Self-extinguishing polystyrene resin composition
Assignee: Daicel Corp
•
Filing: 1974-09-06
•
Granted: 1976-06-29
•
Expires: 1994-09-06
Abstract
Abstract A polystyrene resin composition is prepared by adding to polystyrene resin, a mixture of (a) tricresyl phosphate and/or triphenyl phosphate and (b) a carbonate oligomer of 2,2-(4-4'-dihydroxy-3,3,',5,5'-tetrabromodiphenyl) propane which is terminated at its ends with a monofunctional phenol. These compounds are mixed with the oligomer in a selected mole ratio. The resin composition is self-extinguishing and possesses excellent thermal resistance, without diminution of the other original desireable properties of the resin.
Inventors
- 👤 Yuzo Sonoyama
- 👤 Akira Ohi
- 👤 Yukio Hozumi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 07:36
CPC Classifications
C; C09; C09K; C09K21/00; C09K21/14; C08; C08K; C08K5/00; C08K5/04; C08K5/10; C08K5/109; C08K5/49; C08K5/51; C08K5/52; C08K5/521; C08K5/523; C08L; C08L25/00; C08L25/02; C08L55/00; C08L55/02; C08L2205/00; C08L2205/02; C08L69/00
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
127 words
A self-extinguishing resin composition which comprises a homogeneous mixture of 1. polystyrene resin, and 2. flame retarding agent in an amount sufficient to impart a self-extinguishing property to the resin composition, said flame retarding agent consisting essentially of a. a material selected from the group consisting of tricresyl phosphate, triphenyl phosphate and mixtures thereof, and b. a carbonate oligomer of 2,2 -- 4,4'-dihydroxy-3,3', 5,5'-tetrabromodiphenyl) propane having the formula: ##SPC2## wherein R is hydrogen or alkyl having from 1 to 6 carbon atoms, x is an integer of 1 to 5 and n is an integer of 2 to 10; the molar ratio of ingredient (a) : ingredient (b) being about 1(n):1, said resin composition containing from 3 to 25 percent by weight of said flame retarding agent.
Claim 2
Dependent Claim
127 words
A self-extinguishing resin composition which comprises a homogeneous mixture of 1. polystyrene resin, and 2. flame retarding agent in an amount sufficient to impart a self-extinguishing property to the resin composition, said flame retarding agent consisting essentially of a. a material selected from the group consisting of tricresyl phosphate, triphenyl phosphate and mixtures thereof, and b. a carbonate oligomer of 2,2 -- 4,4'-dihydroxy-3,3', 5,5'-tetrabromodiphenyl) propane having the formula: ##SPC2## wherein R is hydrogen or alkyl having from 1 to 6 carbon atoms, x is an integer of 1 to 5 and n is an integer of 2 to 10; the molar ratio of ingredient (a) : ingredient (b) being about 1(n):1, said resin composition containing from 3 to 25 percent by weight of said flame retarding agent.
Claim 3
Dependent Claim
27 words
A self-extinguishing resin composition according to claim 1 in which n is 3 and said fire retarding agent contains from 70 to 80 mole percent of (a).
Claim 4
Dependent Claim
27 words
A self-extinguishing resin composition according to claim 1 in which n is 6, and said fire retarding agent contains from 80 to 90 mole percent of (a).
Claim 5
Dependent Claim
32 words
A self-extinguishing resin composition according to claim 1, in which the total amount of flame-retarding agent does not exceed 20 percent by weight, based on the total weight of the resin composition.
Claim 6
Dependent Claim
19 words
A self-extinguishing resin composition according to claim 1, in which the flame-retarding agent is blended in the polystyrene resin.
Claim 7
Dependent Claim
33 words
A self-extinguishing resin composition according to claim 1, in which the ingredient (a) is added during polymerization of the polystyrene resin and ingredient (b) is blended in the resin after polymerization is completed.
Claim 8
Dependent Claim
55 words
A self-extinguishing resin composition according to claim 1, wherein the polystyrene resin is a member of the group consisting of polymers of (1) styrene, (2) α -alkyl-substituted styrene, (3) nuclear substituted styrene; and copolymers of (1), (2) or (3) with at least one member of the group consisting of vinyl compounds and conjugated dialkene compounds.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-06-29 | 1979-12-29 | 1980-06-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-06-29 | 1983-12-29 | 1984-06-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-06-29 | 1987-12-29 | 1988-06-29 | $7700.00 | Window Closed / Lapsed |