Abstract A high-strength, coated cemented carbide product comprising a cemented carbide substrate and a fully dense alpha aluminum oxide coating on the substrate. The coating has a thickness of from 1-20 microns and is firmly and adherently bonded to the cemented carbide substrate through a thin intermediate nonometallic layer of an iron group metal aluminate. The coated product combines a wear resistance substantially as high as aluminum oxide coating materials and a transverse rupture strength of at least 150,000 psi. The coated product is prepared by passing water vapor, hydrogen gas and an aluminum halide over the substrate at a temperatue of from 900°-1250°C. the ratio of water vapor to hydrogen gas being between about 0.025 and 2.0.
The product prepared by the process of coating a cemented carbide substrate with a fully dense alpha aluminum oxide coating of from 1-20 microns thickness, which process comprises contacting the carbide substrate with aluminum halide vapor, water vapor and hydrogen gas (over the carbide substrate) at a temperature of from about 900° - 1250°C, the ratio of water vapor to hydrogen gas being between about 0.025 and 2.0, to form a layer of fully dense alpha aluminum oxide on said substrate.
Claim 2
Dependent Claim
81 words
The product prepared by the process of coating a cemented carbide substrate with a fully dense alpha aluminum oxide coating of from 1-20 microns thickness, which process comprises contacting the carbide substrate with aluminum halide vapor, water vapor and hydrogen gas (over the carbide substrate) at a temperature of from about 900° - 1250°C, the ratio of water vapor to hydrogen gas being between about 0.025 and 2.0, to form a layer of fully dense alpha aluminum oxide on said substrate.
Claim 3
Dependent Claim
13 words
The product of claim 1 in which the aluminum halide is aluminum chloride.
Claim 4
Dependent Claim
25 words
The product of claim 1 in which the water vapor is formed during the coating process by the reaction of hydrogen and CO 2 gas.