Water swellable poly(alkylene oxide)
Assignee: Glad Products Co
•
Filing: 1974-10-30
•
Granted: 1976-06-15
•
Expires: 1994-10-30
Abstract
Abstract A process for producing water swellable poly(alkylene oxide) which comprises introducing into a reaction zone an admixture of poly(alkylene oxide) having a molecular weight of at least 100,000 and an inert hydrocarbon solvent containing a free radical catalyst; adding to said reaction zone acrylic acid, heating said reaction zone at a temperature within the range of about 40 DEG C to about 100 DEG C for a time sufficient to produce said water swellable poly(alkylene oxide), and thereafter recovering said water swellable poly(alkylene oxide) from said reaction zone.
Inventors
- 👤 Nan S. Chu
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 10:39
CPC Classifications
C; C08; C08G; C08G65/00; C08G65/02; C08G65/32; C08G65/329; C08G65/331; C08G65/332; C08G65/3322; A; A61; A61L; A61L15/00; A61L15/16; A61L15/42; A61L15/60; C08F; C08F283/00; C08F283/06
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
102 words
A process for producing water swellable poly(alkylene oxide) which comprises introducing into a reaction zone an admixture of poly(alkylene oxide), having a molecular weight of at least 100,000 and an inert hydrocarbon solvent containing a free radical catalyst; adding to said reaction zone from 1% to 50% of acrylic acid, based on the weight of poly(alkylene oxide), the major portion to be added continuously, heating said reaction zone at a temperature within the range of 40°C to about 100°C for a time sufficient to produce said water swellable poly(alkylene oxide), and thereafter recovering said water swellable poly(alkylene oxide) from said reaction zone.
Claim 2
Dependent Claim
102 words
A process for producing water swellable poly(alkylene oxide) which comprises introducing into a reaction zone an admixture of poly(alkylene oxide), having a molecular weight of at least 100,000 and an inert hydrocarbon solvent containing a free radical catalyst; adding to said reaction zone from 1% to 50% of acrylic acid, based on the weight of poly(alkylene oxide), the major portion to be added continuously, heating said reaction zone at a temperature within the range of 40°C to about 100°C for a time sufficient to produce said water swellable poly(alkylene oxide), and thereafter recovering said water swellable poly(alkylene oxide) from said reaction zone.
Claim 3
Dependent Claim
13 words
A process according to claim 1 wherein said poly(alkylene oxide) is poly(ethylene oxide).
Claim 4
Dependent Claim
53 words
A process according to claim 2 wherein a minor amount of acrylic acid is present in said reaction zone with said poly(ethylene oxide), solvent and catalyst and wherein the balance of acrylic acid used is continually added to the reaction mixture containing said poly(ethylene oxide), solvent, catalyst and minor amount of acrylic acid.
Claim 5
Dependent Claim
16 words
A process according to claim 3 wherein said inert hydrocarbon solvent is an aliphatic hydrocarbon solvent.
Claim 6
Dependent Claim
14 words
A process according to claim 3 wherein said free radical catalyst is acetyl peroxide.
Claim 7
Dependent Claim
24 words
A process according to claim 3 wherein the temperature maintained within the reaction zone is within the range of about 50°C to about 80°C.
Claim 8
Dependent Claim
18 words
A process according to claim 2 including the additional step of partially neutralizing said water swellable poly(ethylene oxide).
Claim 9
Dependent Claim
32 words
A product prepared by the process according to claim 7 wherein the resultant pH of said partially neutralized water swellable poly(ethylene oxide) is within the range of about 5.5 to about 6.0.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-06-15 | 1979-12-15 | 1980-06-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-06-15 | 1983-12-15 | 1984-06-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-06-15 | 1987-12-15 | 1988-06-15 | $7700.00 | Window Closed / Lapsed |