainless steel boiler tube with an anticorrosive coating comprising the steps of providing a boiler tube of a stainless steel selected from iron-chromium stainless steel with a chromium content of at least 9% and iron-chromium-nickel stainless steel containing iron as a major component and chromium and nickel as minor components, heat-treating at least a inner surface of said boiler tube under a steam environment at 500° to 1,100°C. until an anticorrosive coating having a thickness of at least 40 μ is formed and subsequently removing a Fe 3 O 4 layer formed on the anticorrosive coating during heat treatment of said at least the inner surface of said boiler tube by subjecting the Fe 2 O 3 layer to an exfoliating treatment.
Claim 3
Dependent Claim
50 words
A method for manufacturing a stainless steel boiler tube with an anticorrosive coating according to claim 1 wherein the temperature of the heat treatment is 1,000° to 1,100°C. and the treatment is conducted until the overall thickness of the anticorrosive coating and the Fe 3 O 4 layer exceeds 100μ.
Claim 4
Dependent Claim
43 words
A method for manufacturing a stainless steel boiler tube with an anticorrosive coating according to claim 2 wherein the time of the heat treatment is 1,000 to 3,000 hours when the temperature of the heat treatment under the steam environment is approximately 600°C.
Claim 5
Dependent Claim
45 words
A method for manufacturing a stainless steel boiler tube with an anticorrosive coating according to claim 2 wherein the time of the heat treatment is 1 to 10 hours when the temperature of the heat treatment under the steam environment is approximately 1,000° to 1,100°C.
Claim 6
Dependent Claim
51 words
A method for manufacturing a stainless steel boiler tube with an anticorrosive coating according to claim 2 further comprising the step of cooling the stainless steel boiler tube to a room temperature after the heat treatment under the steam environment for removing exfoliated scales of said Fe 3 O 4 .
Claim 7
Dependent Claim
72 words
A method for manufacturing a stainless steel boiler tube with an anticorrosive coating according to claim 3 further comprising the steps of elevating the temperature of the stainless steel boiler tube above 650°C after the heat treatment under the steam environment, maintaining the boiler tube at the elevated temperature for 6 hours, and then cooling the boiler tube to a room temperature for removing exfoliated scales of Fe 3 O 4 .
Claim 8
Dependent Claim
55 words
A method for manufacturing a stainless steel boiler tube with an anticorrosive coating according to claim 3 further comprising the steps of passing water of 200 to 300 kg/cm 2 into the stainless steel boiler tube and externally heating the boiler tube so as to maintain the temperature of the steam at 500 to 650°C.
Claim 9
Dependent Claim
31 words
A method for manufacturing a stainless steel boiler tube with an anticorrosive coating according to claim 5 wherein a gas selected from air, steam and cooling gas is blown during cooling.
Claim 10
Dependent Claim
67 words
A method for manufacturing a stainless steel boiler tube with an anticorrosive coating according to claim 4 further comprising the step of cooling the stainless steel boiler tube after the steam treatment at a cooling rate higher than natural cooling rate, the temperature at which said cooling is started is approximately 1,100° to 1,000°C and the temperature at which said cooling is terminated is a room temperature.
Claim 11
Dependent Claim
67 words
A method for manufacturing a stainless steel boiler tube with an anticorrosive coating according to claim 1 wherein the Fe 3 O 4 layer is removed by elevating the temperature of the stainless steel boiler tube to a temperature above 650°C. subsequent to the heat treatment, maintaining the boiler tube at the elevated temperature for 6 hours and thereafter cooling the boiler tube to a room temperature.
Claim 12
Dependent Claim
39 words
A method for manufacturing a stainless steel boiler tube with an anticorrosive coating according to claim 1 wherein the anticorrosive coating consists essentially of a spinel layer which is a composite oxide of the metals forming said stainless steel.
Claim 13
Dependent Claim
29 words
A method for manufacturing a stainless steel boiler tube with an anticorrosive coating according to claim 11 wherein said spinel is a composite oxide of nickel, iron and chromium.
Claim 14
Dependent Claim
28 words
A method for manufacturing a stainless steel boiler tube with an anticorrosive coating according to claim 11 wherein the spinel is a composite oxide of iron and chromium.
Claim 15
Dependent Claim
28 words
A method for manufacturing a stainless steel boiler tube with an anticorrosive coating according to claim 1 wherein said stainless steel consists essentially of iron, nickel and chromium.
Claim 16
Dependent Claim
43 words
A method for manufacturing a stainless steel boiler tube with an anticorrosive coating according to claim 1 wherein said stainless steel consists essentially of 5 - 25% by weight of chromium, 3 - 25% by weight of nickel and a balance of iron.
Claim 17
Dependent Claim
69 words
A method for manufacturing a stainles steel boiler tube with an anticorrosive coating according to claim 1 wherein said stainless steel is selected from a group consisting of 18 Cr stainless steel, 25 Cr stainless steel, 18 Cr - 8 Ni stainless steel, 9 Cr - 1 Mo stainless steel, 22 Cr - 12 Ni stainless steel, 13 Cr stainless steel and 25 Cr - 20 Ni stainless steel.
Claim 18
Dependent Claim
27 words
A method for manufacturing a stainless steel boiler tube with an anticorrosive coating according to claim 1 wherein the pressure of the steam is above atmospheric pressure.
Claim 19
Dependent Claim
34 words
A method for manufacturing a stainless steel boiler tube with an anticorrosive coating according to claim 1 wherein heat treatment is effected until a thickness of the anticorrosive coating is from 40 to 80μ.
Claim 20
Dependent Claim
33 words
A method for manufacturing a stainless steel boiler tube with an anticorrosive coating according to claim 1 wherein the heat treatment is effected until the thickness of the anticorrosive coating is 100 μ.
Claim 21
Independent Claim
134 words
A method for manufacturing a stainless steel boiler tube with an anticorrosive coating comprising the steps of providing a boiler tube of a stainless steel selected from iron-chromium stainless steels with chromium content of at least 9%, passing water under pressure of 200 to 300 kg/cm 2 into said boiler tube, externally heating the boiler tube so as to maintain the temperature of the steam at 500° to 650°C, maintaining the boiler tube at the elevated temperature for 1,000 to 3,000 hours to form a coating having a spinel layer covered with a Fe 3 O 4 layer, maintaining the boiler tube above 650°C for 6 hours and then cooling the boiler tube to a room temperature at a cooling rate higher than natural cooling rate to remove the Fe 3 O 4 layer.
Claim 22
Independent Claim
134 words
A method for manufacturing a stainless steel boiler tube with an anticorrosive coating comprising the steps of providing a boiler tube of a stainless steel selected from iron-chromium stainless steels with chromium content of at least 9%, passing water under pressure of 200 to 300 kg/cm 2 into said boiler tube, externally heating the boiler tube so as to maintain the temperature of the steam at 500° to 650°C, maintaining the boiler tube at the elevated temperature for 1,000 to 3,000 hours to form a coating having a spinel layer covered with a Fe 3 O 4 layer, maintaining the boiler tube above 650°C for 6 hours and then cooling the boiler tube to a room temperature at a cooling rate higher than natural cooling rate to remove the Fe 3 O 4 layer.
References Cited (Backward Citations)
US3705057A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-07-13 | 1980-01-12 | 1980-07-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-07-13 | 1984-01-12 | 1984-07-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-07-13 | 1988-01-12 | 1988-07-13 | $7700.00 | Window Closed / Lapsed |