Process for the recovery of selenium from waste gas
Assignee: AGC Inc
•
Filing: 1974-11-14
•
Granted: 1976-06-29
•
Expires: 1994-11-14
Abstract
Abstract Selenium is recovered from combustion waste gas, especially the combustion waste gas evolved from glass melting furnaces by a process in which the waste gas is contacted with an absorbing solution containing an alkali metal sulfite or bisulfite, whereby metallic selenium and selenium compounds are absorbed, the temperature of the waste gas is decreased and the humidity of the waste gas is increased. The treated waste gas in then passed through a moist glass fiber filter which collects the remaining amounts of selenium from the waste gas. The absorbing solution is combined with the solution used to wash the glass fiber filter and the combined solutions are treated with an acid which reduces all of the selenium present in the solution to metallic selenium which precipitates from solution.
Inventors
- 👤 Hisashi Kakuta
- 👤 Shigetada Matoba
- 👤 Kenichi Shimizu
- 👤 Satoshi Yamashita
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 21:34
CPC Classifications
C; C01; C01B; C01B19/00; C01B19/02
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
135 words
A process for the recovery of selenium from combustion waste gas, which comprises: contacting said combustion waste gas with a first absorbing solution which contains at least one absorbent selected from the group consisting of an alkali metal sulfite and an alkali metal bisulfite, whereby the major portion of the selenium component of said waste gas is absorbed therein, and wherein said waste gas is cooled so that the humidity of said gas is increased; passing said gas through a moistened glass fiber filter of glass wool having a bulk density of 150-250 kg/m 3 , so that the residual selenium in said gas is collected thereon; combining the selenium component collected on said filter with the first absorbing solution; and acidifying said combined solution to reduce and precipitate said selenium component to metallic selenium.
Claim 2
Dependent Claim
135 words
A process for the recovery of selenium from combustion waste gas, which comprises: contacting said combustion waste gas with a first absorbing solution which contains at least one absorbent selected from the group consisting of an alkali metal sulfite and an alkali metal bisulfite, whereby the major portion of the selenium component of said waste gas is absorbed therein, and wherein said waste gas is cooled so that the humidity of said gas is increased; passing said gas through a moistened glass fiber filter of glass wool having a bulk density of 150-250 kg/m 3 , so that the residual selenium in said gas is collected thereon; combining the selenium component collected on said filter with the first absorbing solution; and acidifying said combined solution to reduce and precipitate said selenium component to metallic selenium.
Claim 3
Dependent Claim
38 words
The process of claim 1, wherein said waste gas is contacted with said first absorbing solution which cools it to 50° - 90°C and which humidifies said waste gas by saturating or super saturating the gas with moisture.
Claim 4
Dependent Claim
25 words
The process of claim 1, wherein the concentration of said absorbent in said first absorbing solution is in the range of 0.1 - 10 wt.%.
Claim 5
Dependent Claim
63 words
The process of claim 1, wherein an alkali metal sulfite or bisulfite is produced in said first absorbing solution by contacting the waste gas with said first absorbing solution to which is continuously added an alkali metal hydroxide or carbonate, and wherein the oxides of selenium are principally removed from said waste gas by contacting the waste gas with said first absorbing solution.
Claim 6
Dependent Claim
42 words
The process of claim 1, wherein said glass fiber filter containing residual selenium thereon is washed with a second absorbing solution which comprises an alkali metal sulfite or bisulfite solution to dissolve and remove said collected selenium from said glass fiber filter.
Claim 7
Dependent Claim
56 words
The process of claim 5, wherein the pH of said first absorbing solution after contact with said waste gas is adjusted to 6 - 9, and the pH of said second absorbing solution discharged after washing said glass fiber filter is adjusted to from 5 - 7 in order to prevent the formation of sodium carbonate.
Claim 8
Dependent Claim
45 words
The process of claim 5, wherein said first and second absorbing solutions discharged after contact with said waste gas and after washing said glass fiber filters respectively are combined and adjusted to a pH of from 1 - 3 by the addition of an acid.
References Cited (Backward Citations)
US1271899A
Cited
US2349697A
Cited
US2889206A
Cited
US2809092A
Cited
US2981603A
Cited
US3179497A
Cited
US3558268A
Cited
US3723595A
Cited
US3739549A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-06-29 | 1979-12-29 | 1980-06-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-06-29 | 1983-12-29 | 1984-06-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-06-29 | 1987-12-29 | 1988-06-29 | $7700.00 | Window Closed / Lapsed |