Method of making ceramic semiconductor elements with ohmic contact surfaces
Assignee: Texas Instruments Inc
•
Filing: 1975-02-03
•
Granted: 1976-06-08
•
Expires: 1995-02-03
Abstract
Abstract Ceramic semiconductor elements having ohmic contact surfaces are made by dispersing bentonite clay in a bonding composition consisting of a metal powder in a phosphate-chromate-metal ion solution to form a thixotropic coating material, by screen printing the coating material onto limited surface areas of ceramic semiconductor bodies, and by heating the coated bodies for curing the coating material to form adherent ohmic contact layers on the limited surface areas of the ceramic bodies.
Inventors
- 👤 Peter G. Fuller
- 👤 Hans A. Stoeckler
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 20:36
CPC Classifications
H; H01; H01C; H01C17/00; H01C17/28; H01C17/281; H01C17/283
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
85 words
A method for forming a ceramic semiconductor element having ohmic contact surfaces thereon comprising the steps of combining bentonite clay with a bonding composition consisting essentially of a dispersion of a solid particulate material in an aqueous phosphate-chromate-metal ion solution to form a thixotropic coating material, screen-printing the coating material on selected limited surfaces of a ceramic semiconductor body, and heating said coated ceramic semiconductor body for heat curing said coating material to form ohmic contact layers in adherent relation to said ceramic semiconductor body.
Claim 2
Independent Claim
85 words
A method for forming a ceramic semiconductor element having ohmic contact surfaces thereon comprising the steps of combining bentonite clay with a bonding composition consisting essentially of a dispersion of a solid particulate material in an aqueous phosphate-chromate-metal ion solution to form a thixotropic coating material, screen-printing the coating material on selected limited surfaces of a ceramic semiconductor body, and heating said coated ceramic semiconductor body for heat curing said coating material to form ohmic contact layers in adherent relation to said ceramic semiconductor body.
Claim 3
Dependent Claim
24 words
A method as set forth in claim 1 wherein said coating material incorporates from about 3 to 18 percent by weight of bentonite clay.
Claim 4
Dependent Claim
33 words
A method as set forth in claim 2 wherein said coated ceramic semiconductor body is heated to a temperature from about 625° to 680°C. for a period from about 10 to 20 minutes.
Claim 5
Dependent Claim
25 words
A method as set forth in claim 3 wherein an additional metal coating is formed on said ohmic contact layers for improving the solderability thereof.
Claim 6
Dependent Claim
54 words
A method as set forth in claim 4 wherein a metal-containing glass frit is deposited over the coating material screen-printed onto the ceramic body before said heat curing of said coating material and wherein said glass frit is fused during said heat-curing of said coating material for improving solderability of said ohmic contact layers.
Claim 7
Dependent Claim
39 words
A method as set forth in claim 4 wherein a metal containing glass frit is deposited over said ohmic contact layers and is subsequently heated for fusing said glass frit to improve the solderability of said ohmic contact layers.
References Cited (Backward Citations)
US3248251A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-06-08 | 1979-12-08 | 1980-06-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-06-08 | 1983-12-08 | 1984-06-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-06-08 | 1987-12-08 | 1988-06-08 | $7700.00 | Window Closed / Lapsed |