Film excellent in slip characteristics and its production
Assignee: Toyobo Co Ltd
•
Filing: 1974-06-27
•
Granted: 1976-07-06
•
Expires: 1994-06-27
Abstract
Abstract A polyester block copolymer film excellent in slip characteristics and blocking resistance, which is prepared by melt extruding a polyester block copolymer in a film and cooling the film in a melt state at a temperature of about 40° to 120°C to solidify it, the polyester block copolymer comprising crystalline polyester segments and non-crystalline polymer segments in a weight ratio of 99 : 1 to 10 : 90 and having a number average molecular weight of about 10,000 to 100,000, the melting point of a self-supporting high polymer substantially constituted with the monomer components of the said crystalline polyester segments alone being not lower than about 200°C and the melting point or softening point of a polymer substantially constituted with the said non-crystalline polymer segments themselves being not higher than about 80°C.
Inventors
- 👤 Ikuya Hayashi
- 👤 Yukio Yamane
- 👤 Chiyozi Hitomi
- 👤 Keiske Miyake
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 02:29
CPC Classifications
C; C08; C08G; C08G63/00; C08G63/66; C08G63/668; C08G63/672; C08G63/02; C08G63/60; B; B29; B29C; B29C48/00; B29C48/03; B29C48/07; B29C48/08
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
213 words
A film of a polyester block copolymer, which has the following physical constants: (1) Specific gravity 1.003-1.300
(2) Young's modulus (kg/cm.sup.2)
not more than 1,500
(at 20°C)
(3) Breaking strength (kg/cm.sup.2)
150-800 (at 20°C)
(4) Breaking elongation (%)
not less than 300
(at 20°C)
(5) Impact strength (kg.cm/25μ)
not less than 8
(at 20°C
(6) Thermal adhesion (kg/cm)
not less than 0.5
(at 20°C)
(7) Oxygen permeability constant
0.5 × 10.sup.-.sup.10 -100
(cc.cm/cm.sup.2.sec.cmHg)
× 10.sup.-.sup.10 (at 30°C)
(8) Clarity (%) not less than 80
(9) Haze (%) not more than 2, the polyester block copolymer comprising crystalline polyester segments and non-crystalline polymer segments in a weight ratio of 99 : 1 to 10 : 90 and having a number average molecular weight of about 10,000 to 100,000, the melting point of a high self-supporting polymer substantially constituted with the monomer components of the said crystalline polyester segments alone being not lower than about 200°C and the melting point or softening point of a polymer substantially constituted with the said non-crystalline polymer segments themselves being not higher than about 80°C, said film being prepared by melt extruding said polyester block copolymer to form a film and cooling the film in a melt state at a temperature of about 40° to 120°C to solidify it.
Claim 2
Dependent Claim
213 words
A film of a polyester block copolymer, which has the following physical constants: (1) Specific gravity 1.003-1.300
(2) Young's modulus (kg/cm.sup.2)
not more than 1,500
(at 20°C)
(3) Breaking strength (kg/cm.sup.2)
150-800 (at 20°C)
(4) Breaking elongation (%)
not less than 300
(at 20°C)
(5) Impact strength (kg.cm/25μ)
not less than 8
(at 20°C
(6) Thermal adhesion (kg/cm)
not less than 0.5
(at 20°C)
(7) Oxygen permeability constant
0.5 × 10.sup.-.sup.10 -100
(cc.cm/cm.sup.2.sec.cmHg)
× 10.sup.-.sup.10 (at 30°C)
(8) Clarity (%) not less than 80
(9) Haze (%) not more than 2, the polyester block copolymer comprising crystalline polyester segments and non-crystalline polymer segments in a weight ratio of 99 : 1 to 10 : 90 and having a number average molecular weight of about 10,000 to 100,000, the melting point of a high self-supporting polymer substantially constituted with the monomer components of the said crystalline polyester segments alone being not lower than about 200°C and the melting point or softening point of a polymer substantially constituted with the said non-crystalline polymer segments themselves being not higher than about 80°C, said film being prepared by melt extruding said polyester block copolymer to form a film and cooling the film in a melt state at a temperature of about 40° to 120°C to solidify it.
Claim 3
Dependent Claim
18 words
The film according to claim 1, which has a blocking strength of not more than about 1.3 g/cm.
Claim 4
Dependent Claim
42 words
The film according to claim 1, wherein the polyester block copolymer is incorporated with at least one inorganic material in fine particles in an amount of about 0.01 to 5 % by weight based on the weight of the polyester block copolymer.
Claim 5
Dependent Claim
31 words
The film according to claim 3, wherein the inorganic material is present in the form of fine particles having a particle size of about 0.1 to 10 μ on the average.
