Process for producing a solid solution of aluminum oxide in silicon nitride
Assignee: University of Utah
•
Filing: 1974-04-29
•
Granted: 1976-06-01
•
Expires: 1994-04-29
Abstract
Abstract A method of producing a sinterable refractory material having a low coefficient of thermal expansion and comprising essentially a dispersion of aluminum oxide throughout a silicon nitride matrix, herein called SIALON. The process includes obtaining aluminum and silicon from generally readily available raw material sources.
Inventors
- 👤 Ivan B. Cutler
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 22:10
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/515; C04B35/58; C04B35/597; C01; C01B; C01B21/00; C01B21/082; C01B21/0821; C01B21/0826
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
184 words
A method of producing a refractory material consisting essentially of a solid solution of aluminum oxide in silicon nitride, the composition by weight percent being 15% to 70% aluminum oxide and 85% to 30% silicon nitride, the method comprising the steps of: obtaining silicon dioxide and aluminum oxide reactants selected from the group consisting of: clay having a composition by weight percent of 40% to 20% aluminum oxide and 46% to 70% silicon dioxide; a coked mixture of rice hulls and an aluminum source, the aluminum source being selected from the group consisting of clays formed by the geologic decomposition of aluminum compounds, oxides and salts of aluminum and aluminum metal, the concentration of aluminum not exceeding 20% by weight; and a precipitate having a composition by weight percent of 10% to 65% aluminum oxide and 35% to 90% silicon dioxide; placing the reactants in an enclosure; and heating the reactants to a temperature within the range on the order of about 1200°C to 1600°C in the presence of carbon and nitrogen until a solid solution of aluminum oxide in silicon nitride is produced.
Claim 2
Independent Claim
184 words
A method of producing a refractory material consisting essentially of a solid solution of aluminum oxide in silicon nitride, the composition by weight percent being 15% to 70% aluminum oxide and 85% to 30% silicon nitride, the method comprising the steps of: obtaining silicon dioxide and aluminum oxide reactants selected from the group consisting of: clay having a composition by weight percent of 40% to 20% aluminum oxide and 46% to 70% silicon dioxide; a coked mixture of rice hulls and an aluminum source, the aluminum source being selected from the group consisting of clays formed by the geologic decomposition of aluminum compounds, oxides and salts of aluminum and aluminum metal, the concentration of aluminum not exceeding 20% by weight; and a precipitate having a composition by weight percent of 10% to 65% aluminum oxide and 35% to 90% silicon dioxide; placing the reactants in an enclosure; and heating the reactants to a temperature within the range on the order of about 1200°C to 1600°C in the presence of carbon and nitrogen until a solid solution of aluminum oxide in silicon nitride is produced.
Claim 3
Dependent Claim
20 words
A method as defined in claim 1 wherein said obtaining step is further defined by dispersing carbon in said reactants.
Claim 4
Dependent Claim
28 words
A method as defined in claim 1 wherein said heating step further comprises flushing gaseous by-products of the reaction from the enclosure with excess quantities of nitrogen gas.
Claim 5
Independent Claim
234 words
A method of producing a sintered refractory product having a predetermined shape, the refractory material consisting essentially of a solid solution of aluminum oxide in silicon nitride, the composition by weight percent being 15% to 70% aluminum oxide and 85% to 30% silicon nitride, the method comprising the steps of: obtaining silicon dioxide and aluminum oxide reactants selected from the group consisting of: clay having a composition by weight percent of 40% to 20% aluminum oxide and 46% to 70% silicon dioxide; a coked mixture of rice hulls and an aluminum source, the aluminum source being selected from the group consisting of clays formed by the geologic decomposition of aluminum compounds, oxides and salts of aluminum and aluminum metal, the concentration of the aluminum not exceeding 20% by weight; and a precipitate having a composition by weight percent of 10% to 65% aluminum oxide and 35% to 90% silicon dioxide; placing the reactants in a chamber; heating the reactants to a temperature within the range on the order of about 1200°C to 1600°C in the presence of carbon until aluminum oxide and silicon carbide are produced; molding the aluminum oxide and silicon carbide into the predetermined shape; and sintering the molded shape at a temperature within the range on the order of about 1300°C to 1900°C and in the presence of nitrogen until a solid solution of aluminum oxide in silicon nitride is produced.
Claim 6
Independent Claim
234 words
A method of producing a sintered refractory product having a predetermined shape, the refractory material consisting essentially of a solid solution of aluminum oxide in silicon nitride, the composition by weight percent being 15% to 70% aluminum oxide and 85% to 30% silicon nitride, the method comprising the steps of: obtaining silicon dioxide and aluminum oxide reactants selected from the group consisting of: clay having a composition by weight percent of 40% to 20% aluminum oxide and 46% to 70% silicon dioxide; a coked mixture of rice hulls and an aluminum source, the aluminum source being selected from the group consisting of clays formed by the geologic decomposition of aluminum compounds, oxides and salts of aluminum and aluminum metal, the concentration of the aluminum not exceeding 20% by weight; and a precipitate having a composition by weight percent of 10% to 65% aluminum oxide and 35% to 90% silicon dioxide; placing the reactants in a chamber; heating the reactants to a temperature within the range on the order of about 1200°C to 1600°C in the presence of carbon until aluminum oxide and silicon carbide are produced; molding the aluminum oxide and silicon carbide into the predetermined shape; and sintering the molded shape at a temperature within the range on the order of about 1300°C to 1900°C and in the presence of nitrogen until a solid solution of aluminum oxide in silicon nitride is produced.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-06-01 | 1979-12-01 | 1980-06-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-06-01 | 1983-12-01 | 1984-06-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-06-01 | 1987-12-01 | 1988-06-01 | $7700.00 | Window Closed / Lapsed |