Method for improving brightness of kaolinite clays including iron pyrites

Claim 1

A method for preparing a brightened coating kaolin from a crude kaolinitic clay, discolored with contaminants including discoloring iron-based contaminants in the form of iron pyrites and sulfurous contaminants, comprising: subjecting said crude clay to comminution; k roasting said comminuted crude clay in an oxidizing atmosphere at a temperature from 400°C to 600°C for a period of about 2 hours, said temperature being sufficient to oxidize the pyrites but insufficient to drive off the chemically bound water from the kaolinite crystals, a substantial cessation of sulfurous fumes being noted at the completion of said roasting; converting at least a portion of the sulfurous contaminants to a form exhibiting increased magnetic susceptibility and increased solubility in chemical leachants selected from the group consisting of zinc dithionite, zinc salts of hydrosulfurous acid, sodium salts of hydrosulfurous acid and combinations thereof; thereafter forming an aqueous slurry of said roasted clay, said slurry being of about 40% solids; subjecting at least a portion of said slurry to a magnetic field having an intensity of at least 2.4 kilogauss and high field gradients for a period of about four minutes to separate at least part of said converted components; and thereafter subjecting said slurry to leaching employing from 0.1 to 2.5 weight percent of leach selected from the group consisting of zinc dithionite, zinc salts of hydrosulfurous acid, sodium salts of hydrosulfurous acid and combinations thereof and to filtration.

Claim 2

A method for preparing a brightened coating kaolin from a crude kaolinitic clay, discolored with contaminants including discoloring iron-based contaminants in the form of iron pyrites and sulfurous contaminants, comprising: subjecting said crude clay to comminution; k roasting said comminuted crude clay in an oxidizing atmosphere at a temperature from 400°C to 600°C for a period of about 2 hours, said temperature being sufficient to oxidize the pyrites but insufficient to drive off the chemically bound water from the kaolinite crystals, a substantial cessation of sulfurous fumes being noted at the completion of said roasting; converting at least a portion of the sulfurous contaminants to a form exhibiting increased magnetic susceptibility and increased solubility in chemical leachants selected from the group consisting of zinc dithionite, zinc salts of hydrosulfurous acid, sodium salts of hydrosulfurous acid and combinations thereof; thereafter forming an aqueous slurry of said roasted clay, said slurry being of about 40% solids; subjecting at least a portion of said slurry to a magnetic field having an intensity of at least 2.4 kilogauss and high field gradients for a period of about four minutes to separate at least part of said converted components; and thereafter subjecting said slurry to leaching employing from 0.1 to 2.5 weight percent of leach selected from the group consisting of zinc dithionite, zinc salts of hydrosulfurous acid, sodium salts of hydrosulfurous acid and combinations thereof and to filtration.