Claim 6
Dependent Claim
36 words
The film according to claim 4, wherein the inorganic material is a member selected from the group consisting of oxides and salts of the metals belonging to Groups II, III and IV of the periodic table.
Claim 7
Dependent Claim
18 words
The film according to claim 3, which has a blocking strength of not more than about 0.5 g/cm.
Claim 8
Dependent Claim
27 words
The film according to claim 6, which has a static friction coefficient of about 0.4 to 1.0 and a kinetic friction coefficient of about 0.5 to 2.0.
Claim 9
Dependent Claim
47 words
The film according to claim 1, wherein the crystalline polyester segments comprise terephthalic acid or a mixture thereof with isophthalic acid as the dicarboxylic acid component and ethylene glycol or tetramethylene glycol as the glycol component and the non-crystalline polymer segments comprise polyethylene glycol or polytetramethylene glycol.
Claim 10
Dependent Claim
30 words
The film according to claim 1, wherein the polyester block copolymer is a polytetramethylene terephthalate-polytetramethylene oxide block copolymer having a weight ratio of 90 : 10 to 40 : 60.
Claim 11
Dependent Claim
135 words
A process for preparing a polyester block copolymer film excellent in slip characteristics and blocking resistance, which comprises melt extruding a polyester block copolymer to form a film and cooling the film in a melt state at a temperature of about 40° to 120°C to solidify it, the polyester block copolymer comprising crystalline polyester segments and non-crystalline polymer segments in a weight ratio of 99 : 1 to 10 : 90 and having a number average molecular weight of about 10,000 to 100,000, the melting point of a high self-supporting polymer substantially constituted with the monomer components of the said crystalline polyester segments alone being not lower than about 200°C and the melting point or softening point of a polymer substantially constituted with the said non-crystalline polymer segments themselves being not higher than about 80°C.
Claim 12
Dependent Claim
135 words
A process for preparing a polyester block copolymer film excellent in slip characteristics and blocking resistance, which comprises melt extruding a polyester block copolymer to form a film and cooling the film in a melt state at a temperature of about 40° to 120°C to solidify it, the polyester block copolymer comprising crystalline polyester segments and non-crystalline polymer segments in a weight ratio of 99 : 1 to 10 : 90 and having a number average molecular weight of about 10,000 to 100,000, the melting point of a high self-supporting polymer substantially constituted with the monomer components of the said crystalline polyester segments alone being not lower than about 200°C and the melting point or softening point of a polymer substantially constituted with the said non-crystalline polymer segments themselves being not higher than about 80°C.
Claim 13
Dependent Claim
29 words
The process according to claim 10, wherein the weight ratio of the crystalline polyester segments and the non-crystalline polymer segments is from 90 : 10 to 20 : 80.
Claim 14
Dependent Claim
30 words
The process according to claim 10, wherein the non-crystalline polymer segments are those having a molecular weight of about 400 to 8,000 when a polymer is produced with them alone.
Claim 15
Dependent Claim
50 words
The process according to claim 10, wherein the crystalline polyester segments are constituted with terephthalic acid or its mixture with isophthalic acid as the dicarboxylic acid component and ethylene glycol or tetramethylene glycol as the glycol component and the non-crystalline polymer segments are constituted with polyethylene glycol or polytetramethylene glycol.
Claim 16
Dependent Claim
30 words
The process according to claim 10, wherein the polyester block copolymer is a polytetramethylene terephthalate-polytetramethylene oxide block copolymer having a weight ratio of 90 : 10 to 40 : 60.
Claim 17
Dependent Claim
37 words
The process according to claim 10, wherein said polyester block copolymer having a water content of not more than 0.2 % by weight is melt extruded at a temperature of about 160° to 280°C in an extruder.
Claim 18
Dependent Claim
31 words
The process according to claim 15, wherein the extruded film in a melt state is cooled at a temperature of about 40' to 120°C. with a cooling roll to solidify it.
Claim 19
Dependent Claim
42 words
The process according to claim 10, wherein the polyester block copolymer is incorporated with at least one inorganic material in fine particles in an amount of about 0.01 to 5 % by weight based on the weight of the polyester block copolymer.
Claim 20
Dependent Claim
30 words
The process according to claim 17, wherein the inorganic material is present in the form of fine particles having a particle size of about 0.1 to 10μ on the average.
Claim 21
Dependent Claim
36 words
The process according to claim 18, wherein the inorganic material is a member selected from the group consisting of oxides and salts of the metals belonging to Groups II, III and IV of the periodic table.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-07-06 | 1980-01-05 | 1980-07-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-07-06 | 1984-01-05 | 1984-07-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-07-06 | 1988-01-05 | 1988-07-06 | $7700.00 | Window Closed / Lapsed |