Chemically opening chrysotile asbestos and encapsulating
Assignee: University of Toronto Innovations Foundation
•
Filing: 1973-01-19
•
Granted: 1976-06-22
•
Expires: 1993-01-19
Abstract
Abstract Chrysotile asbestos is chemically opened into the individual fibrils by soluble vinylic polymer polyelectrolytes containing carboxylic acid groups in aqueous media. Polyacrylic acids, polymethacrylic acids, maleic anhydride polymers and water-soluble copolymers thereof are preferred polyelectrolytes and form stable colloidal dispersions. The polyelectrolytes are neutralized to alkaline pH with inorganic or organic bases, but preferably with basic vinylic monomers when complete encapsulation is desired. By a further aspect of the invention the polyelectrolyte-coated fibrils in aqueous dispersion are encapsulated by copolymerization with (a) a basic vinylic comonomer (used for pH control) such as dimethylaminoethyl methacrylate, t-butylaminoethyl methacrylate or a vinylpyridine; and (b) a non-basic vinylic comonomer such as styrene, divinylbenzene, vinyl chloride or fluoride, vinyl acetate, methyl methacrylate, ethyl acrylate, acrylonitrile, and methacrylonitrile. The encapsulated fibrils are advantageous for forming reinforced composites including laminates and foamed or cellular products.
Inventors
- 👤 Marinos Xanthos
- 👤 Raymond T. Woodhams
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 15:12
CPC Classifications
D; D21; D21H; D21H11/00; D21H11/16; D21H11/18; C; C04; C04B; C04B20/00; C04B20/02; C04B20/08; D21H13/00; D21H13/36; D21H13/38; D21H13/42; D21H5/00; D21H5/12; D21H5/1236; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24802; Y10T428/24893; Y10T428/29; Y10T428/2982; Y10T428/2991; Y10T428/2993; Y10T428/2998
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
88 words
A method of chemically opening chrysotile asbestos into individual fibrils and at least partially encapsulating with polymer comprising: a. physically breaking up the asbestos and shredding the fibres to a preliminary stage, b. dispersing the resulting asbestos shreds in an aqueous alkaline medium of alkaline pH up to about 10 containing a soluble vinylic polymer polyelectrolyte having free carboxylic acid groups, with agitation to chemically open and coat the individual asbestos fibrils, and c. insolubilizing the polyelectrolyte on the fibrils, and separating coated fibrils from the aqueous medium.
Claim 2
Independent Claim
88 words
A method of chemically opening chrysotile asbestos into individual fibrils and at least partially encapsulating with polymer comprising: a. physically breaking up the asbestos and shredding the fibres to a preliminary stage, b. dispersing the resulting asbestos shreds in an aqueous alkaline medium of alkaline pH up to about 10 containing a soluble vinylic polymer polyelectrolyte having free carboxylic acid groups, with agitation to chemically open and coat the individual asbestos fibrils, and c. insolubilizing the polyelectrolyte on the fibrils, and separating coated fibrils from the aqueous medium.
Claim 3
Dependent Claim
28 words
The method of claim 1 wherein the polyelectrolyte is selected from the group consisting of polymers of acrylic acid, polymers of methacrylic acid, and copolymers of maleic anhydride.
Claim 4
Dependent Claim
17 words
The method of claim 1 wherein the pH of the aqueous medium is adjusted to about 8-10.
Claim 5
Dependent Claim
19 words
The method of claim 1 wherein the polyelectrolyte is insolubilized in (c) with an inorganic or volatile organic base.
Claim 6
Dependent Claim
20 words
The method of claim 1 wherein the polyelectrolyte on the fibrils is reacted and polymerized with a basic vinylic monomer.
Claim 7
Dependent Claim
44 words
The method of claim 1 wherein the polyelectrolyte is insolubilized and reacted and polymerized with both a basic vinylic comonomer and non-basic vinylic comonomer to encapsulate the individual fibrils with polymer, the weight ratio of basic to non-basic comonomer being at least about 0.33
Claim 8
Dependent Claim
119 words
A method of chemically opening chrysotile asbestos into individual fibrils and encapsulating the fibrils with polymer as in claim 1 comprising: a. physically breaking up the asbestos and shredding the fibres to a preliminary stage, b. dispersing the resulting asbestos shreds in an aqueous medium of pH about 8-10 containing both soluble vinylic polymer polyelectrolyte selected from the group consisting of polymers of acrylic acid, polymers of methacrylic acid, and copolymers of maleic anhydride and a basic vinylic monomer selected from the group consisting of dimethylaminoethyl methacrylate, t-butylaminoethyl methacrylate and a vinylpyridine, with agitation to chemically open and coat the individual asbestos fibrils, and c. insolubilizing the polyelectrolyte, polymerizing the monomer and separating the encapsulated fibrils from aqueous media.
