Method for improving adherence of phosphor-photobinder layer during luminescent-screen making
Assignee: RCA Licensing Corp
•
Filing: 1974-11-25
•
Granted: 1976-06-29
•
Expires: 1994-11-25
Abstract
Abstract The inner surface of a faceplate panel of a cathode-ray tube is cleaned and then precoated with water-insoluble, organic, polymeric particles, the precoating having a weight of 0.08 to 0.80 and preferably 0.20 to 0.40 mg/cm2. A subsequently applied phosphor-photobinder coating is exposed to a light image and then developed with a turbulent quantity of aqueous liquid. The phosphor-photobinder coating exhibits improved adherence during the developing step due to the presence of the precoating.
Inventors
- 👤 Stanley Arthur Harper
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 17:59
CPC Classifications
C; C03; C03C; C03C17/00; C03C17/34; C03C17/3405; G; G03; G03F; G03F7/00; G03F7/004; G03F7/09; G03F7/11; H; H01; H01J; H01J9/00; H01J9/20; H01J9/22; H01J9/227; H01J9/2271; C03C2217/00; C03C2217/40; C03C2217/42; C03C2217/43; C03C2217/46; C03C2217/48; Y; Y10; Y10S; Y10S430/00; Y10S430/136
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
102 words
A method for preparing a luminescent screen upon a glass surface comprising a. adhering to said glass surface a dry, non-photosensitive precoating consisting essentially of discreet water-insoluble, organic, polymeric particles, said precoating having a weight of about 0.08 to 0.80 milligrams per square centimeter, b. depositing upon said precoating a layer of a slurry comprising phosphor particles and a photosensitive binder therefor, c. exposing said coating to a light image whereby to form in said coating selected regions of greater solubility and selected regions of lesser solubility, d. and then developing said exposed coating by selectively removing said regions of greater solubility.
Claim 2
Independent Claim
102 words
A method for preparing a luminescent screen upon a glass surface comprising a. adhering to said glass surface a dry, non-photosensitive precoating consisting essentially of discreet water-insoluble, organic, polymeric particles, said precoating having a weight of about 0.08 to 0.80 milligrams per square centimeter, b. depositing upon said precoating a layer of a slurry comprising phosphor particles and a photosensitive binder therefor, c. exposing said coating to a light image whereby to form in said coating selected regions of greater solubility and selected regions of lesser solubility, d. and then developing said exposed coating by selectively removing said regions of greater solubility.
Claim 3
Dependent Claim
59 words
The method defined in claim 1 wherein step (a) includes i. applying to said glass surface of a coating of an aqueous emulsion comprising 5 to 15 weight percent of said water-insoluble organic, polymeric particles which are rendered nondispersible in water when dried and which are volatilized when baked in air at about 400°C, and ii. drying said coating.
Claim 4
Dependent Claim
15 words
The method defined in claim 2 wherein said coating is dried at temperatures below 55°C.
Claim 5
Dependent Claim
25 words
The method defined in claim 2 wherein said polymeric particles consist essentially of polystyrene copolymer and are about 0.10 to 0.35 micron in average diameter.
Claim 6
Dependent Claim
22 words
The method defined in claim 2 wherein said emulsion includes up to 5 weight percent of water-insoluble particles of acrylic polymeric material.
Claim 7
Independent Claim
149 words
A method for preparing a luminescent screen upon a glass surface comprising a. applying to said glass surface a layer of an aqueous emulsion containing 5 to 15 weight percent of a water-insoluble polystyrene, b. drying said emulsion layer to produce a dry, non-photosensitive precoating consisting essentially of discrete water-insoluble polymeric particles adhered to said glass surface, said precoating having a weight of about 0.08 to 0.80 milligrams per square centimeter, c. depositing on said precoating a layer of a slurry comprising phosphor particles, polyvinyl alcohol, and a photosensitizer therefor, d. drying said slurry layer to produce a coating on said precoating, e. exposing said coating to a light image to produce selected regions of greater solubility and selected regions of lesser solubility in said coating, f. and then developing said coating by applying thereto a turbulent quantity of aqueous liquid to selectively remove said regions of greater solubility.
Claim 8
Independent Claim
149 words
A method for preparing a luminescent screen upon a glass surface comprising a. applying to said glass surface a layer of an aqueous emulsion containing 5 to 15 weight percent of a water-insoluble polystyrene, b. drying said emulsion layer to produce a dry, non-photosensitive precoating consisting essentially of discrete water-insoluble polymeric particles adhered to said glass surface, said precoating having a weight of about 0.08 to 0.80 milligrams per square centimeter, c. depositing on said precoating a layer of a slurry comprising phosphor particles, polyvinyl alcohol, and a photosensitizer therefor, d. drying said slurry layer to produce a coating on said precoating, e. exposing said coating to a light image to produce selected regions of greater solubility and selected regions of lesser solubility in said coating, f. and then developing said coating by applying thereto a turbulent quantity of aqueous liquid to selectively remove said regions of greater solubility.
Claim 9
Dependent Claim
22 words
The method defined in claim 6 wherein precoating weight is in the range of about 0.20 to 0.40 milligrams per square centimeter.
Claim 10
Dependent Claim
27 words
The method defined in claim 6 wherein said emulsion includes a proportion of water-insoluble acrylic copolymer up to about 36 weight percent of the polystyrene particles present.
Claim 11
Dependent Claim
22 words
The method defined in claim 6 wherein said coating has a weight of about 4 to 6 milligrams phosphor per square centimeter.
Claim 12
Dependent Claim
23 words
The method defined in claim 6 wherein said developing step includes applying a pressure spray of aqueous developing liquid to said exposed coating.
References Cited (Backward Citations)
US2785331A
Cited
US3275466A
Cited
US3481733A
Cited
US3440077A
Cited
US3483010A
Cited
US3582389A
Cited
US3623867A
Cited
US3661580A
Cited
US3703401A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-06-29 | 1979-12-29 | 1980-06-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-06-29 | 1983-12-29 | 1984-06-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-06-29 | 1987-12-29 | 1988-06-29 | $7700.00 | Window Closed / Lapsed |