Method for treating polymeric substrates prior to plating
Assignee: Oxy Metal Industries Corp
•
Filing: 1975-03-11
•
Granted: 1976-06-08
•
Expires: 1995-03-11
Abstract
Abstract The present invention is directed to a process and composition effective prior to the electroless plating of polymeric substrates to substantially completely remove hexavalent chromium ions present in the aqueous acidic solution utilized to etch the plastic part. This novel result is accomplished by treating the polymeric substrate with a hydroxylamine salt in an acidic solution which may contain hydrochloric acid, sulfuric acid or partially neutralized acidic salts. The process and composition of this invention may be employed as a neutralizer prior to the activating step or subsequent thereto as an accelerator, or at both locations in the process for maximum effectiveness.
Inventors
- 👤 Warren Russell Doty
- 👤 Timothy James Kinney
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 20:45
CPC Classifications
C; C23; C23C; C23C18/00; C23C18/16; C23C18/18; C23C18/20; C23C18/28; H; H05; H05K; H05K3/00; H05K3/10; H05K3/18; H05K3/181; H05K3/38; H05K3/381
Claims Analysis
Total Claims: 4
Claim 1
Independent Claim
114 words
A method of treating a polymeric plastic substrate prior to plating a surface thereof, which comprises etching a surface of the substrate with an aqueous acid solution containing therein hexavalent chromium ions, rinsing and neutralizing, activating the etched substrate surface by contact with an acidic tin-palladium complex medium, rinsing the activated surface and accelerating said activated and rinsed surface of the polymeric substrate, the improvement which comprises contacting the polymeric substrate, in either or both the neutralizing and accelerating step with a hydroxylamine salt in an acidic solution containing therein hydrochloric acid, sulfuric acid or partially neutralized acidic salts whereby the hexavalent chromium ions from the etching step are reduced to the trivalent state.
Claim 2
Independent Claim
114 words
A method of treating a polymeric plastic substrate prior to plating a surface thereof, which comprises etching a surface of the substrate with an aqueous acid solution containing therein hexavalent chromium ions, rinsing and neutralizing, activating the etched substrate surface by contact with an acidic tin-palladium complex medium, rinsing the activated surface and accelerating said activated and rinsed surface of the polymeric substrate, the improvement which comprises contacting the polymeric substrate, in either or both the neutralizing and accelerating step with a hydroxylamine salt in an acidic solution containing therein hydrochloric acid, sulfuric acid or partially neutralized acidic salts whereby the hexavalent chromium ions from the etching step are reduced to the trivalent state.
Claim 3
Dependent Claim
40 words
A method of treating a polymeric plastic substrate as defined in claim 1, in which the hydroxylamine salt is present in the amount of about 0.005 to 10 g/l and the acidic solution is from approximately 10 to 225 g/l.
Claim 4
Dependent Claim
53 words
A method of treating a polymeric plastic substrate as defined in claim 1, in which the hydroxylamine salt is selected from the group consisting of hydroxylamine hydrochloride, NH 2 OH.HCl, hydroxylammonium acid sulfate, NH 2 OH.H 2 SO 4 , hydroxylammonium sulfate, (NH 2 OH) 2 .H 2 SO 4 and related compounds.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-06-08 | 1979-12-08 | 1980-06-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-06-08 | 1983-12-08 | 1984-06-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-06-08 | 1987-12-08 | 1988-06-08 | $7700.00 | Window Closed / Lapsed |