Method for a surface treatment of cemented carbide article
Assignee: Toyota Central R&D Labs Inc
•
Filing: 1973-11-13
•
Granted: 1976-05-25
•
Expires: 1993-11-13
Abstract
Abstract A method for forming a very hard layer on the surface of an iron, ferrous alloy or cemented carbide article in a treating molten bath, comprising preparing the treating molten bath composed of boron oxide and chromium, immersing the article in the treating molten bath and applying an electric current to the treating molten bath through said article being used as the cathode, thereby forming a very hard layer composed of chromium carbide and/or chromium boride on the surface of said article. The method of this invention can quickly form a uniform and dense layer on the surface of the article and can be carried out in the open air.
Inventors
- 👤 Noboru Komatsu
- 👤 Tohru Arai
- 👤 Yoshihiko Sugimoto
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 01:02
CPC Classifications
C; C25; C25D; C25D3/00; C25D3/66
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
143 words
A method for forming a hard layer containing at least one member selected from the group consisting of chromium carbide and chromium boride on the surface of a cemented carbide article containing at least 0.05% by weight of carbon, which comprises preparing a molten bath containing molten boron oxide and a substance containing chromium, immersing the article into the molten bath contained in a vessel, applying an electric current to the molten bath through said article as a cathode so as to deposit a member selected from the group consisting of (1) chromium and (2) a mixture of chromium and boron, on the surface of the article and form a hard layer containing at least one member selected from the group consisting of chromium carbide and chromium boride on the surface of said article, and removing the resultant article from the molten bath.
Claim 2
Independent Claim
143 words
A method for forming a hard layer containing at least one member selected from the group consisting of chromium carbide and chromium boride on the surface of a cemented carbide article containing at least 0.05% by weight of carbon, which comprises preparing a molten bath containing molten boron oxide and a substance containing chromium, immersing the article into the molten bath contained in a vessel, applying an electric current to the molten bath through said article as a cathode so as to deposit a member selected from the group consisting of (1) chromium and (2) a mixture of chromium and boron, on the surface of the article and form a hard layer containing at least one member selected from the group consisting of chromium carbide and chromium boride on the surface of said article, and removing the resultant article from the molten bath.
Claim 3
Dependent Claim
35 words
A method according to claim 1, wherein said molten bath contains 50 to 99% by weight of said boron oxide, the remainer of said molten bath being the chromium-containing substance dissolved in said boron oxide.
Claim 4
Dependent Claim
15 words
A method according to claim 2, wherein said chromium-containing substance is an oxide of chromium.
Claim 5
Dependent Claim
34 words
A method according to claim 3, wherein said cemented carbide article is treated in said molten bath at a current density of the cathode within a range from 0.01 to 15 A/cm 2 .
Claim 6
Dependent Claim
22 words
A method according to claim 4, wherein said molten bath is maintained at a temperature within the range from 800° to 1100°C.
Claim 7
Dependent Claim
53 words
A method according to claim 3, wherein said oxide of chromium is selected fromm the group consisting of Cr 2 O 3 , (NH 4 ) 2 Cr 2 O 7 , K 2 Cr 2 O 7 , K 2 CrO 4 , Na 2 Cr 2 O 7 and mixtures thereof.
Claim 8
Dependent Claim
17 words
A method according to claim 2, wherein said chromium-containing substance is metallic chromium or a chromium alloy.
Claim 9
Dependent Claim
17 words
A method according to claim 7, wherein said chromium-containing substance is in the form of a powder.
Claim 10
Dependent Claim
28 words
A method according to claim 7, wherein said chromium-containing substance is in the form of a block, and said block is anodically dissolved in the molten boron oxide.
Claim 11
Dependent Claim
34 words
A method according to claim 7, wherein said cemented carbide article is treated in said molten bath at a current density of the cathode within a range from 0.01 to 15 A/cm 2 .
Claim 12
Dependent Claim
15 words
A method according to claim 2, wherein said chromium-containing substance is a halide of chromium.
Claim 13
Dependent Claim
33 words
A method according to claim 11, wherein said halide is selected from the group consisting of CrCl 3 , CrCl 2 , CrF 3 , CrBr 3 , CrI 3 and mixtures thereof.
Claim 14
Dependent Claim
34 words
A method according to claim 11, wherein said cemented carbide article is treated in said molten bath at a current density of the cathode within a range from 0.01 to 15 A/cm 2 .
Claim 15
Dependent Claim
22 words
A method according to claim 1, wherein said boron oxide is selected from the group consisting of boric acid and a borate.
Claim 16
Dependent Claim
21 words
A method according to claim 14, wherein said borate is selected from the group consisting of sodium borate and potassium borate.
Claim 17
Dependent Claim
27 words
A method according to claim 1, wherein said molten bath contains 1 to 50% by weight of chromium, the remainder of said molten bath being boron oxide.
Claim 18
Dependent Claim
41 words
A method according to claim 1, wherein a mixture of chromium and boron is deposited on the surface of the article and the hard layer formed on the surface of the article contains a mixture of chromium carbide and chromium boride.
References Cited (Backward Citations)
US556092A
Cited
GB286457A
Cited
US2746915A
Cited
US2950233A
Cited
US2984605A
Cited
US3485725A
Cited
US3671297A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-05-25 | 1979-11-24 | 1980-05-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-05-25 | 1983-11-24 | 1984-05-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-05-25 | 1987-11-24 | 1988-05-25 | $7700.00 | Window Closed / Lapsed |