Cationic froth flotation process
Assignee: Hanna Mining Co
•
Filing: 1974-01-07
•
Granted: 1976-06-01
•
Expires: 1994-01-07
Abstract
Abstract An improved cationic froth flotation process for the separation of silicious gangue particles from oxidic iron mineral particles wherein the silicious particles are induced to float, and the iron mineral particles remain in suspension near the bottom of the flotation cell. More particularly, the invention relates to an improvement in the cationic froth flotation process by the incorporation of a small amount of a Group II metal salt as a modifier. The recovered iron concentrates obtained by the improved procedure of the invention are of a higher grade and contain lesser amounts of silicious material.
Inventors
- 👤 Mason L. Dicks
- 👤 James B. Morrow
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 12:25
CPC Classifications
B; B03; B03D; B03D1/00; B03D1/02; B03D1/001; B03D1/004; B03D1/008; B03D1/01; B03D1/016; B03D2201/00; B03D2201/02; B03D2201/06; B03D2203/00; B03D2203/02
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
105 words
In the method of beneficiating silicious iron ore by cationic froth flotation of the silicious gangue particles from the iron mineral particles in an aqueous pulp of such ore comprising the steps of desliming an aqueous slurry of said ore and thereafter subjecting an aqueous pulp of such ore to a froth-flotation treatment in the presence of a starch depressant, a cationic collector, and a frother, the improvement consisting essentially of the incorporation of a small amount of a Group II metal compound which is a halide, sulfate, or or, nitrate, salt into the pulp after the desliming step and prior to the froth-flotation treatment.
Claim 2
Dependent Claim
105 words
In the method of beneficiating silicious iron ore by cationic froth flotation of the silicious gangue particles from the iron mineral particles in an aqueous pulp of such ore comprising the steps of desliming an aqueous slurry of said ore and thereafter subjecting an aqueous pulp of such ore to a froth-flotation treatment in the presence of a starch depressant, a cationic collector, and a frother, the improvement consisting essentially of the incorporation of a small amount of a Group II metal compound which is a halide, sulfate, or or, nitrate, salt into the pulp after the desliming step and prior to the froth-flotation treatment.
Claim 3
Dependent Claim
28 words
The method of claim 1 wherein the pH of the pulp containing the cationic collector, starch, frother and Group II metal compound is maintained between 7.5 and 10.5.
Claim 4
Dependent Claim
17 words
The method of claim 1 wherein the Group II metal compound is a Group II metal halide.
Claim 5
Dependent Claim
17 words
The method of claim 1 wherein the Group II metal compound is a Group II metal sulfate.
Claim 6
Dependent Claim
27 words
The method of claim 1 wherein the Group II metal compound is incorporated in an amount up to about 3.6 pounds per long ton of crude ore.
Claim 7
Dependent Claim
12 words
The method of claim 1 wherein the cationic collector is an amine.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-06-01 | 1979-12-01 | 1980-06-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-06-01 | 1983-12-01 | 1984-06-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-06-01 | 1987-12-01 | 1988-06-01 | $7700.00 | Window Closed / Lapsed |