Assignee: Westvaco Corp
•
Filing: 1975-04-21
•
Granted: 1976-05-25
•
Expires: 1995-04-21
Abstract
Abstract A method is disclosed for making low-porosity, free-flowing cement pastes with extended set times, improved workability and reduced expansion due to alkali aggregate reactions, by combining hydraulic cements, especially Portland-type cements, ground without gypsum with from 0.1% to about 1.0% of an alkali or alkaline earth lignosulfonate or sulfonated lignin, combining 20% to 40% of water with 0.1% to 2.0% of an alkali bicarbonate, and thereafter mixing together the combined cement and lignin with the combined water and alkali bicarbonate. As an alternate embodiment of this process, the alkali or alkaline earth lignosulfonate or sulfonated lignin may be added to the water-bicarbonate rather than blended directly with the cement. These low-porosity pastes when mixed with aggregates produce mortars and concretes that have extended set times and are very workable during processing.
Inventors
- 👤 Lynden J. Stryker
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 16:33
CPC Classifications
C; C04; C04B; C04B28/00; C04B28/02
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
89 words
A method of making a gypsum-free, low porosity free-flowing cement paste which consists essentially of the following mixing sequence; a. combining hydraulic cement without gypsum ground to a fineness of from 3,500 to 9,000 cm. 2 /gram with from 0.1% to about 1.5% of alkali or alkaline earth lignosulfonate or sulfonated lignin, b. combining 20% to 40% of water with 0.1% to 2.0% of an alkali bicarbonate, and c. thereafter mixing together the combined materials of steps (a) and (b), all percentages based on dry weight of ground cement.
Claim 2
Independent Claim
89 words
A method of making a gypsum-free, low porosity free-flowing cement paste which consists essentially of the following mixing sequence; a. combining hydraulic cement without gypsum ground to a fineness of from 3,500 to 9,000 cm. 2 /gram with from 0.1% to about 1.5% of alkali or alkaline earth lignosulfonate or sulfonated lignin, b. combining 20% to 40% of water with 0.1% to 2.0% of an alkali bicarbonate, and c. thereafter mixing together the combined materials of steps (a) and (b), all percentages based on dry weight of ground cement.
Claim 3
Dependent Claim
18 words
The method according to claim 1 wherein said lignin is present in an amount from 0.3% to 0.8%.
Claim 4
Dependent Claim
19 words
The method according to claim 1 wherein said alkali bicarbonate is present in an amount from 0.7% to 1.5%.
Claim 5
Dependent Claim
28 words
The method according to claim 1 wherein said alkali bicarbonate is sodium carbonate, said lignin is a sulfonated alkali lignin and said hydraulic cement is a Portland cement.
Claim 6
Independent Claim
83 words
A method of making a gypsum-free, low porosity, free-flowing cement paste which consists essentially of; a. admixing from 0.1% to about 1.5% of alkali or alkaline earth lignosulfonate or sulfonated lignin, from 0.1% to about 2.0% of an alkali bicarbonate with 20% to 40% of water, all percentages based on the dry weight of ground cement, and then b. mixing the materials of step (a) with hydraulic cement without gypsum ground to a Blaine fineness of from 3,500 to 9,000 cm. 2 /gm.
Claim 7
Independent Claim
83 words
A method of making a gypsum-free, low porosity, free-flowing cement paste which consists essentially of; a. admixing from 0.1% to about 1.5% of alkali or alkaline earth lignosulfonate or sulfonated lignin, from 0.1% to about 2.0% of an alkali bicarbonate with 20% to 40% of water, all percentages based on the dry weight of ground cement, and then b. mixing the materials of step (a) with hydraulic cement without gypsum ground to a Blaine fineness of from 3,500 to 9,000 cm. 2 /gm.
Claim 8
Dependent Claim
18 words
The method accordng to claim 5 wherein said lignin is present in an amount from 0.3% to 0.8%.
Claim 9
Dependent Claim
19 words
The method according to claim 5 wherein said alkali bicarbonate is present in an amount from 0.7% to 1.5%.
Claim 10
Dependent Claim
28 words
The method according to claim 5 wherein said alkali bicarbonate is sodium bicarbonate, said lignin is a sulfonated alkali lignin, and said hydraulic cement is a Portland cement.
Claim 11
Independent Claim
110 words
A method of making a gypsum-free, low porosity, free-flowing cement paste which consists essentially of the following mixing sequence; a. combining hydraulic cement ground to a Blaine fineness of from 3,500 to 9,000 cm. 2 /gm. with a portion of alkali or alkaline earth lignosulfonate or sulfonated lignin, b. combining 20% to 40% of water with 0.1% to 2.0% of an alkali bicarbonate and the remaining portion of said lignin from step (a), the total amount lignin in steps (a) and (b) being from 0.1% to about 1.5%, and c. thereafter mixing together the combined materials of steps (a) and (b), all percentages based on dry weight of ground cement.
Claim 12
Independent Claim
110 words
A method of making a gypsum-free, low porosity, free-flowing cement paste which consists essentially of the following mixing sequence; a. combining hydraulic cement ground to a Blaine fineness of from 3,500 to 9,000 cm. 2 /gm. with a portion of alkali or alkaline earth lignosulfonate or sulfonated lignin, b. combining 20% to 40% of water with 0.1% to 2.0% of an alkali bicarbonate and the remaining portion of said lignin from step (a), the total amount lignin in steps (a) and (b) being from 0.1% to about 1.5%, and c. thereafter mixing together the combined materials of steps (a) and (b), all percentages based on dry weight of ground cement.
Claim 13
Independent Claim
112 words
A method of making a gypsum-free, low porosity, free-flowing cement paste which consists essentially of; a. admixing a portion of alkali or alkaline earth lignosulfonate or sulfonated lignin, from 0.1% to about 2.0% of an alkali bicarbonate with 20% to 40% of water, and then b. mixing the remaining portion of said lignin from step (a) with hydraulic cement without gypsum ground to a Blaine fineness of from 3,500 to 9,000 cm. 2 /gm., the total amount of lignin in steps (a) and (b) being from 0.1% to about 1.5%, all percentages based on the dry weight of ground cement, and then c. mixing the materials of steps (a) and (b) together.
Claim 14
Independent Claim
112 words
A method of making a gypsum-free, low porosity, free-flowing cement paste which consists essentially of; a. admixing a portion of alkali or alkaline earth lignosulfonate or sulfonated lignin, from 0.1% to about 2.0% of an alkali bicarbonate with 20% to 40% of water, and then b. mixing the remaining portion of said lignin from step (a) with hydraulic cement without gypsum ground to a Blaine fineness of from 3,500 to 9,000 cm. 2 /gm., the total amount of lignin in steps (a) and (b) being from 0.1% to about 1.5%, all percentages based on the dry weight of ground cement, and then c. mixing the materials of steps (a) and (b) together.
References Cited (Backward Citations)
US2646360A
Cited
US3689294A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-05-25 | 1979-11-24 | 1980-05-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-05-25 | 1983-11-24 | 1984-05-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-05-25 | 1987-11-24 | 1988-05-25 | $7700.00 | Window Closed / Lapsed |