Claim 9
Independent Claim
150 words
A method of chemically-opening chrysotile asbestos into individual fibrils and encapsulating the fibrils with polymer comprising: a. physically breaking up the asbestos and shredding the fibres to a preliminary stage, b. dispersing the resulting asbestos shreds in an aqueous medium of alkaline pH up to about 10 containing i. a soluble vinylic polymer polyelectrolyte selected from the group consisting of polymers of acrylic acid, polymers of methacrylic acid, and copolymers of maleic anhydride; ii. basic vinylic monomer selected from the group consisting of dimethylaminoethyl methacrylate, t-butylaminoethyl methacrylate and a vinylpyridine; and iii. non-basic vinylic comonomer and a polymerization initiator therefor; to chemically open and coat the individual asbestos fibrils, the weight ratio of basic monomer to non-basic comonomer being at least about 0.33, and c. insolubilizing the polyelectrolyte, copolymerizing the basic and non-basic monomers to encapsulate the fibrils with polyelectrolyte and copolymer, and separating the encapsulated fibrils from aqueous media.
Claim 10
Independent Claim
150 words
A method of chemically-opening chrysotile asbestos into individual fibrils and encapsulating the fibrils with polymer comprising: a. physically breaking up the asbestos and shredding the fibres to a preliminary stage, b. dispersing the resulting asbestos shreds in an aqueous medium of alkaline pH up to about 10 containing i. a soluble vinylic polymer polyelectrolyte selected from the group consisting of polymers of acrylic acid, polymers of methacrylic acid, and copolymers of maleic anhydride; ii. basic vinylic monomer selected from the group consisting of dimethylaminoethyl methacrylate, t-butylaminoethyl methacrylate and a vinylpyridine; and iii. non-basic vinylic comonomer and a polymerization initiator therefor; to chemically open and coat the individual asbestos fibrils, the weight ratio of basic monomer to non-basic comonomer being at least about 0.33, and c. insolubilizing the polyelectrolyte, copolymerizing the basic and non-basic monomers to encapsulate the fibrils with polyelectrolyte and copolymer, and separating the encapsulated fibrils from aqueous media.
Claim 11
Dependent Claim
18 words
The method of claim 8 wherein the non-basic monomer is a styrene and an oil-soluble initiator is used.
Claim 12
Dependent Claim
46 words
Chemically-opened, chrysotile asbestos fibrils encapsulated with polymer comprising a vinylic polymer polyelectrolyte and polymerized basic vinylic monomer, the polyelectrolyte having carboxylic acid groups neutralized by the basic groups of said monomer, the amount of polymer being from about 2 to 100% by weight of the asbestos.
Claim 13
Dependent Claim
46 words
Chemically-opened, chrysotile asbestos fibrils encapsulated with polymer comprising a vinylic polymer polyelectrolyte and polymerized basic vinylic monomer, the polyelectrolyte having carboxylic acid groups neutralized by the basic groups of said monomer, the amount of polymer being from about 2 to 100% by weight of the asbestos.
Claim 14
Dependent Claim
25 words
The encapsulated fibrils of claim 10 wherein the basic vinylic monomer is selected from the group consisting of dimethylaminoethyl methacrylate, t-butylaminoethyl methacrylate and a vinylpyridine.
Claim 15
Dependent Claim
18 words
The encapsulated fibrils of claim 10 wherein the polymer comprises non-basic vinylic monomer copolymerized with said basic monomer.
Claim 16
Dependent Claim
29 words
The encapsulated fibrils of claim 10 wherein the polyelectrolyte is selected from the group consisting of polymers of acrylic acid, polymers of methacrylic acid, and copolymers of maleic anhydride.
References Cited (Backward Citations)
US2609313A
Cited
US2940892A
Cited
US3409499A
Cited
US3410751A
Cited
US3582460A
Cited
US3535150A
Cited
US3519591A
Cited
US3635879A
Cited
US3721637A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-06-22 | 1979-12-22 | 1980-06-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-06-22 | 1983-12-22 | 1984-06-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-06-22 | 1987-12-22 | 1988-06-22 | $7700.00 | Window Closed / Lapsed |