Process for preparing silver-cadmium oxide alloys
Assignee: AMI DELAWARE Inc
•
Filing: 1974-11-11
•
Granted: 1976-07-13
•
Expires: 1994-11-11
Abstract
Abstract This application describes the addition of an alkali metal, generally in the form of a salt thereof, to a mixture of silver and cadmium oxide, prior to the sintering step, to improve the as-sintered densities of the resultant alloy material.
Inventors
- 👤 Han J. Kim
- 👤 F. Joseph Reid
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 14:39
CPC Classifications
C; C22; C22C; C22C1/00; C22C1/10; C22C1/1078; B; B22; B22F; B22F3/00; B22F3/10; B22F3/1003; C22C32/00; C22C32/001; C22C32/0015; C22C32/0021; H; H01; H01H; H01H1/00; H01H1/02; H01H1/021; H01H1/023; H01H1/0237; H01H1/02372; H01H1/02374; Y; Y10; Y10S; Y10S75/00; Y10S75/95
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
85 words
A method for preparing a silver-cadmium oxide alloy comprising forming a compact of silver particles, cadmium oxide particles and a density-increasing additive selected from the group consisting of the alkali metal and alkaline earth metal salts of nitric acid; heating said additive-containing compact to a temperature below the final sintering temperature for a period of time sufficient to decompose said additive; and then sintering said heated compact to form a silver-cadmium oxide alloy having improved sintered density as compared to alloys prepared without said additive.
Claim 2
Independent Claim
85 words
A method for preparing a silver-cadmium oxide alloy comprising forming a compact of silver particles, cadmium oxide particles and a density-increasing additive selected from the group consisting of the alkali metal and alkaline earth metal salts of nitric acid; heating said additive-containing compact to a temperature below the final sintering temperature for a period of time sufficient to decompose said additive; and then sintering said heated compact to form a silver-cadmium oxide alloy having improved sintered density as compared to alloys prepared without said additive.
Claim 3
Dependent Claim
25 words
The method of claim 1 wherein said compact contains about 70% to about 95% silver particles and about 30% to about 5% cadmium oxide particles.
Claim 4
Dependent Claim
19 words
The method of claim 2 wherein said additive-containing compact contains about 0.05% to about 0.5% of said density-increasing additive.
Claim 5
Dependent Claim
29 words
The method of claim 1 wherein said additive-containing compact contains about 85% silver particles, about 15% cadmium oxide particles, and about 0.1% to about 0.2% of said density-increasing additive.
Claim 6
Dependent Claim
12 words
The method of claim 1 wherein said density-increasing additive is lithium nitrate.
Claim 7
Dependent Claim
23 words
The method of claim 5 wherein said additive-containing compact is heated to about 600°-700°C for about 1-4 hours to decompose said lithium nitrate.
Claim 8
Dependent Claim
37 words
The method of claim 1 wherein said additive-containing compact is formed by providing a blend of silver particles, cadmium oxide particles and said density-increasing additive, and pressing at high pressure said blend to form said additive-containing compact.
Claim 9
Dependent Claim
40 words
The method of claim 1 wherein said additive-containing compact is formed by pressing at high pressure a blend of silver and cadmium oxide particles to form a compact, and thereafter treating said compact with a solution of said density-increasing additive.
Claim 10
Dependent Claim
19 words
The method of claim 1 wherein said silver-cadmium oxide alloy has a sintered density of about 99% of theoretical.
Claim 11
Independent Claim
89 words
The method for preparing a silver-cadmium oxide alloy comprising forming a compact comprising about 15% finely-divided cadmium oxide particles, about 85% finely-divided silver particles, and about 0.1 to about 0.2% lithium nitrate based upon the total weight of said silver and said cadmium oxide; heating said compact at about 600°-700°C for about 1-4 hours to decompose said lithium nitrate; and thereafter heating said compact at about 850°-950°C for about 1/2 - 2 hours to form a silver cadmium oxide alloy having an as-sintered density of about 99% of theoretical.
Claim 12
Independent Claim
89 words
The method for preparing a silver-cadmium oxide alloy comprising forming a compact comprising about 15% finely-divided cadmium oxide particles, about 85% finely-divided silver particles, and about 0.1 to about 0.2% lithium nitrate based upon the total weight of said silver and said cadmium oxide; heating said compact at about 600°-700°C for about 1-4 hours to decompose said lithium nitrate; and thereafter heating said compact at about 850°-950°C for about 1/2 - 2 hours to form a silver cadmium oxide alloy having an as-sintered density of about 99% of theoretical.
Claim 13
Independent Claim
92 words
A method for preparing a silver-cadmium oxide alloy comprising forming a compact of about 70-95% silver particles, about 5-30% cadmium oxide particles, and about 0.05-0.5% of a density-increasing additive selected from the group consisting of the alkali metal and alkaline earth metal salts of nitric acid; heating said additive-containing compact to a temperature below the final sintering temperature for a period of time sufficient to decompose said additive; and then sintering said heated compact to form a silver-cadmium oxide alloy having improved sintered density as compared to alloys prepared without said additive.
Claim 14
Independent Claim
92 words
A method for preparing a silver-cadmium oxide alloy comprising forming a compact of about 70-95% silver particles, about 5-30% cadmium oxide particles, and about 0.05-0.5% of a density-increasing additive selected from the group consisting of the alkali metal and alkaline earth metal salts of nitric acid; heating said additive-containing compact to a temperature below the final sintering temperature for a period of time sufficient to decompose said additive; and then sintering said heated compact to form a silver-cadmium oxide alloy having improved sintered density as compared to alloys prepared without said additive.
Claim 15
Dependent Claim
11 words
The method of claim 11 wherein said additive is lithium nitrate.
Claim 16
Dependent Claim
19 words
The method of claim 11 wherein said silver-cadmium oxide alloy has a sintered density of about 99% of theoretical.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-07-13 | 1980-01-12 | 1980-07-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-07-13 | 1984-01-12 | 1984-07-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-07-13 | 1988-01-12 | 1988-07-13 | $7700.00 | Window Closed / Lapsed |