Graft copolymer in polyamide polyethylene blends
Assignee: EIDP Inc
•
Filing: 1974-11-13
•
Granted: 1976-06-15
•
Expires: 1994-11-13
Abstract
Abstract Polymeric blend of 60 to 90 parts by weight of a polyamide, e.g., polyhexamethylene adipamide or polycaprolactam, and 40 to 10 parts by weight of polyethylene or crystalline copolymer of ethylene, e.g., ethylene and methacrylic acid, characterized in that there is present in the blend 1.8 to 8.0 parts by weight of a thermoplastic graft copolymer consisting essentially of a trunk copolymer derived from ethylene and a comonomer providing amine-reactive sites and polycaprolactam side chains linked to said reactive sites through amide or imide linkages. The modified blends are useful as injection molding resins, for wire jacketing, etc.
Inventors
- 👤 Howard Warner Starkweather, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 21:15
CPC Classifications
C; C08; C08L; C08L77/00
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
170 words
A polymeric blend comprising 60 to 90 parts by weight of a polyamide selected from the group consisting of polyhexamethylene adipamide, polycaprolactam and copolymers thereof and 40 to 10 parts by weight of polyethylene, characterized in that there is present in the blend 1.8 to 8.0 parts by weight of a plastic graft copolymer consisting essentially of a trunk copolymer derived from 70 to 99 percent by weight ethylene and a comonomer providing amine-reactive sites and polycaprolactam side chains having an average degree of polymerization of about 5 to 30 and having end groups selected from the class consisting of N-alkyl amide where alkyl is in the range of 1 to 20 carbon atoms and carboxylic acid, said side chains being linked to said reactive sites through amide or imide linkages, said graft copolymer having a polyamide content of 15 to 50 percent by weight based on the weight of graft copolymer and having two DTA melting points, one at 80° to 115°C. and the other at at least 165°C.
Claim 2
Dependent Claim
170 words
A polymeric blend comprising 60 to 90 parts by weight of a polyamide selected from the group consisting of polyhexamethylene adipamide, polycaprolactam and copolymers thereof and 40 to 10 parts by weight of polyethylene, characterized in that there is present in the blend 1.8 to 8.0 parts by weight of a plastic graft copolymer consisting essentially of a trunk copolymer derived from 70 to 99 percent by weight ethylene and a comonomer providing amine-reactive sites and polycaprolactam side chains having an average degree of polymerization of about 5 to 30 and having end groups selected from the class consisting of N-alkyl amide where alkyl is in the range of 1 to 20 carbon atoms and carboxylic acid, said side chains being linked to said reactive sites through amide or imide linkages, said graft copolymer having a polyamide content of 15 to 50 percent by weight based on the weight of graft copolymer and having two DTA melting points, one at 80° to 115°C. and the other at at least 165°C.
Claim 3
Dependent Claim
47 words
A blend according to claim 1 wherein the comonomer providing amine-reactive sites is selected from the group consisting of an anhydride group, a vicinal pair of carboxylic groups, and a carboxylic group adjacent to an alkoxycarbonyl group wherein the alkoxy group contains up to 20 carbon atoms.
Claim 4
Dependent Claim
18 words
A blend according to claim 1 wherein the trunk copolymer has a melt index of 5 to 200.
Claim 5
Dependent Claim
30 words
A blend according to claim 3 wherein the caprolactam side chains are present in the amount of 15 to 35 percent by weight based on the weight of graft copolymer.
Claim 6
Dependent Claim
26 words
A blend according to claim 1 wherein the non-reactive end groups are N-alkyl amide wherein alkyl is in the range of 4 to 6 carbon atoms.
Claim 7
Dependent Claim
37 words
A blend according to claim 1 wherein the comonomer of the trunk copolymer providing the amine-reactive sites is selected from the group consisting of maleic anhydride, half ester of maleic acid and half ester of itaconic acid.
Claim 8
Dependent Claim
17 words
A blend according to claim 1 wherein the trunk copolymer is derived from ethylene and maleic anhydride.
Claim 9
Dependent Claim
18 words
A blend according to claim 1 wherein the trunk copolymer is derived from ethylene and ethyl hydrogen maleate.
Claim 10
Dependent Claim
19 words
A blend according to claim 1 wherein the trunk copolymer and polycaprolactam side chains are linked through imide linkages.
Claim 11
Dependent Claim
19 words
A blend according to claim 1 wherein the trunk copolymer and polycaprolactam side chains are linked through amide linkages.
Claim 12
Dependent Claim
39 words
A blend according to claim 4 comprising 75 parts by weight of polyamide, 25 parts by weight polyethylene and 2 parts by weight of graft copolymer in which the polycaprolactam branches have a degree of polymerization of about 7.
Claim 13
Dependent Claim
21 words
A blend according to claim 1 wherein flexural modulus of the graft copolymer at room temperature is at least 28,000 p.s.i.
Claim 14
Dependent Claim
12 words
A blend according to claim 1 wherein the polyamide is polyhexamethylene adipamide.
Claim 15
Dependent Claim
11 words
A blend according to claim 1 wherein the polyamide is polycaprolactam.
Claim 16
Dependent Claim
170 words
A polymeric blend comprising 60 to 90 parts by weight of a polyamide selected from the group consisting of polyhexamethylene adipamide, polycaprolactam and copolymers thereof and 40 to 10 parts by weight of polyethylene, characterized in that there is present in the blend 1.8 to 8.0 parts by weight of a plastic graft copolymer consisting essentially of a trunk copolymer derived from 70 to 99 percent by weight ethylene and a comonomer providing amine-reactive sites and polycaprolactam side chains having an average degree of polymerization of about 6 to 8 and having end groups selected from the class consisting of N-alkyl amide where alkyl is in the range of 1 to 20 carbon atoms and carboxylic acid, said side chains being linked to said reactive sites through amide or imide linkages, said graft copolymer having a polyamide content of 15 to 50 percent by weight based on the weight of graft copolymer and having two DTA melting points, one at 80° to 115°C. and the other at at least 165°C.
Claim 17
Dependent Claim
170 words
A polymeric blend comprising 60 to 90 parts by weight of a polyamide selected from the group consisting of polyhexamethylene adipamide, polycaprolactam and copolymers thereof and 40 to 10 parts by weight of polyethylene, characterized in that there is present in the blend 1.8 to 8.0 parts by weight of a plastic graft copolymer consisting essentially of a trunk copolymer derived from 70 to 99 percent by weight ethylene and a comonomer providing amine-reactive sites and polycaprolactam side chains having an average degree of polymerization of about 6 to 8 and having end groups selected from the class consisting of N-alkyl amide where alkyl is in the range of 1 to 20 carbon atoms and carboxylic acid, said side chains being linked to said reactive sites through amide or imide linkages, said graft copolymer having a polyamide content of 15 to 50 percent by weight based on the weight of graft copolymer and having two DTA melting points, one at 80° to 115°C. and the other at at least 165°C.
References Cited (Backward Citations)
US2524045A
Cited
US3136738A
Cited
US3325561A
Cited
US3388186A
Cited
US3465059A
Cited
US3676400A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-06-15 | 1979-12-15 | 1980-06-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-06-15 | 1983-12-15 | 1984-06-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-06-15 | 1987-12-15 | 1988-06-15 | $7700.00 | Window Closed / Lapsed |