Method of manufacturing a cap-sensitive and non-sensitive aqueous gel suspension explosive
Assignee: SLURRY EXPLOSIVE Corp A CORPORATION OF OK
•
Filing: 1975-03-10
•
Granted: 1976-06-08
•
Expires: 1995-03-10
Abstract
Abstract Non-cap sensitive aqueous gel explosives containing no suspended solid fuels are made by combining water, hexamethylenetetramine, ammonium nitrate, sodium nitrate, ammonium perchlorate and nitric acid, along with sufficient polysaccharide gum to thicken the mixture. These explosives are rendered cap sensitive by mixing therewith paint grade aluminum powder or other conventional sensitizing agents. According to a preferred procedure, a cap sensitive aqueous gel explosive is made by a procedure in which nitric acid and aqueous hexamethylenetetramine solution are first combined under controlled conditions of temperature and pH and ammonium nitrate, sodium nitrate, ammonium perchlorate, thickening agent and aluminum powder are added in controlled amounts in a specified order. The products possess cap sensitivity, even at temperatures as low as minus 23°C.
Inventors
- 👤 Edwin G. Marhofer
- 👤 Mike L. Marrello
- 👤 Glenn E. Tolle
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 15:20
CPC Classifications
C; C06; C06B; C06B47/00; C06B47/14
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
192 words
The method of manufacturing a cap-sensitive aqueous gel suspension explosive consisting essentially of the steps: a. Mixing with a 30 to 40 weight percent aqueous solution of hexamethylenetetramine sufficient nitric acid to obtain a pH of 5.0 to 5.3, while controlling the temperature of the resulting mixture so that it does not rise above 66°C, so as to produce an aqueous solution in which the hexamethylenetetramine content is from 25 to 35 weight percent; then dissolving in this solution sufficient ammonium perchlorate to yield a concentration of from 5.0 to 6.0 percent, sufficient sodium nitrate to yield a concentration of 8.0 to 9.0 percent and sufficient ammonium nitrate to yield a concentration of 30 to 45 percent in the resulting solution; b. into each 100 parts of the solution resulting from step (a) mixing thoroughly 60 to 65 parts by weight of finely ground ammonium nitrate and sufficient polysaccharide gum and crosslinking agent to thicken the mixture to a gel-like consistency; c. after the mixture produced in step (b) has become thickened, mixing from 6 to 8 parts of paint pigment grade aluminum powder therewith until the mixture is uniform in appearance.
Claim 2
Independent Claim
192 words
The method of manufacturing a cap-sensitive aqueous gel suspension explosive consisting essentially of the steps: a. Mixing with a 30 to 40 weight percent aqueous solution of hexamethylenetetramine sufficient nitric acid to obtain a pH of 5.0 to 5.3, while controlling the temperature of the resulting mixture so that it does not rise above 66°C, so as to produce an aqueous solution in which the hexamethylenetetramine content is from 25 to 35 weight percent; then dissolving in this solution sufficient ammonium perchlorate to yield a concentration of from 5.0 to 6.0 percent, sufficient sodium nitrate to yield a concentration of 8.0 to 9.0 percent and sufficient ammonium nitrate to yield a concentration of 30 to 45 percent in the resulting solution; b. into each 100 parts of the solution resulting from step (a) mixing thoroughly 60 to 65 parts by weight of finely ground ammonium nitrate and sufficient polysaccharide gum and crosslinking agent to thicken the mixture to a gel-like consistency; c. after the mixture produced in step (b) has become thickened, mixing from 6 to 8 parts of paint pigment grade aluminum powder therewith until the mixture is uniform in appearance.
Claim 3
Dependent Claim
12 words
The cap-sensitive explosive product made according to the method of claim 1.
Claim 4
Dependent Claim
48 words
The cap-sensitive explosive product made according to the method of claim 1 composed of 9.5 percent hexamethylenetetramine, 2.7 percent nitric acid, 57.5 percent ammonium nitrate, 5 percent sodium nitrate, 3 percent ammonium perchlorate, 4 percent paint pigment grade aluminum powder, 1 percent guar gum with crosslinker and water.
Claim 5
Independent Claim
131 words
The method of manufacturing a non-cap sensitive aqueous gel explosive containing no suspended solid fuel consisting essentially of the steps: a. preparing a mother liquor consisting of 26 to 36 weight percent water, from 14 to 24 weight percent hexamethylenetetramine, from 30 weight percent to a sufficient quantity of ammonium nitrate to saturate the solution, from 5 to 15 weight percent ammonium perchlorate and sufficient nitric acid to obtain a pH of 4.0 to 6.5 and, b. adding from 80 to 175 parts of particulate ammonium nitrate to each 100 parts of the mother liquor prepared in step (a) so as to bring the total water content of the resulting composition to within 13 to 18 weight percent, along with sufficient polysaccharide gum to thicken the mixture to a gel consistency.
Claim 6
Independent Claim
131 words
The method of manufacturing a non-cap sensitive aqueous gel explosive containing no suspended solid fuel consisting essentially of the steps: a. preparing a mother liquor consisting of 26 to 36 weight percent water, from 14 to 24 weight percent hexamethylenetetramine, from 30 weight percent to a sufficient quantity of ammonium nitrate to saturate the solution, from 5 to 15 weight percent ammonium perchlorate and sufficient nitric acid to obtain a pH of 4.0 to 6.5 and, b. adding from 80 to 175 parts of particulate ammonium nitrate to each 100 parts of the mother liquor prepared in step (a) so as to bring the total water content of the resulting composition to within 13 to 18 weight percent, along with sufficient polysaccharide gum to thicken the mixture to a gel consistency.
Claim 7
Dependent Claim
13 words
The non-cap sensitive aqueous gel explosive made by the process of claim 4.
Claim 8
Dependent Claim
42 words
The non-cap sensitive aqueous gel explosive made by the process of claim 4 composed of 8.2 percent hexamethylenetetramine, 2.3 percent nitric acid, 66.7 percent ammonium nitrate, 4.3 percent sodium nitrate, 2.6 percent ammonium perchlorate, one percent guar gum with crosslinker and water.
References Cited (Backward Citations)
US3676236A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-06-08 | 1979-12-08 | 1980-06-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-06-08 | 1983-12-08 | 1984-06-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-06-08 | 1987-12-08 | 1988-06-08 | $7700.00 | Window Closed / Lapsed |