Assignee: Mitsubishi Chemical Corp
•
Filing: 1974-12-03
•
Granted: 1976-06-22
•
Expires: 1994-12-03
Abstract
Abstract A flame-resistant resin composition consisting essentially of 100 parts by weight of polytetramethylene terephthalate, 3 to 40 parts by weight of a flame retardant represented by the general formula, WHEREIN N + M IS A NUMBER OF 0 TO 10; X is a bromine or chlorine atom; and i, j, k and l are individually an integer of 1 to 4, and antimony trioxide, the weight ratio of said flame retardant to said antimony trioxide being in the range of from 0.25 to 6. This composition is excellent in mechanical properties, thermal properties and moldability, and causes no spread of fire to other materials even when dripped at the time of combustion.
Inventors
- 👤 Kazumasa Kamada
- 👤 Ryoji Handa
- 👤 Masafumi Hongo
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 21:07
CPC Classifications
C; C08; C08K; C08K5/00; C08K5/04; C08K5/15; C08K5/151; C08K5/1515; C08L; C08L67/00; C08L67/02; Y; Y10; Y10S; Y10S260/00; Y10S260/24
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
94 words
A flame-resistant resin composition consisting essentially of 100 parts by weight of a polytetramethylene terephthalate, 3 to 40 parts by weight of a flame retardant represented by the general formula (I), ##SPC5## wherein n + m, which represents an average degree of polymerization, is a number of 0 to 10; X is a bromine or chlorine atom; and i, j, k and l are individually an integer of 1 to 4, and antimony trioxide, the weight ratio of said flame retardant to said antimony trioxide being in the range of from 0.25 to 6.
Claim 2
Dependent Claim
94 words
A flame-resistant resin composition consisting essentially of 100 parts by weight of a polytetramethylene terephthalate, 3 to 40 parts by weight of a flame retardant represented by the general formula (I), ##SPC5## wherein n + m, which represents an average degree of polymerization, is a number of 0 to 10; X is a bromine or chlorine atom; and i, j, k and l are individually an integer of 1 to 4, and antimony trioxide, the weight ratio of said flame retardant to said antimony trioxide being in the range of from 0.25 to 6.
Claim 3
Dependent Claim
33 words
A composition according to claim 1, wherein the flame retardant is a compound of the general formula (I), in which m = 0, and i = j = k = l = 2.
Claim 4
Dependent Claim
32 words
A composition according to claim 1, wherein the polytetramethylene terephthalate has an intrinsic viscosity of 0.6 to 3 dl/g as measured at 25°C. in an equal weight mixture of tetrachloroethane and phenol.
Claim 5
Dependent Claim
25 words
A composition according to claim 1, wherein the amount of the flame retardant of the general formula (I) is 5 to 25 parts by weight.
Claim 6
Dependent Claim
45 words
A composition according to claim 1, wherein the average degree of polymerization n + m in the general formula (I) is 1.5 to 10, and the weight ratio of the flame retardant to the antimony trioxide is in the range of from 0,25 to 5.
Claim 7
Dependent Claim
47 words
A composition according to claim 1, wherein the average degree of polymerization n + m in the general formula (I) is less than 1.5 including 0, and the weight ratio of the flame retardant to the antimony trioxide is in the range of from 0.25 to 6.
Claim 8
Dependent Claim
27 words
A composition according to claim 4, wherein the weight ratio of the flame retardant to the antimony trioxide is in the range of from 0.5 to 4.
Claim 9
Dependent Claim
19 words
A composition according to claim 1, wherein the polytetramethylene terephthalate contains less than 40% by weight of other polymer.
Claim 10
Dependent Claim
24 words
A composition according to claim 8, wherein the said other polymer is polycarbonate, polystyrene, polymethyl methacrylate, polyethylene terephthalate, polyethylene, polypropylene, ABS resin or nylon.
Claim 11
Dependent Claim
101 words
A composition according to claim 1, wherein the polytetramethylene terephthalate has an intrinsic viscosity of 0.9 - 2.0 dl/g as measured in an equal weight mixture of tetrachloroethane and phenol at 25°C and the flame retardant is represented by the formula (I) as defined in claim 1, provided that n = 0.1 - 5 and m = 0, the amount of the flame retardant being 13 - 20 parts by weight per 100 parts by weight of the polytetramethylene terephthalate, and the weight ratio of the flame retardant to the antimony trioxide being in the range of from 1.4 to 4.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-06-22 | 1979-12-22 | 1980-06-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-06-22 | 1983-12-22 | 1984-06-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-06-22 | 1987-12-22 | 1988-06-22 | $7700.00 | Window Closed / Lapsed |